Hydrogen Reduction Kinetics of Magnetite Concentrate Particles Relevant to a Novel Flash Ironmaking Process

A novel ironmaking technology is under development at the University of Utah. The purpose of this research was to determine comprehensive kinetics of the flash reduction reaction of magnetite concentrate particles by hydrogen. Experiments were carried out in the temperature range of 1423 K to 1673 K (1150 °C to 1400 °C) with the other experimental variables being hydrogen partial pressure and particle size. The nucleation and growth kinetics expression was found to describe the reduction rate of fine concentrate particles and the reduction kinetics had a 1/2-order dependence on hydrogen partial pressure and an activation energy of 463 kJ/mol. Unexpectedly, large concentrate particles reacted faster at 1423 K and 1473 K (1150 °C and 1200 °C), but the effect of particle size was negligible when the reduction temperature was above 1573 K (1300 °C). A complete reaction rate expression incorporating all these factors was formulated.