Characteristics of Non-metallic Inclusions in Steel Obtained from Different-Sized Samplers

verfasst von: Hang Liao, Shufeng Yang, Jingshe Li, Jie Feng

Erschienen in: Metallurgical and Materials Transactions B | Ausgabe 6/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

To determine the effect of sampler size on the detection of inclusions in liquid steel, four different-sized samplers were designed for industrial sampling from a continuous casting tundish. The samples were evaluated via scanning electron microscopy and energy-dispersive spectroscopy. With increasing sample size, the cooling rate of the sample and velocity for particle engulfment decreased. The extent of encapsulation of complex inclusions increased from 0 pct with the smallest sampler to 48.2 pct with the largest sampler. In the samplers that cooled at 41.2 and 26.7 K s−1, the major inclusions were calcium aluminates; in the larger samplers, which cooled more slowly at 8.2 and 1.0 K s−1, the complex inclusions predominately comprised Al2O3 + (Ca, Mn)S and Al2O3 + CaS, respectively. The sizes of the sulfides gradually increased with increasing sampler size; for example, the sulfide average diameter increased from 2.5 to 3.5 μm when the sampler inner diameter increased from 50 to 70 mm. The main direction of movement of the inclusions during the sampling process was upward.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H.C. Gao and X.H. Luan: Sci. Technol. Baotou Steel, 1996, vol. 1(4), pp. 92-94. H.C. Gao and X.H. Luan: Sci. Technol. Baotou Steel, 1996, vol. 1(4), pp. 92-94.
2.
Zurück zum Zitat W.J.Wang, X.H.Wang and J.M.Zhang: Contin. Cast., 2001, vol. 1(2), pp. 25-27. W.J.Wang, X.H.Wang and J.M.Zhang: Contin. Cast., 2001, vol. 1(2), pp. 25-27.
3.
Zurück zum Zitat X.J.Li, D.Q.Zhou and T.Hu: Yeh Chin Fen His Metall. Anal., 2001, vol. 21(5), pp. 71-72. X.J.Li, D.Q.Zhou and T.Hu: Yeh Chin Fen His Metall. Anal., 2001, vol. 21(5), pp. 71-72.
4.
Zurück zum Zitat Y.H.Zhang and S.Q.Li: Tianjin Metall. T’ien-chin Yeh Chin, 2003, vol. 1(3), pp. 13-15. Y.H.Zhang and S.Q.Li: Tianjin Metall. T’ien-chin Yeh Chin, 2003, vol. 1(3), pp. 13-15.
5.
Zurück zum Zitat Y.N.Wang, J.Yang and Y.P.Bao: Metall.Mater.Trans.B, 2014, vol. 45(6), pp. 2269-2278.CrossRef Y.N.Wang, J.Yang and Y.P.Bao: Metall.Mater.Trans.B, 2014, vol. 45(6), pp. 2269-2278.CrossRef
6.
Zurück zum Zitat K.Sakata and H.Suito: Metall.Mater.Trans.B, 1999, vol. 30(6), pp. 1053-1063.CrossRef K.Sakata and H.Suito: Metall.Mater.Trans.B, 1999, vol. 30(6), pp. 1053-1063.CrossRef
7.
Zurück zum Zitat Y.N.Wang, Y.P.Bao and M.Wang: Metall.Mater.Trans.B, 2013, vol. 44(5): pp. 1144-1154.CrossRef Y.N.Wang, Y.P.Bao and M.Wang: Metall.Mater.Trans.B, 2013, vol. 44(5): pp. 1144-1154.CrossRef
8.
Zurück zum Zitat F. Ruby-Meyer, A. Carré, and E. Hénault: European Commission, Euro25039 EN, 2012, p. 37. F. Ruby-Meyer, A. Carré, and E. Hénault: European Commission, Euro25039 EN, 2012, p. 37.
9.
10.
Zurück zum Zitat Z. Zhang, A. Tilliander, A. Karasev, et al.: ISIJ Int., 2010, vol. 50 (12), pp. 1746–55. Z. Zhang, A. Tilliander, A. Karasev, et al.: ISIJ Int., 2010, vol. 50 (12), pp. 1746–55.
11.
Zurück zum Zitat Z. Zhang, A. Tilliander, M. Iguchi: ISIJ Int., 2009, vol. 49(10), pp. 1522-1529.CrossRef Z. Zhang, A. Tilliander, M. Iguchi: ISIJ Int., 2009, vol. 49(10), pp. 1522-1529.CrossRef
12.
Zurück zum Zitat L. Wang, S. Yang and J. Li: Metall.Mater.Trans.B, 2016, vol. 47(1), pp. 99-107.CrossRef L. Wang, S. Yang and J. Li: Metall.Mater.Trans.B, 2016, vol. 47(1), pp. 99-107.CrossRef
13.
Zurück zum Zitat Z.H.Chen, J.B.Yue, S.X.Luo and X.L.Gan: Ind. Metro., 2011, vol. S2, pp. 20-22. Z.H.Chen, J.B.Yue, S.X.Luo and X.L.Gan: Ind. Metro., 2011, vol. S2, pp. 20-22.
14.
15.
Zurück zum Zitat H.T. Wang, Z.B. Xu and F.M. Wang: J. Univ. Sci. Technol. Beijing, 2007, vol. 29(9), pp. 884-889. H.T. Wang, Z.B. Xu and F.M. Wang: J. Univ. Sci. Technol. Beijing, 2007, vol. 29(9), pp. 884-889.
16.
Zurück zum Zitat Z.Q.Li, L.Wu and T.Liu: J.Northeast.Univ.,Nat.Sci., 2012, vol. 33(9), pp. 1294-1298. Z.Q.Li, L.Wu and T.Liu: J.Northeast.Univ.,Nat.Sci., 2012, vol. 33(9), pp. 1294-1298.
17.
Zurück zum Zitat M.Wintz, M.Bobadilla and J.Lehmann: ISIJ Int., 1995, vol. 35(6), pp. 715-722.CrossRef M.Wintz, M.Bobadilla and J.Lehmann: ISIJ Int., 1995, vol. 35(6), pp. 715-722.CrossRef
18.
Zurück zum Zitat H.Goto, K.Miyazawa and K.Yamaguchi: ISIJ Int., 1994, vol. 34(5), pp. 414-419.CrossRef H.Goto, K.Miyazawa and K.Yamaguchi: ISIJ Int., 1994, vol. 34(5), pp. 414-419.CrossRef
19.
Zurück zum Zitat H.Goto, K.Miyazawa and K.Tanaka: ISIJ Int., 1995, vol. 35(3), pp. 286-291.CrossRef H.Goto, K.Miyazawa and K.Tanaka: ISIJ Int., 1995, vol. 35(3), pp. 286-291.CrossRef
20.
Zurück zum Zitat H.Goto, K.Miyazawa and H.Honma: ISIJ Int., 1996, vol. 36(5), pp. 537-542.CrossRef H.Goto, K.Miyazawa and H.Honma: ISIJ Int., 1996, vol. 36(5), pp. 537-542.CrossRef
21.
22.
Zurück zum Zitat J.M.Cabrera-Marrero, V.Carreno-Galindo and R.D.Morales: ISIJ Int., 1998, vol. 38(8), pp. 812-821.CrossRef J.M.Cabrera-Marrero, V.Carreno-Galindo and R.D.Morales: ISIJ Int., 1998, vol. 38(8), pp. 812-821.CrossRef
23.
Zurück zum Zitat M.El-Bealy and B.G.Thomas: Metall.Mater.Trans.B, 1996, vol. 27(4), pp. 689-693.CrossRef M.El-Bealy and B.G.Thomas: Metall.Mater.Trans.B, 1996, vol. 27(4), pp. 689-693.CrossRef
24.
25.
Zurück zum Zitat H.M.Muhmond and H.Fredriksson: Metall.Mater.Trans.B, 2013, vol. 44(2), pp. 283-298.CrossRef H.M.Muhmond and H.Fredriksson: Metall.Mater.Trans.B, 2013, vol. 44(2), pp. 283-298.CrossRef
26.
Zurück zum Zitat Y.Wang, S.Sridhar and M.Valdez: Metall.Mater.Trans.B, 2002, vol, 33(4), pp. 625-632.CrossRef Y.Wang, S.Sridhar and M.Valdez: Metall.Mater.Trans.B, 2002, vol, 33(4), pp. 625-632.CrossRef
27.
28.
Zurück zum Zitat D.M.Stefanescu and A.V.Catalina: ISIJ Int., 1998, vol. 38(5), pp. 503-505.CrossRef D.M.Stefanescu and A.V.Catalina: ISIJ Int., 1998, vol. 38(5), pp. 503-505.CrossRef
29.
Zurück zum Zitat F.R. Juretzko, A.V. Catalina and D.M. Stefanescu: J. Jpn. Soc. Microgravity Appl., 1998, vol. 2(540), pp. 15. F.R. Juretzko, A.V. Catalina and D.M. Stefanescu: J. Jpn. Soc. Microgravity Appl., 1998, vol. 2(540), pp. 15.
30.
Zurück zum Zitat S. Lei, M. Jiang, D. Yang, et al.: J. Univ. Sci. Technol. B., 2013, vol. 11, pp. 1443–49. S. Lei, M. Jiang, D. Yang, et al.: J. Univ. Sci. Technol. B., 2013, vol. 11, pp. 1443–49.
31.
Zurück zum Zitat L.Holappa, M.Hämäläinen and M.Liukkonen: Ironmak.Steelmak., 2003, vol. 30(2), pp. 111-115.CrossRef L.Holappa, M.Hämäläinen and M.Liukkonen: Ironmak.Steelmak., 2003, vol. 30(2), pp. 111-115.CrossRef
32.
Zurück zum Zitat S.K.Choudhary and A.Ghosh: ISIJ Int., 2008, vol. 48(11), pp. 1552-1559.CrossRef S.K.Choudhary and A.Ghosh: ISIJ Int., 2008, vol. 48(11), pp. 1552-1559.CrossRef
Metadaten
Titel
Characteristics of Non-metallic Inclusions in Steel Obtained from Different-Sized Samplers
verfasst von
Hang Liao
Shufeng Yang
Jingshe Li
Jie Feng
Publikationsdatum
14.09.2017
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions B / Ausgabe 6/2017
Print ISSN: 1073-5615
Elektronische ISSN: 1543-1916
DOI
https://doi.org/10.1007/s11663-017-1085-7

Weitere Artikel der Ausgabe 6/2017

Metallurgical and Materials Transactions B 6/2017 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.