Synergistic Effects of Hydrogen and Stress on Corrosion of X100 Pipeline Steel in a Near-Neutral pH Solution

verfasst von: C. Zhang, Y. F. Cheng

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 9/2010

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this work, scanning vibrating electrode technique and local electrochemical impedance spectroscopy measurements were used to investigate the effects of stress and hydrogen on electrochemical corrosion behavior of a X100 pipeline steel in a near-neutral pH solution. The stress distribution on the test specimen was calculated using the finite element method. Results demonstrated that the hydrogen-charging enhances the local anodic dissolution of the steel, contributing to the formation of a layer of corrosion product. However, there is little difference of the charge-transfer resistance between the regions with and without hydrogen-charging due to rapid diffusion of hydrogen atoms throughout the specimen with time. When the local stress concentration is not significant enough to approach the yielding strength of the steel, the steel is still in a relatively stable state, and there is a uniform distribution of dissolution rate over the whole surface of the steel specimen. Although the stress-enhanced activation is not sufficient to result in an apparent difference of current density of the steel, the activation of the steel would activate dislocations, which serve as effective traps to the charged hydrogen atoms. With the increase of hydrogen concentration, the hydrogen-enhanced anodic dissolution becomes dominant.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat K.T. Corbett, R.R. Bowen, and C.W. Petersen, High Strength Steel Pipeline Economics, Int. J. Offshore Polar Eng., 2004, 14, p 75–79 K.T. Corbett, R.R. Bowen, and C.W. Petersen, High Strength Steel Pipeline Economics, Int. J. Offshore Polar Eng., 2004, 14, p 75–79
2.
Zurück zum Zitat F.J. Sánchez, B. Mishra, and D.L. Olson, Magnetization Effect on Hydrogen Absorption in High-strength Steels and its Implications, Scripta Mater., 2005, 53, p 1443–1448CrossRef F.J. Sánchez, B. Mishra, and D.L. Olson, Magnetization Effect on Hydrogen Absorption in High-strength Steels and its Implications, Scripta Mater., 2005, 53, p 1443–1448CrossRef
3.
Zurück zum Zitat C. Kalwa, H.G. Hillenbrand, and M. Gräf, High-strength Steel Pipes: New Developments and Applications, Onshore Pipeline Conference, Houston, Texas, June 10-11, 2002 C. Kalwa, H.G. Hillenbrand, and M. Gräf, High-strength Steel Pipes: New Developments and Applications, Onshore Pipeline Conference, Houston, Texas, June 10-11, 2002
4.
Zurück zum Zitat D. Porter, A. Laukkanen, P. Nevasmaa, K. Rahka, and K. Wallin, Performance of TMCP Steel with Respect to Mechanical Properties After Cold Forming and Post-forming Heat Treatment, Int. J. Pressure Vessels Piping, 2004, 81, p 867–877CrossRef D. Porter, A. Laukkanen, P. Nevasmaa, K. Rahka, and K. Wallin, Performance of TMCP Steel with Respect to Mechanical Properties After Cold Forming and Post-forming Heat Treatment, Int. J. Pressure Vessels Piping, 2004, 81, p 867–877CrossRef
5.
Zurück zum Zitat H.E. Minor, A. Kifani, M. Louah, Z. Azari, and G. Pluvinage, Fracture Toughness of High Strength Steel—Using the Notch Stress Intensity Factor and Volumetric Approach, Struct. Saf., 2003, 25, p 35–45CrossRef H.E. Minor, A. Kifani, M. Louah, Z. Azari, and G. Pluvinage, Fracture Toughness of High Strength Steel—Using the Notch Stress Intensity Factor and Volumetric Approach, Struct. Saf., 2003, 25, p 35–45CrossRef
6.
Zurück zum Zitat Y.Z. Wang, R.W. Revie, M.T. Shehata, R.N. Parkins, and K. Krist, Initiation of Environment Induced Cracking in Pipeline Steel: Micro-structural Correlation, International Pipeline Conference, ASME, Calgary, 1998. Y.Z. Wang, R.W. Revie, M.T. Shehata, R.N. Parkins, and K. Krist, Initiation of Environment Induced Cracking in Pipeline Steel: Micro-structural Correlation, International Pipeline Conference, ASME, Calgary, 1998.
7.
Zurück zum Zitat W. Zheng, Stress Corrosion Cracking of High (or Low) Strength Steels: Preliminary Results and Relevance to New Pipeline Systems, Presentations in the TransCanada Pipelines SCC Workshop, Calgary, Sept 22, 2006 W. Zheng, Stress Corrosion Cracking of High (or Low) Strength Steels: Preliminary Results and Relevance to New Pipeline Systems, Presentations in the TransCanada Pipelines SCC Workshop, Calgary, Sept 22, 2006
8.
Zurück zum Zitat W. Zheng, D. Billy, J. Li, J.T. Bowker, J.A. Gianetto, R.W. Revie, and G. Williams, Studies of Stress Corrosion Cracking of X100 Steel by a Full Scale Test Apparatus, Proceedings of the 2006 International Pipeline Conference, IPC2006-10084, Calgary, Canada, Sept 25-29, 2006 W. Zheng, D. Billy, J. Li, J.T. Bowker, J.A. Gianetto, R.W. Revie, and G. Williams, Studies of Stress Corrosion Cracking of X100 Steel by a Full Scale Test Apparatus, Proceedings of the 2006 International Pipeline Conference, IPC2006-10084, Calgary, Canada, Sept 25-29, 2006
9.
Zurück zum Zitat M.A. Almonsour, “Sulfide Stress Corrosion Resistance of X100 Steel in H2S Environments,” MSc thesis, University of British Columbia, Vancouver, 2007 M.A. Almonsour, “Sulfide Stress Corrosion Resistance of X100 Steel in H2S Environments,” MSc thesis, University of British Columbia, Vancouver, 2007
10.
Zurück zum Zitat R.N. Parkins, A Review of Stress Corrosion Cracking of High Pressure Gas Pipelines, Corrosion 2000, NACE, Houston, 2000, Paper No. 363 R.N. Parkins, A Review of Stress Corrosion Cracking of High Pressure Gas Pipelines, Corrosion 2000, NACE, Houston, 2000, Paper No. 363
11.
Zurück zum Zitat B.Y. Fang, A. Atrens, J.Q. Wang, E.H. Han, Z.Y. Zhu, and W. Ke, Review of Stress Corrosion Cracking of Pipeline Steels in “Low” and “High” pH Solutions, J. Mater. Sci., 2003, 38, p 127–132CrossRef B.Y. Fang, A. Atrens, J.Q. Wang, E.H. Han, Z.Y. Zhu, and W. Ke, Review of Stress Corrosion Cracking of Pipeline Steels in “Low” and “High” pH Solutions, J. Mater. Sci., 2003, 38, p 127–132CrossRef
12.
Zurück zum Zitat M. Baker Jr., Stress Corrosion Cracking Studies, Integrity Management Program DTRS56-02-D-70036, Department of Transportation, Office and Pipeline Safety, 2004 M. Baker Jr., Stress Corrosion Cracking Studies, Integrity Management Program DTRS56-02-D-70036, Department of Transportation, Office and Pipeline Safety, 2004
13.
Zurück zum Zitat National Energy Board, Report of Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines, MH-2-95, November 1996 National Energy Board, Report of Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines, MH-2-95, November 1996
14.
Zurück zum Zitat Y.F. Cheng, Thermodynamically Modeling the Interactions of Hydrogen, Stress and Anodic Dissolution at Crack-tip During Near-neutral pH SCC in Pipelines, J. Mater. Sci., 2007, 42, p 2701–2705CrossRefADS Y.F. Cheng, Thermodynamically Modeling the Interactions of Hydrogen, Stress and Anodic Dissolution at Crack-tip During Near-neutral pH SCC in Pipelines, J. Mater. Sci., 2007, 42, p 2701–2705CrossRefADS
15.
Zurück zum Zitat C.W. Du, X.G. Li, P. Liang, Z.Y. Liu, G.F. Jia, and Y.F. Cheng, Effects of Microstructure on Corrosion of X70 Pipe Steel in an Alkaline Soil, J. Mater. Eng. Perform., 2009, 18, p 216–220CrossRef C.W. Du, X.G. Li, P. Liang, Z.Y. Liu, G.F. Jia, and Y.F. Cheng, Effects of Microstructure on Corrosion of X70 Pipe Steel in an Alkaline Soil, J. Mater. Eng. Perform., 2009, 18, p 216–220CrossRef
16.
Zurück zum Zitat R.N. Parkins, W.K. Blanchards, Jr., and B.S. Delanty, Transgranular Stress Corrosion Cracking of High-pressure Pipelines in Contact with Solutions of Near Neutral pH, Corrosion, 1994, 50, p 394–408CrossRef R.N. Parkins, W.K. Blanchards, Jr., and B.S. Delanty, Transgranular Stress Corrosion Cracking of High-pressure Pipelines in Contact with Solutions of Near Neutral pH, Corrosion, 1994, 50, p 394–408CrossRef
17.
Zurück zum Zitat L. Niu and Y.F. Cheng, Corrosion Behaviour of X-70 Pipe Steel in Near-neutral pH Solution, Appl. Surf. Sci., 2007, 253, p 8626–8631CrossRefADS L. Niu and Y.F. Cheng, Corrosion Behaviour of X-70 Pipe Steel in Near-neutral pH Solution, Appl. Surf. Sci., 2007, 253, p 8626–8631CrossRefADS
18.
Zurück zum Zitat W. Bouaeshi, S. Ironside, and R. Eadie, Research and Cracking Implications from an Assessment of Two Variants of Near-neutral pH Crack Colonies in Liquid Pipelines, Corrosion, 2007, 63, p 648–660CrossRef W. Bouaeshi, S. Ironside, and R. Eadie, Research and Cracking Implications from an Assessment of Two Variants of Near-neutral pH Crack Colonies in Liquid Pipelines, Corrosion, 2007, 63, p 648–660CrossRef
19.
Zurück zum Zitat Y.F. Cheng and L. Niu, Mechanism for Hydrogen Evolution Reaction on Pipeline Steel in Near-neutral pH Solution, Electrochem. Commun., 2007, 9, p 558–562CrossRef Y.F. Cheng and L. Niu, Mechanism for Hydrogen Evolution Reaction on Pipeline Steel in Near-neutral pH Solution, Electrochem. Commun., 2007, 9, p 558–562CrossRef
20.
Zurück zum Zitat B. Gu, J. Luo, and X. Mao, Hydrogen-facilitated Anodic Dissolution-type Stress Corrosion Cracking of Pipeline Steels in Near-neutral pH Solution, Corrosion, 1999, 55, p 96–108CrossRef B. Gu, J. Luo, and X. Mao, Hydrogen-facilitated Anodic Dissolution-type Stress Corrosion Cracking of Pipeline Steels in Near-neutral pH Solution, Corrosion, 1999, 55, p 96–108CrossRef
21.
Zurück zum Zitat L.J. Qiao, J.L. Luo, and X. Mao, Hydrogen Evolution and Enrichment Around Stress Corrosion Crack Tips of Pipeline Steels in Dilute Bicarbonate Solution, Corrosion, 1998, 54, p 115–120CrossRef L.J. Qiao, J.L. Luo, and X. Mao, Hydrogen Evolution and Enrichment Around Stress Corrosion Crack Tips of Pipeline Steels in Dilute Bicarbonate Solution, Corrosion, 1998, 54, p 115–120CrossRef
22.
Zurück zum Zitat L. Zhang, X.G. Li, C.W. Du, and Y.F. Cheng, Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in a CO2-containing Solution, J. Mater. Eng. Perform., 2009, 18, p 319–323CrossRef L. Zhang, X.G. Li, C.W. Du, and Y.F. Cheng, Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in a CO2-containing Solution, J. Mater. Eng. Perform., 2009, 18, p 319–323CrossRef
23.
Zurück zum Zitat T.M. Ahmed, S.B. Lambert, R. Sutherby, and A. Plumtrel, Cyclic Crack Growth of X-60 Pipeline Steel in a Neutral Dilute Solution, Corrosion, 1997, 53, p 581–590CrossRef T.M. Ahmed, S.B. Lambert, R. Sutherby, and A. Plumtrel, Cyclic Crack Growth of X-60 Pipeline Steel in a Neutral Dilute Solution, Corrosion, 1997, 53, p 581–590CrossRef
24.
Zurück zum Zitat T.R. Jack, B. Erno, and K. Krist, Generation of Near-neutral pH and High pH SC Environments on Buried Pipelines, Corrosion/2000, NACE, Houston, TX, 2000, Paper No. 362 T.R. Jack, B. Erno, and K. Krist, Generation of Near-neutral pH and High pH SC Environments on Buried Pipelines, Corrosion/2000, NACE, Houston, TX, 2000, Paper No. 362
25.
Zurück zum Zitat J.A. Beavers, C.L. Durr, B.S. Delanty, D.M. Owen, and R.L. Sutherby, Near-neutral pH SCC: Crack Propagation in Susceptible Soil Environments, Corrosion/2001, NACE, Houston, TX, 2001, Paper No. 217 J.A. Beavers, C.L. Durr, B.S. Delanty, D.M. Owen, and R.L. Sutherby, Near-neutral pH SCC: Crack Propagation in Susceptible Soil Environments, Corrosion/2001, NACE, Houston, TX, 2001, Paper No. 217
26.
Zurück zum Zitat R.R. Fessler and K. Krist, Research Challenges Regarding Stress Corrosion Cracking of Pipelines, Corrosion/2000, NACE, Houston, TX, 2000, Paper No. 370 R.R. Fessler and K. Krist, Research Challenges Regarding Stress Corrosion Cracking of Pipelines, Corrosion/2000, NACE, Houston, TX, 2000, Paper No. 370
27.
Zurück zum Zitat X. Tang and Y.F. Cheng, Micro-electrochemical Characterization of the Effect of Applied Stress on Local Anodic Dissolution Behavior of Pipeline Steel Under Near-neutral pH Condition, Electrochim. Acta, 2009, 54, p 1499–1505CrossRef X. Tang and Y.F. Cheng, Micro-electrochemical Characterization of the Effect of Applied Stress on Local Anodic Dissolution Behavior of Pipeline Steel Under Near-neutral pH Condition, Electrochim. Acta, 2009, 54, p 1499–1505CrossRef
28.
Zurück zum Zitat G.Z. Meng, C. Zhang, and Y.F. Cheng, Effects of Corrosion Product Deposit on the Subsequent Cathodic and Anodic Reactions of X-70 Steel in Near-neutral pH Solution, Corros. Sci., 2008, 50, p 3116–3122CrossRef G.Z. Meng, C. Zhang, and Y.F. Cheng, Effects of Corrosion Product Deposit on the Subsequent Cathodic and Anodic Reactions of X-70 Steel in Near-neutral pH Solution, Corros. Sci., 2008, 50, p 3116–3122CrossRef
29.
Zurück zum Zitat C.F. Dong, A.Q. Fu, X.G. Li, and Y.F. Cheng, Localized EIS Characterization of Corrosion of Steel at Coating Defect Under Cathodic Protection, Electrochim. Acta, 2008, 54, p 628–633CrossRef C.F. Dong, A.Q. Fu, X.G. Li, and Y.F. Cheng, Localized EIS Characterization of Corrosion of Steel at Coating Defect Under Cathodic Protection, Electrochim. Acta, 2008, 54, p 628–633CrossRef
30.
Zurück zum Zitat X. Tang and Y.F. Cheng, Localized Dissolution Electrochemistry at Surface Irregularities of Pipeline Steel, Appl. Surf. Sci., 2008, 254, p 5199–5205CrossRefADS X. Tang and Y.F. Cheng, Localized Dissolution Electrochemistry at Surface Irregularities of Pipeline Steel, Appl. Surf. Sci., 2008, 254, p 5199–5205CrossRefADS
31.
Zurück zum Zitat M.C. Li and Y.F. Cheng, Mechanistic Investigation of Hydrogen-enhanced Anodic Dissolution of X-70 Pipe Steel and its Implication on Near-neutral pH SCC of Pipelines, Electrochim. Acta, 2007, 52, p 8111–8117CrossRef M.C. Li and Y.F. Cheng, Mechanistic Investigation of Hydrogen-enhanced Anodic Dissolution of X-70 Pipe Steel and its Implication on Near-neutral pH SCC of Pipelines, Electrochim. Acta, 2007, 52, p 8111–8117CrossRef
32.
Zurück zum Zitat Y.F. Cheng and X. Tang, Micro-electrochemical Characterization of the Synergism of Hydrogen and Stress in Anodic Dissolution of Steel and its Implications on Pipeline Stress Corrosion Cracking, Proceeding of the 6th International Pipeline Conference, IPC2008-64142, Calgary, Canada, Sept 29 to Oct 3, 2008 Y.F. Cheng and X. Tang, Micro-electrochemical Characterization of the Synergism of Hydrogen and Stress in Anodic Dissolution of Steel and its Implications on Pipeline Stress Corrosion Cracking, Proceeding of the 6th International Pipeline Conference, IPC2008-64142, Calgary, Canada, Sept 29 to Oct 3, 2008
33.
Zurück zum Zitat M.Z. Yang, J.L. Luo, Q. Yang, L.J. Qiao, Z.Q. Qin, and P.R. Norton, Effects of Hydrogen on Semiconductivity of Passive Film and Corrosion Behavior of 310 Stainless Steel, J. Electrochem. Soc., 1999, 146, p 2107–2112CrossRef M.Z. Yang, J.L. Luo, Q. Yang, L.J. Qiao, Z.Q. Qin, and P.R. Norton, Effects of Hydrogen on Semiconductivity of Passive Film and Corrosion Behavior of 310 Stainless Steel, J. Electrochem. Soc., 1999, 146, p 2107–2112CrossRef
34.
Zurück zum Zitat E. Sanjuan, “Studies of Corrosion and Stress Corrosion Cracking Behavior of High-strength Pipeline Steels in Carbonate/Bicarbonate Solutions,” MSc thesis, University of Calgary, Canada, March 2008 E. Sanjuan, “Studies of Corrosion and Stress Corrosion Cracking Behavior of High-strength Pipeline Steels in Carbonate/Bicarbonate Solutions,” MSc thesis, University of Calgary, Canada, March 2008
Metadaten
Titel
Synergistic Effects of Hydrogen and Stress on Corrosion of X100 Pipeline Steel in a Near-Neutral pH Solution
verfasst von
C. Zhang
Y. F. Cheng
Publikationsdatum
01.12.2010
Verlag
Springer US
Erschienen in
Journal of Materials Engineering and Performance / Ausgabe 9/2010
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI
https://doi.org/10.1007/s11665-009-9579-3

Weitere Artikel der Ausgabe 9/2010

Journal of Materials Engineering and Performance 9/2010 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.