In Situ Neutron Diffraction Study of the Influence of Microstructure on the Mechanical Response of Additively Manufactured 304L Stainless Steel

verfasst von: D. W. Brown, D. P. Adams, L. Balogh, J. S. Carpenter, B. Clausen, G King, B. Reedlunn, T. A. Palmer, M. C. Maguire, S. C. Vogel

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 12/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In situ neutron diffraction measurements were completed during tensile and compressive deformation of stainless steel 304L additively manufactured (AM) using a high power directed energy deposition process. Traditionally produced wrought 304L material was also studied for comparison. The AM material exhibited roughly 200 MPa higher flow stress relative to the wrought material. Crystallite size, crystallographic texture, dislocation density, and lattice strains were all characterized to understand the differences in the macroscopic mechanical behavior. The AM material’s initial dislocation density was about 10 times that of the wrought material, and the flow strength of both materials obeyed the Taylor equation, indicating that the AM material’s increased yield strength was primarily due to greater dislocation density. Also, a ~50 MPa flow strength tension/compression asymmetry was observed in the AM material, and several potential causes were examined.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat D.D. Gu, W. Meiners, K. Wissenbach, R. Poprawe, Int. Mater. Rev., 2012, vol. 57, pp. 133-164.CrossRef D.D. Gu, W. Meiners, K. Wissenbach, R. Poprawe, Int. Mater. Rev., 2012, vol. 57, pp. 133-164.CrossRef
2.
Zurück zum Zitat S.A. Davis, J.M. Vitek, T.L. Hebble, Welding Journal, 1987, vol. 66, pp. S289-S300. S.A. Davis, J.M. Vitek, T.L. Hebble, Welding Journal, 1987, vol. 66, pp. S289-S300.
3.
Zurück zum Zitat Z. Wang, T.A. Palmer, A.M. Beese, Acta Mater., 2016, vol. 110, pp. 226-235.CrossRef Z. Wang, T.A. Palmer, A.M. Beese, Acta Mater., 2016, vol. 110, pp. 226-235.CrossRef
4.
Zurück zum Zitat B.E. Carroll, T.A. Palmer, A.M. Beese, Acta Mater., 2015, vol. 87, pp. 309-320.CrossRef B.E. Carroll, T.A. Palmer, A.M. Beese, Acta Mater., 2015, vol. 87, pp. 309-320.CrossRef
5.
Zurück zum Zitat P. Akerfeldt, M.-L. Antti, R. Pederson, Mater. Sci. Eng., A, 2016, vol. 674, pp. 428-437.CrossRef P. Akerfeldt, M.-L. Antti, R. Pederson, Mater. Sci. Eng., A, 2016, vol. 674, pp. 428-437.CrossRef
6.
Zurück zum Zitat E. Nishida, B. Song, M. Maguire, D. Adams, J. Carroll, J. Wise, J. Bishop, T. Palmer: in Dymat 2015—11th International Conference on the Mechanical and Physical Behaviour of Materials under Dynamic Loading, E. Cadoni, ed., 2015. E. Nishida, B. Song, M. Maguire, D. Adams, J. Carroll, J. Wise, J. Bishop, T. Palmer: in Dymat 2015—11th International Conference on the Mechanical and Physical Behaviour of Materials under Dynamic Loading, E. Cadoni, ed., 2015.
7.
Zurück zum Zitat G.T. Gray, III, V. Livescu, P.A. Rigg, C.P. Trujillo, C.M. Cady, S.R. Chen, J.S. Carpenter, T.J. Lienert, S. Fensin: in Dymat 2015—11th International Conference on the Mechanical and Physical Behaviour of Materials Under Dynamic Loading, E. Cadoni, ed., 2015. G.T. Gray, III, V. Livescu, P.A. Rigg, C.P. Trujillo, C.M. Cady, S.R. Chen, J.S. Carpenter, T.J. Lienert, S. Fensin: in Dymat 2015—11th International Conference on the Mechanical and Physical Behaviour of Materials Under Dynamic Loading, E. Cadoni, ed., 2015.
8.
Zurück zum Zitat W.E. King, A.T. Anderson, R.M. Ferencz, N.E. Hodge, C. Kamath, S.A. Khairallah, A.M. Rubenchik: Appl. Phys. Rev., 2015, vol. 2, 041304CrossRef W.E. King, A.T. Anderson, R.M. Ferencz, N.E. Hodge, C. Kamath, S.A. Khairallah, A.M. Rubenchik: Appl. Phys. Rev., 2015, vol. 2, 041304CrossRef
9.
Zurück zum Zitat B. Clausen: PhD. Technical University of Denmark, 1997. B. Clausen: PhD. Technical University of Denmark, 1997.
10.
Zurück zum Zitat M. Gharghouri, G. Weatherly, J. Embury, J. Root, Phil. Mag. A, 1999, 7, vol. 79, pp. 1671-1695CrossRef M. Gharghouri, G. Weatherly, J. Embury, J. Root, Phil. Mag. A, 1999, 7, vol. 79, pp. 1671-1695CrossRef
11.
Zurück zum Zitat M.R. Daymond, C.N. Tome, M.A.M. Bourke, Acta Mater., 2000, vol. 48(2), pp. 553-564.CrossRef M.R. Daymond, C.N. Tome, M.A.M. Bourke, Acta Mater., 2000, vol. 48(2), pp. 553-564.CrossRef
12.
Zurück zum Zitat L. Balogh, D. Brown, P. Mosbrucker, F. Long, M. Daymond, Acta Mater., 2012, vol. 60(15), pp. 5567-5577.CrossRef L. Balogh, D. Brown, P. Mosbrucker, F. Long, M. Daymond, Acta Mater., 2012, vol. 60(15), pp. 5567-5577.CrossRef
13.
Zurück zum Zitat S. Agnew, C. Tome, D. Brown, T. Holden, S. Vogel, Scr. Mater., 2003, vol. 48 (8), pp. 1003-1008.CrossRef S. Agnew, C. Tome, D. Brown, T. Holden, S. Vogel, Scr. Mater., 2003, vol. 48 (8), pp. 1003-1008.CrossRef
14.
Zurück zum Zitat R. Tandon, T. Wilks, M. Gieseke, C. Noelke, S. Kaierle, T.A. Palmer: Euro Powder Metallurgy Association (EPMA): AM – Special Processes and Materials Reims, Fr, 2015. R. Tandon, T. Wilks, M. Gieseke, C. Noelke, S. Kaierle, T.A. Palmer: Euro Powder Metallurgy Association (EPMA): AM – Special Processes and Materials Reims, Fr, 2015.
15.
Zurück zum Zitat VAMAS-20, Technical Specification, ISO/TS 21432, 2005 VAMAS-20, Technical Specification, ISO/TS 21432, 2005
16.
Zurück zum Zitat M.A.M. Bourke, D.C. Dunand, E. Ustundag, Appl. Phys. A, 2002, vol. A74, pp. S1707-S1709.CrossRef M.A.M. Bourke, D.C. Dunand, E. Ustundag, Appl. Phys. A, 2002, vol. A74, pp. S1707-S1709.CrossRef
17.
Zurück zum Zitat H. Wenk, L. Lutterotti, S. Vogel, Nucl. Instrum. Methods Phys. Res. Sect. A, 2003, vol. 515(3), pp. 575-588.CrossRef H. Wenk, L. Lutterotti, S. Vogel, Nucl. Instrum. Methods Phys. Res. Sect. A, 2003, vol. 515(3), pp. 575-588.CrossRef
18.
Zurück zum Zitat D.W. Brown, M.A. Okuniewski, T.A. Sisneros, B. Clausen, G.A. Moore, L. Balogh, J. Nuc. Matl., 2016, vol. 482, pp. 63-74.CrossRef D.W. Brown, M.A. Okuniewski, T.A. Sisneros, B. Clausen, G.A. Moore, L. Balogh, J. Nuc. Matl., 2016, vol. 482, pp. 63-74.CrossRef
19.
Zurück zum Zitat D.W. Brown, M.A.M. Bourke, B. Clausen, D.R. Korzekwa, R.C. Korzekwa, R.J. McCabe, T.A. Sisneros, D.F. Teter, Mater. Sci. Eng., A, 2009, vol. 512, pp. 67-75.CrossRef D.W. Brown, M.A.M. Bourke, B. Clausen, D.R. Korzekwa, R.C. Korzekwa, R.J. McCabe, T.A. Sisneros, D.F. Teter, Mater. Sci. Eng., A, 2009, vol. 512, pp. 67-75.CrossRef
20.
21.
Zurück zum Zitat G. Ribarik, J. Gubicza, T. Ungar, Mater. Sci. Eng., A, 2004, vol. 387, pp. 343-347.CrossRef G. Ribarik, J. Gubicza, T. Ungar, Mater. Sci. Eng., A, 2004, vol. 387, pp. 343-347.CrossRef
22.
Zurück zum Zitat L. Lutterotti, S. Matthies, H.-R. Wenk, A.J. Schultz, J.W. Richardson, J. App. Phys., 1997, vol. 81, pp. 594-600.CrossRef L. Lutterotti, S. Matthies, H.-R. Wenk, A.J. Schultz, J.W. Richardson, J. App. Phys., 1997, vol. 81, pp. 594-600.CrossRef
23.
Zurück zum Zitat H.R. Wenk, L. Lutterotti, S.C. Vogel, Powder Diffr., 2010, vol. 25(3), pp. 283-296.CrossRef H.R. Wenk, L. Lutterotti, S.C. Vogel, Powder Diffr., 2010, vol. 25(3), pp. 283-296.CrossRef
24.
Zurück zum Zitat Y.S. Touloukian, R.K. Kirby, R.E. Taylor, P.D. Desai, Thermal Expansion: Metallic Elements and Alloys, Plenum Publishing Company, New York, 1975.CrossRef Y.S. Touloukian, R.K. Kirby, R.E. Taylor, P.D. Desai, Thermal Expansion: Metallic Elements and Alloys, Plenum Publishing Company, New York, 1975.CrossRef
25.
Zurück zum Zitat M.R. Daymond, M.A.M. Bourke, R.B. Von Dreele, B. Clausen, T. Lorentzen, J. App. Phys., 1997, vol. 82(4), pp. 1554-1562.CrossRef M.R. Daymond, M.A.M. Bourke, R.B. Von Dreele, B. Clausen, T. Lorentzen, J. App. Phys., 1997, vol. 82(4), pp. 1554-1562.CrossRef
26.
27.
Zurück zum Zitat I.C. Noyan, J.B. Cohen, Residual Stress-Measurement by Diffraction and Interpretation, Springer-Verlag, New York., 1987. I.C. Noyan, J.B. Cohen, Residual Stress-Measurement by Diffraction and Interpretation, Springer-Verlag, New York., 1987.
28.
Zurück zum Zitat T.M. Holden, J.H. Root, R.A. Holt, M. Hayashi, Physica B, 1995, vol. 213, pp. 793-796 CrossRef T.M. Holden, J.H. Root, R.A. Holt, M. Hayashi, Physica B, 1995, vol. 213, pp. 793-796 CrossRef
29.
Zurück zum Zitat A.D. Krawitz, T.M. Holden, MRS Bulletin, 1990, vol. 15(11), pp. 57-64.CrossRef A.D. Krawitz, T.M. Holden, MRS Bulletin, 1990, vol. 15(11), pp. 57-64.CrossRef
30.
Zurück zum Zitat T.M. Holden, R.A. Holt, G. Dolling, B.M. Powell, J.E. Winegar, Metall. Trans. A, 1988, vol. 19(9), pp. 2207-2214.CrossRef T.M. Holden, R.A. Holt, G. Dolling, B.M. Powell, J.E. Winegar, Metall. Trans. A, 1988, vol. 19(9), pp. 2207-2214.CrossRef
31.
Zurück zum Zitat T.M. Holden, R.A. Holt, A.P. Clarke, Mater. Sci. Eng. A, 1998, vol. 246(1-2), pp. 180-198.CrossRef T.M. Holden, R.A. Holt, A.P. Clarke, Mater. Sci. Eng. A, 1998, vol. 246(1-2), pp. 180-198.CrossRef
32.
Zurück zum Zitat A.C. Larson, R.B. Von Dreele, Los Alamos National Lab, Los Alamos, NM, 1986. A.C. Larson, R.B. Von Dreele, Los Alamos National Lab, Los Alamos, NM, 1986.
33.
Zurück zum Zitat T. Ungar, J. Gubicza, G. Ribarik, A. Borbely, J. App. Crys., 2001, vol. 34(3), pp. 298-310.CrossRef T. Ungar, J. Gubicza, G. Ribarik, A. Borbely, J. App. Crys., 2001, vol. 34(3), pp. 298-310.CrossRef
34.
35.
Zurück zum Zitat T. Ungár, G. Tichy, J. Gubicza, R.J. Hellmig, Powder Diffr., 2005, vol. 20(4), pp. 366-375.CrossRef T. Ungár, G. Tichy, J. Gubicza, R.J. Hellmig, Powder Diffr., 2005, vol. 20(4), pp. 366-375.CrossRef
37.
Zurück zum Zitat U.F. Kocks, C.N. Tome, H.R. Wenk, Texture and Anisotropy, Cambridge University Press, Cambridge, 1998. U.F. Kocks, C.N. Tome, H.R. Wenk, Texture and Anisotropy, Cambridge University Press, Cambridge, 1998.
38.
Zurück zum Zitat C.J. Neil, J.A. Wollmershauser, B. Clausen, C.N. Tome, S.R. Agnew, Int. J. Plas., 2010, vol. 26(12), pp. 1772-1791.CrossRef C.J. Neil, J.A. Wollmershauser, B. Clausen, C.N. Tome, S.R. Agnew, Int. J. Plas., 2010, vol. 26(12), pp. 1772-1791.CrossRef
40.
Zurück zum Zitat B. Clausen, T. Lorentzen, M.A.M. Bourke, M.R. Daymond: Mater. Sci. Eng. A, 1999, vol. 259(1):17-24.CrossRef B. Clausen, T. Lorentzen, M.A.M. Bourke, M.R. Daymond: Mater. Sci. Eng. A, 1999, vol. 259(1):17-24.CrossRef
41.
42.
Zurück zum Zitat R.P. Reed, Jom-Journal of the Minerals Metals & Materials Society, 1989, vol. 41(3), pp. 16-21.CrossRef R.P. Reed, Jom-Journal of the Minerals Metals & Materials Society, 1989, vol. 41(3), pp. 16-21.CrossRef
43.
Zurück zum Zitat G.I. Taylor, J. Inst. Met., 1938, vol. 62, pp. 307-324. G.I. Taylor, J. Inst. Met., 1938, vol. 62, pp. 307-324.
44.
Zurück zum Zitat E.O. Hall, Proceedings of the Physical Society of London Section B, 1951, vol. 64(381), pp. 747-753.CrossRef E.O. Hall, Proceedings of the Physical Society of London Section B, 1951, vol. 64(381), pp. 747-753.CrossRef
45.
Zurück zum Zitat N.J. Petch, Journal of the Iron and Steel Institute, 1953, vol. 174(1), pp. 25-28. N.J. Petch, Journal of the Iron and Steel Institute, 1953, vol. 174(1), pp. 25-28.
46.
Zurück zum Zitat R.E. Stoller, S.J. Zinkle, J. Nuc. Mater., 2000, vol. 283, pp. 349-352.CrossRef R.E. Stoller, S.J. Zinkle, J. Nuc. Mater., 2000, vol. 283, pp. 349-352.CrossRef
48.
Zurück zum Zitat H.J. Frost, M.F. Ashby, Deformation Mechanism Maps, Pergamon Press, Oxford, UK, 1982. H.J. Frost, M.F. Ashby, Deformation Mechanism Maps, Pergamon Press, Oxford, UK, 1982.
49.
51.
Zurück zum Zitat D.W. Brown, I.J. Beyerlein, T.A. Sisneros, B. Clausen, C.N. Tome, Int. J. Plas., 2012, vol. 29, pp. 120-135.CrossRef D.W. Brown, I.J. Beyerlein, T.A. Sisneros, B. Clausen, C.N. Tome, Int. J. Plas., 2012, vol. 29, pp. 120-135.CrossRef
Metadaten
Titel
In Situ Neutron Diffraction Study of the Influence of Microstructure on the Mechanical Response of Additively Manufactured 304L Stainless Steel
verfasst von
D. W. Brown
D. P. Adams
L. Balogh
J. S. Carpenter
B. Clausen
G King
B. Reedlunn
T. A. Palmer
M. C. Maguire
S. C. Vogel
Publikationsdatum
10.10.2017
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 12/2017
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-017-4330-4

Weitere Artikel der Ausgabe 12/2017

Metallurgical and Materials Transactions A 12/2017 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.