Effect of Silicon on the Desulfurization of Al-Killed Steels: Part II. Experimental Results and Plant Trials

Recent observations suggest that increased silicon levels improve ladle desulfurization of aluminum-killed steel. A kinetic model was developed and presented in part I of this paper, demonstrating that increased silicon levels in steel suppress the consumption of aluminum by parasitic reactions like silica reduction and FeO/MnO reduction, thus making more aluminum available at the interface for desulfurization. The results are increases in the rate and the extent of desulfurization. Predictions were compared with laboratory induction furnace melts using 1 kg of steel and 0.1 kg slag. The experimental results demonstrate the beneficial effect of silicon on the desulfurization reaction and that alumina can be reduced out of the slag and aluminum picked up by the steel, if the silicon content in the steel is high enough. The experimental results are in close agreement with the model predictions. Plant trials also show that with increased silicon content, both the rate and extent of desulfurization increase; incorporating silicon early into the ladle desulfurization process leads to considerable savings in aluminum consumption.