Erschienen in: Metallurgical and Materials Transactions A 6/2013

01.06.2013 | Communication

High-Temperature Tensile Properties of Nano-Oxide Dispersion Strengthened Ferritic Steels Produced by Mechanical Alloying and Spark Plasma Sintering

verfasst von: Xavier Boulnat, Damien Fabregue, Michel Perez, Marie-Hélène Mathon, Yann de Carlan

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 6/2013

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Oxide-dispersion strengthened (ODS) ferritic steels were produced by mechanical alloying and subsequent spark plasma sintering. Very fast heating rates were used to minimize porosity when controlling grain size and precipitation of dispersoids within a compacted material. Sintering cycles performed at 1373 K (1100 °C) induced heterogeneous, but fine grain size distribution and high density of nano-oxides. Yield strengths at room temperature and at 923 K (650 °C) are 975 MPa and 298 MPa, respectively. Furthermore, high-temperature ductility is much increased: total strain of 28 pct at 923 K (650 °C).

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat S. Ukai, M. Harada, H. Okada, M. Inoue, S. Nomura, S. Shikakura, T. Nishida, M. Fujiwara, K. Asabe: J. Nucl. Mater., 1993, vol. 204, pp. 65–73.CrossRef S. Ukai, M. Harada, H. Okada, M. Inoue, S. Nomura, S. Shikakura, T. Nishida, M. Fujiwara, K. Asabe: J. Nucl. Mater., 1993, vol. 204, pp. 65–73.CrossRef
2.
Zurück zum Zitat S. Ukai, M. Fujiwara: J. Nucl. Mater., 2002, vol. 307-311, pp. 749-57.CrossRef S. Ukai, M. Fujiwara: J. Nucl. Mater., 2002, vol. 307-311, pp. 749-57.CrossRef
3.
Zurück zum Zitat R.L. Klueh, D.S. Gelles, S. Jitsukawa, A. Kimura, G.R. Odette, B. van der Schaaf, M. Victoria: J. Nucl. Mater., 2002, vol. 307–311, pp. 455–65.CrossRef R.L. Klueh, D.S. Gelles, S. Jitsukawa, A. Kimura, G.R. Odette, B. van der Schaaf, M. Victoria: J. Nucl. Mater., 2002, vol. 307–311, pp. 455–65.CrossRef
4.
Zurück zum Zitat M.J. Alinger, G.R. Odette, D.T. Hoelzer: Acta Mater., 2009, vol. 57, pp. 392–406.CrossRef M.J. Alinger, G.R. Odette, D.T. Hoelzer: Acta Mater., 2009, vol. 57, pp. 392–406.CrossRef
5.
Zurück zum Zitat Y. De Carlan J.L. Béchade, P. Dubuisson, J.L. Seran, P. Billot, A. Bougault, T. Cozzika, S. Doriot, D. Hamon, J. Henry, M. Ratti, N. Lochet, D. Nunes, P. Olier, T. Leblond, M.H. Mathon: J. Nucl. Mater., 2009, vol. 386–388, pp. 430-32.CrossRef Y. De Carlan J.L. Béchade, P. Dubuisson, J.L. Seran, P. Billot, A. Bougault, T. Cozzika, S. Doriot, D. Hamon, J. Henry, M. Ratti, N. Lochet, D. Nunes, P. Olier, T. Leblond, M.H. Mathon: J. Nucl. Mater., 2009, vol. 386–388, pp. 430-32.CrossRef
6.
Zurück zum Zitat P. Dubuisson, Y. de Carlan, V. Garat, M. Blat: J. Nucl. Mater., 2012, vol. 428, pp. 6-12.CrossRef P. Dubuisson, Y. de Carlan, V. Garat, M. Blat: J. Nucl. Mater., 2012, vol. 428, pp. 6-12.CrossRef
7.
Zurück zum Zitat S. Saroja, A. Dasgupta, R. Divakar: J.Nucl. Mater., 2011, vol. 4009, pp. 131-39.CrossRef S. Saroja, A. Dasgupta, R. Divakar: J.Nucl. Mater., 2011, vol. 4009, pp. 131-39.CrossRef
8.
Zurück zum Zitat M. Wang, Z. Zhou, H. Sun, H. Hu, S. Li: Mater. Sci. Eng. A., 2013, vol. 559, pp. 287-92.CrossRef M. Wang, Z. Zhou, H. Sun, H. Hu, S. Li: Mater. Sci. Eng. A., 2013, vol. 559, pp. 287-92.CrossRef
9.
Zurück zum Zitat W.M. Guo, Z.G. Yang, G.J. Zhang: Int. J. Refract. Met. Hard Mater., 2011, vol. 29, pp. 452-55.CrossRef W.M. Guo, Z.G. Yang, G.J. Zhang: Int. J. Refract. Met. Hard Mater., 2011, vol. 29, pp. 452-55.CrossRef
10.
Zurück zum Zitat D. Fabrègue, J. Piallat, E. Maire, Y. Jorand, V. Massardier-Jourdan, G. Bonnefont: Powder Metallurgy, 2012, vol. 55, pp. 76-79.CrossRef D. Fabrègue, J. Piallat, E. Maire, Y. Jorand, V. Massardier-Jourdan, G. Bonnefont: Powder Metallurgy, 2012, vol. 55, pp. 76-79.CrossRef
11.
Zurück zum Zitat R. Orru, R. Licheri, M. Locci, A. Cincotti, G. Cao, Mater. Sci. Eng. R, 2009, vol. 63, pp. 127–287.CrossRef R. Orru, R. Licheri, M. Locci, A. Cincotti, G. Cao, Mater. Sci. Eng. R, 2009, vol. 63, pp. 127–287.CrossRef
12.
Zurück zum Zitat T. Grosdidier, G. Ji, S. Launois: Scripta Mater., 2007, vol. 57, pp. 525-28.CrossRef T. Grosdidier, G. Ji, S. Launois: Scripta Mater., 2007, vol. 57, pp. 525-28.CrossRef
13.
Zurück zum Zitat G. Ji, T. Grosdidier, N. Bozzolo, S. Launois: Intermetallics., 2007, vol. 15, pp. 108-18.CrossRef G. Ji, T. Grosdidier, N. Bozzolo, S. Launois: Intermetallics., 2007, vol. 15, pp. 108-18.CrossRef
14.
Zurück zum Zitat M. Ratti, D. Leuvrey, M.H. Mathon, Y. de Carlan: J. Nucl. Mater., 2009, vol. 386–388, pp. 540-43.CrossRef M. Ratti, D. Leuvrey, M.H. Mathon, Y. de Carlan: J. Nucl. Mater., 2009, vol. 386–388, pp. 540-43.CrossRef
15.
Zurück zum Zitat L. Toualbi, M. Ratti, G. André, F. Onimus, Y. de Carlan, J. Nucl. Mater., 2011, vol. 417, pp. 225–28.CrossRef L. Toualbi, M. Ratti, G. André, F. Onimus, Y. de Carlan, J. Nucl. Mater., 2011, vol. 417, pp. 225–28.CrossRef
16.
Zurück zum Zitat A. Molinari, S. Libardi, M. Leoni, P. Scardi, Acta Mater., 2010, vol. 58, pp. 963–66.CrossRef A. Molinari, S. Libardi, M. Leoni, P. Scardi, Acta Mater., 2010, vol. 58, pp. 963–66.CrossRef
17.
Zurück zum Zitat D. Bouvard: Métallurgie des poudres, Mim, Édition Hermes-Lavoisier, Paris, 2002. D. Bouvard: Métallurgie des poudres, Mim, Édition Hermes-Lavoisier, Paris, 2002.
18.
Zurück zum Zitat M.H. Mathon, M. Perrut, S.Y. Zhong, Y. de Carlan: J. Nucl. Mater., 2012, vol. 428, pp. 147–53.CrossRef M.H. Mathon, M. Perrut, S.Y. Zhong, Y. de Carlan: J. Nucl. Mater., 2012, vol. 428, pp. 147–53.CrossRef
19.
Zurück zum Zitat Q.X. Sun, T. Zhang, X.P. Wang, Q.F. Fang, T. Hao, C.S. Liu: J. Nucl. Mater., 2012, vol. 424, pp. 279–84.CrossRef Q.X. Sun, T. Zhang, X.P. Wang, Q.F. Fang, T. Hao, C.S. Liu: J. Nucl. Mater., 2012, vol. 424, pp. 279–84.CrossRef
20.
Zurück zum Zitat Z. Oksiuta, P. Mueller, P. Spätig, N. Baluc, J. Nucl. Mater., 2011, vol. 412, pp. 221–26.CrossRef Z. Oksiuta, P. Mueller, P. Spätig, N. Baluc, J. Nucl. Mater., 2011, vol. 412, pp. 221–26.CrossRef
21.
Zurück zum Zitat L. Guo, C. Jia, B. Hu, H. Li: Mater. Sci. Eng. A, 2010, vol. 527, pp. 5220–24.CrossRef L. Guo, C. Jia, B. Hu, H. Li: Mater. Sci. Eng. A, 2010, vol. 527, pp. 5220–24.CrossRef
22.
Zurück zum Zitat A. Garcia-Juncedan, M. Hernandez-Mayoral, M. Serrano, Mater. Sci. Eng. A, 2012, vol. 556, pp. 696–703.CrossRef A. Garcia-Juncedan, M. Hernandez-Mayoral, M. Serrano, Mater. Sci. Eng. A, 2012, vol. 556, pp. 696–703.CrossRef
23.
Zurück zum Zitat B. Fournier, A. Steckmeyer, A.-L. Rouffie, J. Malaplate, J. Garnier, M. Ratti, P. Wident, L. Ziolek, I. Tournie, V. Rabeau, J.M. Gentzbittel, T. Kruml, I. Kubena: J. Nucl. Mater., 2012, vol. 430, pp. 142-49.CrossRef B. Fournier, A. Steckmeyer, A.-L. Rouffie, J. Malaplate, J. Garnier, M. Ratti, P. Wident, L. Ziolek, I. Tournie, V. Rabeau, J.M. Gentzbittel, T. Kruml, I. Kubena: J. Nucl. Mater., 2012, vol. 430, pp. 142-49.CrossRef
24.
Zurück zum Zitat P. Unifantowicza, Z. Oksiuta, P. Olier, Y. De Carlan, and N. Baluc: Fusion Eng. Des., 2011, vol. 86, pp. 2413–16. P. Unifantowicza, Z. Oksiuta, P. Olier, Y. De Carlan, and N. Baluc: Fusion Eng. Des., 2011, vol. 86, pp. 2413–16.
25.
Zurück zum Zitat A. Takahashi, Z. Chen, N. Ghoniem, N. Kioussis: J. Nucl. Mater., 2011, vol. 417, pp. 1098-101.CrossRef A. Takahashi, Z. Chen, N. Ghoniem, N. Kioussis: J. Nucl. Mater., 2011, vol. 417, pp. 1098-101.CrossRef
26.
Zurück zum Zitat A. Steckmeyer, M. Praud, B. Fournier, J. Malaplate, J. Garnier, J.L. Béchade, I. Tournié, A. Tancray, A. Bougault, and P. Bonnaillie: J. Nucl. Mater., 2010, vol. 405, pp. 95–100.CrossRef A. Steckmeyer, M. Praud, B. Fournier, J. Malaplate, J. Garnier, J.L. Béchade, I. Tournié, A. Tancray, A. Bougault, and P. Bonnaillie: J. Nucl. Mater., 2010, vol. 405, pp. 95–100.CrossRef
27.
Zurück zum Zitat R. Kasada, S.G. Lee, J. Isselin, J.H. Lee, T. Omura, A. Kimura, T. Okuda, M. Inoue, S. Ukai, S. Ohnuki, T. Fujisawa, F. Abe: J. Nucl. Mater., 2011, vol. 417, pp. 180–84.CrossRef R. Kasada, S.G. Lee, J. Isselin, J.H. Lee, T. Omura, A. Kimura, T. Okuda, M. Inoue, S. Ukai, S. Ohnuki, T. Fujisawa, F. Abe: J. Nucl. Mater., 2011, vol. 417, pp. 180–84.CrossRef
28.
Zurück zum Zitat Y.H. Zhao, Y.Z. Guo, Q. Wei, A.M. Dangelewicz, C. Xu, Y.T. Zhu, T.G. Langdon, Y.Z. Zhou, E.J. Lavernia: Scripta Mater., 2008, vol. 59, pp. 627-30.CrossRef Y.H. Zhao, Y.Z. Guo, Q. Wei, A.M. Dangelewicz, C. Xu, Y.T. Zhu, T.G. Langdon, Y.Z. Zhou, E.J. Lavernia: Scripta Mater., 2008, vol. 59, pp. 627-30.CrossRef
29.
Zurück zum Zitat K.A. Darling, B.G. Butler, H.E. Maupin, L.J. Kecskes, and S.N. Mathaudhu: Proceedings of the 2012 International Conference on Powder Metallurgy & Particulate Materials, Las Vegas, NV, pp. 0929–0939. K.A. Darling, B.G. Butler, H.E. Maupin, L.J. Kecskes, and S.N. Mathaudhu: Proceedings of the 2012 International Conference on Powder Metallurgy & Particulate Materials, Las Vegas, NV, pp. 0929–0939.
30.
Zurück zum Zitat D. Fabrègue, T. Pardoen: J. Mech. Phys. Solids., 2008, vol. 56(3), pp. 719-41.CrossRef D. Fabrègue, T. Pardoen: J. Mech. Phys. Solids., 2008, vol. 56(3), pp. 719-41.CrossRef
31.
Zurück zum Zitat G. Ji, F. Bernard, S. Launois, T. Grosdidier, Mater. Sci. Eng. A, 2013, vol. 559, pp. 566–73.CrossRef G. Ji, F. Bernard, S. Launois, T. Grosdidier, Mater. Sci. Eng. A, 2013, vol. 559, pp. 566–73.CrossRef
32.
Zurück zum Zitat Y. Zhao, T. Topping, J.F. Bingert, J. Thornton, A.M. Dangelewicz, Y. Li: Adv. Mater., 2008, vol. 20, pp. 3028-33.CrossRef Y. Zhao, T. Topping, J.F. Bingert, J. Thornton, A.M. Dangelewicz, Y. Li: Adv. Mater., 2008, vol. 20, pp. 3028-33.CrossRef
34.
35.
Metadaten
Titel
High-Temperature Tensile Properties of Nano-Oxide Dispersion Strengthened Ferritic Steels Produced by Mechanical Alloying and Spark Plasma Sintering
verfasst von
Xavier Boulnat
Damien Fabregue
Michel Perez
Marie-Hélène Mathon
Yann de Carlan
Publikationsdatum
01.06.2013
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 6/2013
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-013-1719-6

Weitere Artikel der Ausgabe 6/2013

Metallurgical and Materials Transactions A 6/2013 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.