Effect of Structural Heterogeneity on In Situ Deformation of Dissimilar Weld Between Ferritic and Austenitic Steel

verfasst von: M. Ghosh, R. Santosh, S. K. Das, G. Das, B. Mahato, J. Korody, S. Kumar, P. K. Singh

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 8/2015

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Low-alloy steel and 304LN austenitic stainless steel were welded using two types of buttering material, namely 309L stainless steel and IN 182. Weld metals were 308L stainless steel and IN 182, respectively, for two different joints. Cross-sectional microstructure of welded assemblies was investigated. Microhardness profile was determined perpendicular to fusion boundary. In situ tensile test was performed in scanning electron microscope keeping low-alloy steel-buttering material interface at the center of gage length. Adjacent to fusion boundary, low-alloy steel exhibited carbon-depleted region and coarsening of matrix grains. Between coarse grain and base material structure, low-alloy steel contained fine grain ferrite-pearlite aggregate. Adjacent to fusion boundary, buttering material consisted of Type-I and Type-II boundaries. Within buttering material close to fusion boundary, thin cluster of martensite was formed. Fusion boundary between buttering material-weld metal and weld metal-304LN stainless steel revealed unmixed zone. All joints failed within buttering material during in situ tensile testing. The fracture location was different for various joints with respect to fusion boundary, depending on variation in local microstructure. Highest bond strength with adequate ductility was obtained for the joint produced with 309L stainless steel-buttering material. High strength of this weld might be attributed to better extent of solid solution strengthening by alloying elements, diffused from low-alloy steel to buttering material.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat C. Jang, J. Lee, J. S. Kim and T. E. Jin; Mechanical property variation within Inconel 82/182 dissimilar metal weld between low alloy steel and 316 stainless steel, Int. J. of Pressure Vessels and Piping 2008, Vol. 85, pp. 635-646.CrossRef C. Jang, J. Lee, J. S. Kim and T. E. Jin; Mechanical property variation within Inconel 82/182 dissimilar metal weld between low alloy steel and 316 stainless steel, Int. J. of Pressure Vessels and Piping 2008, Vol. 85, pp. 635-646.CrossRef
2.
Zurück zum Zitat S. Missori and C. Koerber: Laser beam welding of austenitic-ferritic transition joints, Welding J., 1997, Vol.76, pp. 125s-134s. S. Missori and C. Koerber: Laser beam welding of austenitic-ferritic transition joints, Welding J., 1997, Vol.76, pp. 125s-134s.
3.
Zurück zum Zitat J. N. DuPont, J. N. Lippold and S. D. Kiser: Welding Metallurgy and Weldability of Ni-Base Alloys, John Wiley & Sons Publication, 2009, Chapter 7, pp. 327-376.CrossRef J. N. DuPont, J. N. Lippold and S. D. Kiser: Welding Metallurgy and Weldability of Ni-Base Alloys, John Wiley & Sons Publication, 2009, Chapter 7, pp. 327-376.CrossRef
4.
Zurück zum Zitat A. Celik and A. Alsaran; Mechanical and structural properties of similar and dissimilar steel joints, Mats. Characterization 1999, Vol. 43, pp. 311-318.CrossRef A. Celik and A. Alsaran; Mechanical and structural properties of similar and dissimilar steel joints, Mats. Characterization 1999, Vol. 43, pp. 311-318.CrossRef
5.
Zurück zum Zitat H. Naffakh, M. Shamanian and F. Ashrafizadeh; Dissimilar welding of AISI 310 austenitic stainless stell to nickel-based alloy Inconel 657, J. of Mats. Processing Technol. 2009, Vol. 209, pp. 3628-3639.CrossRef H. Naffakh, M. Shamanian and F. Ashrafizadeh; Dissimilar welding of AISI 310 austenitic stainless stell to nickel-based alloy Inconel 657, J. of Mats. Processing Technol. 2009, Vol. 209, pp. 3628-3639.CrossRef
6.
Zurück zum Zitat M. Sireesha, S. K. Albert, V. Shankar and S. Sundaresan; A comparative evaluation of welding consumables for dissimilar welds between 316LN austenitic stainless steel and alloy 800, J. Of Nuclear Mats., 2000, vol. 279, pp. 65-76.CrossRef M. Sireesha, S. K. Albert, V. Shankar and S. Sundaresan; A comparative evaluation of welding consumables for dissimilar welds between 316LN austenitic stainless steel and alloy 800, J. Of Nuclear Mats., 2000, vol. 279, pp. 65-76.CrossRef
7.
Zurück zum Zitat A. Wiltner, C. Linsmeier and T. Jacob: J. Chem. Phys., 2008, Vol. 129, pp. 084704-1–10.CrossRef A. Wiltner, C. Linsmeier and T. Jacob: J. Chem. Phys., 2008, Vol. 129, pp. 084704-1–10.CrossRef
8.
Zurück zum Zitat C. Pan and E. Zhang: Morphologies of the transition region in dissimilar austenite-ferrite welds,Mater. Char., 1996, Vol. 36, pp. 5-10.CrossRef C. Pan and E. Zhang: Morphologies of the transition region in dissimilar austenite-ferrite welds,Mater. Char., 1996, Vol. 36, pp. 5-10.CrossRef
9.
Zurück zum Zitat H. S. Hosseini, M. Shamanian and A. Kermanpur: Characterization of microstructures and mechanical properties of Inconel 617/310 stainless steel dissimilar welds, Mater. Char., 2011, Vol. 62, pp. 425-431.CrossRef H. S. Hosseini, M. Shamanian and A. Kermanpur: Characterization of microstructures and mechanical properties of Inconel 617/310 stainless steel dissimilar welds, Mater. Char., 2011, Vol. 62, pp. 425-431.CrossRef
10.
Zurück zum Zitat H. Naffakh, M. Shamanian and F. Ashrafizadeh: Dissimilar welding of AISI 310 austenitic stainless steel to nickel based alloy Inconel 657, J. Mats. Proc. Technol., 2009, Vol. 209, pp. 3628-3639.CrossRef H. Naffakh, M. Shamanian and F. Ashrafizadeh: Dissimilar welding of AISI 310 austenitic stainless steel to nickel based alloy Inconel 657, J. Mats. Proc. Technol., 2009, Vol. 209, pp. 3628-3639.CrossRef
11.
Zurück zum Zitat H. T. Lee, S.L. Jeng, C. H. Yen and T.Y. Kuo: Dissimilar welding of nickel based alloy 690 to SUS 304L with Ti addition, J. of Nuclear Mats., 2004, Vol. 2004, pp. 59-69.CrossRef H. T. Lee, S.L. Jeng, C. H. Yen and T.Y. Kuo: Dissimilar welding of nickel based alloy 690 to SUS 304L with Ti addition, J. of Nuclear Mats., 2004, Vol. 2004, pp. 59-69.CrossRef
12.
Zurück zum Zitat F. Matsuda and H. Nakagawa: Trans. of JWRI, 1984, Vol. 13, pp. 159-161. F. Matsuda and H. Nakagawa: Trans. of JWRI, 1984, Vol. 13, pp. 159-161.
13.
Zurück zum Zitat T. W. Nelson, J. C. Lippold and M. J. Mills: Sci. Technol. Weld. Join., 1998, Vol. 3, pp. 249–254.CrossRef T. W. Nelson, J. C. Lippold and M. J. Mills: Sci. Technol. Weld. Join., 1998, Vol. 3, pp. 249–254.CrossRef
14.
Zurück zum Zitat K. Sharma, H. K. Khandelwal, V. Bhasisn and R. Chhibber: Application of ball indentation technique for mechanical properties estimation of bi-metallic weld, Adv. Mats. Res., 2012, Vol. 585, pp. 342-346.CrossRef K. Sharma, H. K. Khandelwal, V. Bhasisn and R. Chhibber: Application of ball indentation technique for mechanical properties estimation of bi-metallic weld, Adv. Mats. Res., 2012, Vol. 585, pp. 342-346.CrossRef
16.
Zurück zum Zitat C. D. Lundin: Dissimilar metal welds – Literature review, Welding J. 1982, Vol. 61, pp. 585s-635s. C. D. Lundin: Dissimilar metal welds – Literature review, Welding J. 1982, Vol. 61, pp. 585s-635s.
17.
Zurück zum Zitat R. L. Klueh and J. F. King: Austenite-ferrite weld joint failures, Welding J. 1982, Vol. 61, pp. 302-311. R. L. Klueh and J. F. King: Austenite-ferrite weld joint failures, Welding J. 1982, Vol. 61, pp. 302-311.
18.
Zurück zum Zitat W. J. Mills and C. M. Brown: Metall. Mater. Trans. A 2001, Vol. 32A, pp. 1161-1174.CrossRef W. J. Mills and C. M. Brown: Metall. Mater. Trans. A 2001, Vol. 32A, pp. 1161-1174.CrossRef
20.
Zurück zum Zitat L. Yang, X. Dang, M. Li, and N. Ji: Proceedings of 2nd International Conference on Electronic and Mechanical Engineering and Information Technology (EMEIT 2012), Shenyang Liaoning, China, Prof. B. Wu, ed., Atlantis Press, Paris, pp. 697–700. L. Yang, X. Dang, M. Li, and N. Ji: Proceedings of 2nd International Conference on Electronic and Mechanical Engineering and Information Technology (EMEIT 2012), Shenyang Liaoning, China, Prof. B. Wu, ed., Atlantis Press, Paris, pp. 697–700.
21.
Zurück zum Zitat N. Wang, S. Mokadem, M. Rappaz and W. Kurz: Solidification cracking of superalloy single- and bi-crystals, Acta Mater., 2004, Vol. 52, pp. 3173-3182.CrossRef N. Wang, S. Mokadem, M. Rappaz and W. Kurz: Solidification cracking of superalloy single- and bi-crystals, Acta Mater., 2004, Vol. 52, pp. 3173-3182.CrossRef
22.
Zurück zum Zitat T. Y. Kuo and H. T. Lee: Effects of filler metal composition on joining properties of alloy 690 weldment, Mats. Sci. & Engg. A., 2002, vol. 338, pp. 202-212.CrossRef T. Y. Kuo and H. T. Lee: Effects of filler metal composition on joining properties of alloy 690 weldment, Mats. Sci. & Engg. A., 2002, vol. 338, pp. 202-212.CrossRef
23.
Zurück zum Zitat R. Dehmolaei, M. Shamanian and A. Kermanpur: Microstructural characterization of dissimilar welds between alloy 800 and HP heat-resistant steel, Mater. Character., 2008, Vol. 59, pp. 1447-1454.CrossRef R. Dehmolaei, M. Shamanian and A. Kermanpur: Microstructural characterization of dissimilar welds between alloy 800 and HP heat-resistant steel, Mater. Character., 2008, Vol. 59, pp. 1447-1454.CrossRef
24.
Zurück zum Zitat W. F. Savage, E. F. Nipess and E.S. Szekeres: Study of weld interface phenomena in low alloy steel, Weld. J., 1976, Vol. 55, pp. 260-268. W. F. Savage, E. F. Nipess and E.S. Szekeres: Study of weld interface phenomena in low alloy steel, Weld. J., 1976, Vol. 55, pp. 260-268.
25.
Zurück zum Zitat C. Pan, R. Wang and J. Gui: 1990, J. Mater. Sci., Vol. 25, pp. 3281-3285.CrossRef C. Pan, R. Wang and J. Gui: 1990, J. Mater. Sci., Vol. 25, pp. 3281-3285.CrossRef
26.
Zurück zum Zitat T.W. Nelson, J.C. Lippold and M. J. Mills: 1999, Weld. J., Vol. 78, pp. 329s-337s. T.W. Nelson, J.C. Lippold and M. J. Mills: 1999, Weld. J., Vol. 78, pp. 329s-337s.
27.
Zurück zum Zitat M.D. Rowe, T.W. Nelson, and J. C. Lippold: 1999, Weld. J., Vol. 78, pp. 31s-37s. M.D. Rowe, T.W. Nelson, and J. C. Lippold: 1999, Weld. J., Vol. 78, pp. 31s-37s.
28.
Zurück zum Zitat J.N. DuPont and C.S. Kusko: Weld. J., 1996, Vol. 86, pp. 51s-54s. J.N. DuPont and C.S. Kusko: Weld. J., 1996, Vol. 86, pp. 51s-54s.
29.
Zurück zum Zitat R.E. Reed-Hill: Physical Metallurgy Principals (Chap. 18), 2nd edition, East West Press Pvt. Ltd., Delhi, 1973, pp. 701-748. R.E. Reed-Hill: Physical Metallurgy Principals (Chap. 18), 2nd edition, East West Press Pvt. Ltd., Delhi, 1973, pp. 701-748.
30.
Zurück zum Zitat S.S. F. DeDafe, F.L. Sicupira, F.C.S. Matos, N.S. Cruz, D.R. Moreira, and D.B. Santos: Mater. Res. 2013, Vol. 16 (6), pp. 1229-36.CrossRef S.S. F. DeDafe, F.L. Sicupira, F.C.S. Matos, N.S. Cruz, D.R. Moreira, and D.B. Santos: Mater. Res. 2013, Vol. 16 (6), pp. 1229-36.CrossRef
31.
Zurück zum Zitat T.W. Nelson, J.C. Lippold, and M. J. Mills: Weld. J., 2000, Vol. 79, pp. 267-277. T.W. Nelson, J.C. Lippold, and M. J. Mills: Weld. J., 2000, Vol. 79, pp. 267-277.
32.
Zurück zum Zitat M. W. A. Rashid, M. Gakim, Z. M. Rosli and M. A. Azam: Formation of Cr23C6 during the sensitization of AISI 304 stainless steel and its effect to pitting corrosion, Int. J. of Electrochemical Sci., 2012, Vol. 7, pp. 9465-9477. M. W. A. Rashid, M. Gakim, Z. M. Rosli and M. A. Azam: Formation of Cr23C6 during the sensitization of AISI 304 stainless steel and its effect to pitting corrosion, Int. J. of Electrochemical Sci., 2012, Vol. 7, pp. 9465-9477.
34.
Zurück zum Zitat G. D. Huang, D. K. Matlock and G. Krauss: Martensite formation, strain rate sensitivity, and deformation behavior of type 304 stainless steel sheet, Met. Mats. Trans A, 1989, Vol. 20, pp.1239-1246.CrossRef G. D. Huang, D. K. Matlock and G. Krauss: Martensite formation, strain rate sensitivity, and deformation behavior of type 304 stainless steel sheet, Met. Mats. Trans A, 1989, Vol. 20, pp.1239-1246.CrossRef
35.
Zurück zum Zitat R. E. Schramm and R. P. Reed: Stacking fault energies of seven commercial austenitic stainless steels, Met. Mats, Trans A, 1975, Vol.6, pp. 1345-1351.CrossRef R. E. Schramm and R. P. Reed: Stacking fault energies of seven commercial austenitic stainless steels, Met. Mats, Trans A, 1975, Vol.6, pp. 1345-1351.CrossRef
36.
Zurück zum Zitat D.J. Siegel: Appl. Phys. Lett., 2005, Vol. 87, pp. 121901-1–1219013.CrossRef D.J. Siegel: Appl. Phys. Lett., 2005, Vol. 87, pp. 121901-1–1219013.CrossRef
37.
Zurück zum Zitat A.M. Shariatpanahi, Hassan Farhangi: Microstructure and mechanical properties of dissimilar ferritic and austenitic steel joints with an intermediate IN 182 buttering layer, Adv. Mats. Res., 2009, Vol. 83-86, pp. 449-456.CrossRef A.M. Shariatpanahi, Hassan Farhangi: Microstructure and mechanical properties of dissimilar ferritic and austenitic steel joints with an intermediate IN 182 buttering layer, Adv. Mats. Res., 2009, Vol. 83-86, pp. 449-456.CrossRef
Metadaten
Titel
Effect of Structural Heterogeneity on In Situ Deformation of Dissimilar Weld Between Ferritic and Austenitic Steel
verfasst von
M. Ghosh
R. Santosh
S. K. Das
G. Das
B. Mahato
J. Korody
S. Kumar
P. K. Singh
Publikationsdatum
01.08.2015
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 8/2015
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-015-2930-4

Weitere Artikel der Ausgabe 8/2015

Metallurgical and Materials Transactions A 8/2015 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.