A large class of modern structural alloys derives its strength from precipitation hardening. Precipitates obstruct the motion of dislocations and thereby increase alloy strength. This paper examines the process using an atomistic-based hierarchical multiscale modeling framework. Atomistic modeling is employed to (1) compute solute-dislocation interaction energies for input into a semi-analytic solute hardening model and (2) evaluate precipitate strengths for use in dislocation line tension simulations. The precipitate microstructure in the dislocation line tension simulations is obtained from simple analytic precipitation kinetics relations. Fitting only the rate constants in the precipitation kinetics model, the macroscopic strength predictions of the hierarchical multiscale model are found to correspond reasonably well with experiments. By analyzing the potential sources of discrepancy between the model’s macroscopic predictions and experiments, this work illuminates the importance of specific atomic-scale processes and highlights important challenges that remain before truly predictive mechanism-based plasticity modeling can be realized.
Similar content being viewed by others
Notes
Note that while H v is usually measured in kgf/mm2, σy is in MPa. Therefore, one needs to divide the right hand side of Eq. [5] by g = 9.807 to get hardness in the units of Vicker’s Pyramid Number (VPN).
We refer the interested reader to Nguyen et al.[89] for insight into the origin and significance of these assumptions.
References
Wilm A. (1911) Metallurgie 8:225–27
Gayle F.W., Goodway M. (1994) Science 266:1015–17
Orowan E.Z. (1934) Phys. 89:634
Polanyi M.Z. (1934) Phys. 89:660
Taylor G.I. (1934) Proc. R. Soc. Lond. A, 145:362–87
Guinier A. (1939) Ann. Phys. 12:161
Preston G.D. (1938) Phil. Mag. 26:855
I. J. Polmear and H. K. Hardy: J. Inst. Met., 1952–1953, vol. 81, pp. 427–32
Hornbogen E. (2001) JJ. Light Met. 1:127–32
I. Polmear: Light Alloys: From Traditional Alloys to Nanocrystals, Butterworth-Heinemann, London, 2006
Liddicoat P.V., Liao X.-Z., Zhao Y., Zhu Y., Murashkin M.Y., Lavernia E.J., Valiev R.Z., Ringer S.P. (2010) Nat. Commun. 1:1–7
R.Z. Valiev, N.A. Enikeev, Murashkin, V.U. Kazykhanov, and X. Sauvage: Scripta Materialia, 2010, vol. 63, pp. 949–52
A. Guinier: Heterogeneities in Solid Solutions, Vol. 9 of Solid State Physics, Elsevier, Amsterdam, 1959, pp. 293–398.
Hono K., Satoh T., Hirano K.-I. (1986) Philos. Mag. A 53:495–504
Ringer S.P., Hono K. (2000) Mater. Charact. 44:101–31
Karlik M., Bigot A., Jouffrey B., Auger P., Belliot S. (2004) Ultramicroscopy 98:219–30
J.M. Silcock, T.J. Heal, and H.K. Hardy: J. Inst. Met., 1953–1954, vol. 82, pp. 239–48
N.F. Mott and F.R.N. Nabarro: Report on the Strength of Solids , The Physical Society, London, 1948, p. 1.
V. Gerold and H. Haberkorn: Phys. Stat. Solidi, 1996, vol. 16, p. 675.
G. Knowles and P.M. Kelly: BSC/ISI Conference, Scarborough, The Iron and Steel Institute, London, 1971, p. 9
Nembach E. (1983) Phys. Stat. Solidi (a) 78:571–81
Hirsch P. B., Kelly A. (1965) Phil. Mag. 12:881
Kelly A., Nicholson R.B. (1963) Progr. Mater. Sci. 10:151–91
Kelly A., Fine M.E. (1957) Acta Metallurgica 5:365–67
Harkness S.D., Hren J.J. (1970) Metall. Trans. Am. Clin. Climatol. Assoc. 1:43–49
L.M. Brown and R.K. Ham: Strengthening Methods in Crystals, Applied Science Publishers, London, 1971, p. 9
Eto T. (1980) Scripta Metallurgica 14:133
Muraishi S., Niwa N., Maekawa A., Kumai S., Sato A. (2002) Philos. Mag. A 82:2755–71
Van Swygenhoven H., Derlet P.M. (2001) Phys. Revi. B 64:224105–9
Rao S.I., Parthasarathy T.A., Dimiduk D.M., Hazzledine P.M. (2004) Phil. Mag. 84:3195–15
Dewald M.P., Curtin W.A. (2007) Modell. Simul. Mater. Sci. Eng. 15:193–95
Zhu T., Li J., Samanta A., Kim H.G., Suresh S. (2007) PNAS 104:3031–36
Osetsky Y.N., Bacon D.J. (2003) J. Nucl. Mater. 323:268–80
Kohler C., Kizler P., Schmauder S. (2005) Model. Simul. Mater. Sci. Eng. 13:35–45
Shim J.-H., Cho Y.W., Kwon S.C., Kim W.W., Wirth B.D. (2007) Appl. Phys. Lett. 90:021906
Terentyev D., Bonny G., Malerba L. (2008) Acta Materialia 56:3229–35
Takahashi A., Ghoniem N.M. (2008) J. Mech. Phys. Solids 56:1534–53
Singh C.V., Warner D.H. (2010) Acta Materialia 58:5797–5805
Singh C.V., Mateos A., Warner D.H. (2011) Scripta Materialia 64:398–401
D.J. Bacon, Y.N. Osetsky, and D. Rodney: Dislocation-Obstacle Interactions at the Atomic Level, vol. 15, chap. 88, pp. 1–90, 2009
Shercliff H., Ashby M. (1990) Acta Metallurgica et Materialia 38:1789–1802
Schmauder S., Binkele P. (2002) Comput. Mater. Sci. 24:42–53
Starink M.J., Gao N., Davin L., Yan J., Cerezo A. (2005) Phil. Mag. 85:1395–17
G.E. Dieter: Mechanical Metallurgy, Materials Science and Engineering, 3rd ed., McGraw-Hill, New York, 1986
D. Hull and D. Bacon: Introduction to Dislocations, 4th edn., Butterworth-Heinemann, London, 2001
Kelchner C., Plimpton S., Hamilton J. (1998) Phys. Rev. B 58:11085–88
Li J. (2003) Modell. Simul. Mater. Sci. Eng. 11:173–77
Friedel J. (1956) Les Dislocations. Gauthier-Villars, Paris, France
Orowan E. (1984) Symposium on Internal Stresses in Metals and Alloys. Institute of Metals, London
Bacon D.J., Kocks U.F., Scattergood R.O. (1973) Phil. Mag. 28:1241–63
Hirsch P.B. (1957) J. Inst. Met. 86:13–14
T. Hatano: Phys. Rev. B, 2006, vol. 74, pp. 020102+
Humphreys F.J., Hirsch P.B. (1970) Proc. R. Soc. Lond. A 318:73–92
Leyson G.P., Curtin W.A., Hector L.G., Woodward C.F. (2010) Nat. Mater. 9:750–55
Labusch R. (1970) Phys. Stat. Solidi (b) 41:659–69
Labusch R. (1972) Acta Metallurgica 20:917–27
Apostol F., Mishin Y. (2011) Phys. Rev. B 83:054116
Olmsted D., Hectorjr L., Curtin W. (2006) J. Mech. Phys. Solids 4:1763–88
olverton C., Ozolins V. (2006) Phys. Revi. B 73:144104
Diak B., Saimoto S. (1997) Mater. Sci. Eng. A 234-236:1019–22
Mousa S.A., Bozarth J., Youssef A., Levine B., Diak B.J., Upadhyaya K.R., Saimoto S. (1998) Prog. Mater Sci. 43:223–63
Foreman A.J.E., Makin M.J. (1967) Canad. J. Phys. 45:511–17
T. Nogaret and D. Rodney: Phys. Rev. B, 2006, vol. 74, pp. 134110+.
Z. Xu and R.C. Picu: Phys. Rev. B, 2007, vol. 76, pp. 094112+.
Dong Y., Nogaret T., Curtin W.A. (2010) Metall. Mater. Trans. A 41:1954–60
Binkele P., Schmauder S. (2003) Z. Metallkd 94:858–63
Taylor G.I. (1938) J. Inst. Met. 62:307–24
G.I. Taylor: Proceedings of the Colloquium on Deformation and Flow of Solids (Madrid, 1955), Springer, Berlin, 1956, pp. 3–12
Stoller R.E., Zinkle S.J. (2000) J. Nucl. Mater. 283-287:349–52
Wang J., Wolverton C., Muller S., Liu Z., Chen L. (2005) Acta Materialia 53:2759–64
Avrami M. (1939) J. Chem. Phys. 7:1103–12
J. Christian: The Theory of Phase Transformations in Metals and Alloys, Pergamon Press, Oxford, 3rd edn., 2002
Hornbogen E. (1967) Aluminum 43:115–21
Massalski T. (1980) J. Phase Equilib. 1:27–33
Wagner C. (1961) Z. Elektrochem. 65:581–91
Nie J.F., Muddle B.C., Polmear I.J. (1996) Mater. Sci. Forum 217-222:1257–62
J. Yan: Ph.D. Thesis, School of Engineering Sciences, University of Southampton, 2006
Starink M. (2004) Int. Mater. Rev. 49:191–26
J. W. Martin: Precipitation Hardening, Butterworth-Heinemann, London, 2nd edn., 1998
Badini C., Marino F., Verne E. (1995) Mater. Sci. Eng. A 191:185–91
Smith G. (1998) Thermochim. Acta 317:7–23
Bassani P., Gariboldi E., Vimercati G. (2007) J. Therm. Anal. Calorim. 87:247–53
Ardell A. (1985) Metall. Trans. A 16A:2131–65
Argon A. (2007) Strengthening Mechanisms in Crystal Plasticity (Oxford Series on Materials Modelling). Oxford University Press, Oxford
T. Hatano and H. Matsui: Phys. Rev. B, 2005, vol. 72, pp. 094105+
Ney H., Labusch R., Haasen P. (1977) Acta Metallurgica 25:1257–69
Olmsted D.L., Hector Jr. L.G., Curtin W., Clifton R. (2005) Modell. Simul. Mater. Sci. Eng. 13:371–88
Hirth J., Lothe J. (1968) Theory of Dislocations. McGraw-Hill, New York
Nguyen L., Baker K., Warner D. (2011) Phys. Rev. B, 2011 84:024118
Warner D.H., Curtin W.A., Qu S. (2007) Nat. Mat. 6:876–81
Warner D., Curtin W. (2009) Acta Materialia 57:4267–77
Trinkle D.R., Woodward C. (2005) Science 310:1665–67
Plimpton S.J. (1995) J. Comp. Phys. 117:1–19
M. S. Daw and M. I. Baskes: Phys. Rev. B, 1984, vol. 29, pp. 6443–53
Mishin Y., Mehl M., Papaconstantopoulos D. (2005) Acta Materialia 53:4029–41
E. Nembach and G. Neite: Prog. Mat. Sci., 1985, vol. 29, pp. 177–319
Acknowledgments
The authors gratefully acknowledge support from Ed Glaessgen and Steve Smith at NASA (Grant No. NNX08BA39A).
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted April 16, 2012.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Movie 1 (corresponding to Fig. 2a): 60 deg interaction between edge dislocation and GP zone involving leading partial cutting and trailing partial looping. MPG (656 KB)
11661_2013_1614_MOESM2_ESM.mpg
Movie 2 (corresponding to Fig. 2b): 0 deg interaction between edge dislocation and GP zone involving full dislocation looping. MPG (342 KB)
Appendices
Appendix A: Atomistic Modeling of Precipitation Hardening
The atomistic simulations were carried out using the freely available open source LAMMPS code.[93] The code was modified to use a recently developed Al-Cu empirical potential developed by Apostol and Mishin.[57] The potential is an angular-dependent extension of the embedded atom method (EAM)[94,95] where the potential energy of the system is
Indices i and j enumerate atoms and the superscripts α, β = 1, 2, 3 refer to the Cartesian directions. The first two terms, taken together, represent regular EAM contributions, where \(\Upphi_{ij}\) is the pair-interaction potential and F i is the embedding energy of atom i with \(\bar{\rho_i}\) loosely representing the electron density. The three remaining terms represent the angular dependence through dipole and quadrupole distortions. The details of the potential can be found in Apostol and Mishin[57] and Mishin et al.[95] We validated our implementation by comparing relaxed cohesive energies, vacancy formation energies, surfaces energies, heats of solution, and formation energy for the θ″ (Al2Cu) phase with independent values provided by Apostol and Mishin.[57] The simulation cell (Figure A1) consisted of an FCC Al lattice, bounded by \(\left(\bar110\right), \left(111\right), \) and \(\left(11\bar2\right)\) faces in X, Y, and Z directions, respectively. Periodic boundary conditions were applied in the X and Z directions, and the Y surfaces were used to apply the load. Starting from a perfect lattice, a precipitate was created by simply changing selected atom types to Cu. The continuum displacement field of an edge dislocation was used to create a dislocation in the center of the simulation cell (X = Y = 0) with a line direction parallel to the Z axis and the burgers vector \(\vec b=1/2[\bar110]. \)
Because GP zones and θ″ precipitates only form on {100}-type planes, there are only three physically relevant orientations by which they interact with edge dislocations, two of which are crystallographically equivalent. The Burgers vector of the edge dislocation will either be at an angle of 60 deg from the precipitate plane or be parallel to it (Figure 1). Thus, we will refer to dislocation–precipitate interactions as either being 60 or being 0 deg in nature. As a simplification, we assume that GP zones are monolayers of Cu atoms with a 100 pct Cu content, while θ′′ precipitates are two Cu layers separated by three Al layers.[14,16]
The minimum cell size was approximately 34 × 42 × 16 nm3 and contained approximately 1.4 million atoms. For the simulations with large GP zones and θ′′ precipitates, a larger cell size was used (with largest cell size being approximately 68 × 44 × 64 nm3 consisting of 11 million atoms). In all cases, box size studies were performed to verify that simulation cell boundary forces were negligible in the X and Y directions. The effect of cell size in the Z direction will be discussed later; however, we note that the cell sizes in the Z direction that we explored are consistent with experimental observations of GP zone and θ″ spacing.[17,28]
Prior to loading, NPT dynamics were performed for 50 ps to relax the system and alleviate out-of-balance forces and net stresses. The system was then loaded in shear by subjecting the atoms near the top and bottom Y surfaces to a constant traction in the X direction given by
for top and bottom Y surfaces, respectively, where τ xy is applied shear stress, A xz is the surface area, and N is the number of atoms on the respective surfaces. The applied shear stress was increased quasi-statically until the dislocation breaks free from the precipitate. At each load step of 5 MPa, non-linear conjugate gradient was performed to minimize the out-of-balance forces to less than 10−8 eV/Å.
Appendix B: Analytic Relations for Critical Resolved Shear Strength of the Precipitate, τc
Assuming a fixed dislocation line tension, ϕc is an intrinsic measure of the strength of the precipitate. Using a simple line tension model and ignoring dislocation self-interactions, the critical stress required for a dislocation to shear a precipitate can be written as
with T being the line tension of the dislocation. Note that this relation suggests τc scales as 1/L.
In the limit of an impenetrable precipitate, the dislocation will bow into a configuration with neighboring segments on each side of the precipitate perpendicular to the dislocations’ original glide direction, i.e., ϕc = 0. In this situation, the dislocation segments will collapse via the Orowan looping mechanism,[49] with a critical stress of
From continuum elasticity theory, T ≈ Gb 2/2, where G is the shear modulus of the matrix material. This leads to \(\tau_{\rm c}^{\rm{Orowan}}=\frac{Gb}{L}\) and \(\tau_{\rm c}=\frac{Gb}{L} \cos{(\phi_{\rm c}/2)}=\tau_{\rm c}^{\rm{Orowan}}\cos{(\phi_{\rm c}/2)}\) for Orowan looping and shearing, respectively. A simple modification is often used to extend these relations into a domain where D is not negligible with respect to L.[26]
with L − D p representing the distance which is available between neighboring precipitate edges for the dislocation to bow-out and D p being the projected cross-sectional diameter of the precipitate along the dislocation line. Because the above expressions ignore dislocation self-interactions, they overestimate precipitate strengthening. Specifically, the attraction between the two segments of dislocation on each side of the precipitate will promote a more acute bowing angle as well as Orowan looping before ϕc = 0 deg. A semi-empirical expression incorporating self-interaction effects has been given by Scattergood and Bacon[50] by fitting to numerical results,
where B is a fitting parameter and A = 1 when the dislocation is initially pure edge and (1 − ν) when pure screw with ν being the Poisson’s ratio.
Appendix C: Derivation of Solute Hardening
The model is built upon an interaction energy function between a solute atom and a dislocation, U(x i , y j ), with x i and y j describing the position of the lattice site of the solute atom with respect to a dislocation with a line direction along the z-axis. Using U(x i , y j ), which is computed from atomistic simulation, the change in energy associated with the movement of a straight dislocation in a field of random solutes a distance w in the direction x can be written as
where n ij is an independent random variable representing the number of solute atoms at position (x i , y j ) along the dislocation line. Considering that the solute locations are uncorrelated, the typical change in energy associated with the movement of a straight segment of dislocation of length, ξ, can be written using a correlation function
as
with c s being the solute concentration. For a finite w, only a finite region near the dislocation segment needs to be considered to compute \(\Updelta E_{\rm p}.\)
The heterogeneity of the energy landscape experienced by the dislocation promotes a curved dislocation line. In the model, the curvature of the dislocation line is approximated as a series of straight dislocation segments of length ξ that exist at discrete increments of w in the glide direction. The extra line energy due to a segment of dislocation length ξ gliding a distance w away from its neighboring segments can be written as
with \(\Upgamma\) representing the line energy.
The total energy change associated with the glide of a segment of dislocation from an originally straight dislocation is the sum of its change in line energy and change in interaction energy.
By minimizing this equation in terms of ξ and w, characteristic length scales ξc and w c can be obtained.
Considering that the strength-controlling energy barriers to dislocation glide result from segments of dislocation length ξc that must move from a typical favorable interaction energy fluctuation past a typical unfavorable interaction energy fluctuation over a distance of w c while regaining the line energy \(\Updelta E_{\rm el}(\xi_{\rm c},w_{\rm c}), \) the typical energy barrier to the glide of a dislocation segment is
Finally, assuming a sinusoidal energy profile with a peak of \(\Updelta E_{\rm b}\) over a distance of w c provides the zero-temperature shear stress needed to move a typical segment of dislocation forward,
Appendix D: Hardening Contributions
The strength of the Al-Cu alloy will increase as Cu atoms transfer from solute to GP zones if \( \frac{{\partial \tau _{{{\text{yGP}}}} }}{{\partial c_{{{\text{GP}}}} }} > \frac{{\partial \tau _{{{\text{ys}}}} }}{{\partial c_{{\text{s}}} }} \) with c = c GP + c s where c GP represents the concentration of Cu belonging to GP zones and τyGP represents the strengthening due to GP zones. While \(\frac{\partial \tau_{\rm{ys}}}{\partial c_{\rm s}}\) can be explicitly expressed in terms of c s, i.e., τys∝ c 2/3s (Section III and,[54] \(\frac{\partial \tau_{\rm{yGP}}}{\partial c_{\rm{GP}}}\) must be approximated due to its non-analytic dependence on GP zone diameter. For the Al-4 wt pct Cu alloy aged at 383 K (110 °C), τyGP(c GP) can be described reasonably well with a simple power law
with the fitting constant τ 0yGP = 1400 MPa. Considering this relation and τys/c 2/3s = 1138 MPa (from Section III), the inequality, \(\frac{\partial \tau_{\rm{yGP}}}{\partial c_{\rm{GP}}} > \frac{\partial \tau_{\rm{ys}}}{\partial c_{\rm s}}, \) implies that strength will increase as Cu atoms transfer from solute to GP zones if c GP < 0.663 c 7/12s .
Appendix E: Derivation of Plastic Strain Rate in the Presence of Thermal Activation
First, the rate at which the controlling thermally activated events occur is assumed to follow an Arrhenius relation
The exponential prefactor, \(\tilde{\nu_0}, \) is assumed to be a constant and the energy barrier, \(\Updelta E,\) is assumed to only depend upon the ratio of the applied load, τ, over the load at which the thermally activated events occur instantaneouslyFootnote 2, τinst. Assuming that the shape of the energy barrier, with respect to the reaction coordinate, is sinusoidal, the functional form of \(\Updelta E\) can be approximated to the first order as
Finally, the rate at which the controlling thermally activated events occur, ν, is assumed proportional to the plastic strain rate, \(\dot{\gamma}. \)
Assembling the above assumptions and Eqs. [E1] and [E2], one can construct a popular expression for relating the applied load τ to the plastic strain rate \(\dot{\gamma}\) in the presence of thermal activation,[54,55]
Rights and permissions
About this article
Cite this article
Singh, C.V., Warner, D.H. An Atomistic-Based Hierarchical Multiscale Examination of Age Hardening in an Al-Cu Alloy. Metall Mater Trans A 44, 2625–2644 (2013). https://doi.org/10.1007/s11661-013-1614-1
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-013-1614-1