Abstract
The thermal diffusivity of Fe-Al alloys in the concentration range 22 to 50 at.% Al was measured within a temperature range of 20 to 600 °C. The thermal diffusivity of the Fe-25 and 28 at.% Al alloys decreases with increasing temperature up to the Curie temperature, and then it increases up to the temperature when the D03 ↔ B2 transformation occurs. The thermal diffusivity of Fe-22 at.% Al alloys increases with rising temperature up to the temperature when D03 ↔ B2 transformation occurs, and then it decreases. A further decrease in thermal diffusivity follows up to the Curie temperature. The thermal diffusivity of Fe-34 and Fe-40 at.% Al increases monotonically with the rising temperature. The thermal diffusivity of Fe-50 at.% Al alloys decreases only up to 100 °C, and does not change any further with increasing temperature. Thermal conductivity is the highest for Fe-25 and Fe-50 at.% Al alloys at room temperature. Thermal conductivity rises for all studied alloys with increasing temperature. The smallest increase was registered for Fe-25 at.% Al alloys.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
L. Nordheim: Ann. Physik 1931, vol. 9, p. 607.
C.H. Johansson and J.O. Linde: Ann. Physik, 1936, vol. 25, p. 1.
R. Feder and R.W. Cahn: Phil. Mag., 1960, vol. 5, p. 343.
H.R. Shanks, A.H. Klein, and G.C. Danielson: J. Appl. Phys., 1967, vol. 18, p. 7.
G.R. Caskey, J.M. Franz, and D.L. Sellmyer: J. Phys. Chem. Solids, 1973, vol. 34, p. 1179.
R. Berman: Thermal Conduction in Solids, Clarendon Press, Oxford, United Kingdom, 1976.
R. Taylor and C.M. Fowler: Thermal Conductivity, V.V. Mirkovich, ed., Plenum Press, New York, NY, 1978, vol. 15, p. 453.
O. Kubaschewski: Iron-Binary Phase Diagrams, Springer-Verlag, Berlin, 1982, vol. 5.
A. Rudajevova: Mater. Res. Bull., 1991, vol. 26, p. 1363.
T.A. Hyde, C.H. Sellers, J.K. Wright, and R.N. Wright: Scripta Metall. Mater., 1994, vol. 330, p. 113.
S. Hanai, Y. Terada, K. Nakagawa, T. Mohri, and T. Suzuki: Intermetallics, 1995, vol. 3, p. 347.
V.E. Zinovjev, N.B. Puskarova, J.A. Manzujev, S.G. Taluc, V.I. Gorbatov, B.V. Vlasov, and M.I. Sanbakova: Eizika Metallov i Metallovedenije, 1995, vol. 47, p. 79.
S. Hanai, Y. Terada, K. Ohkubo, T. Mohri, and T. Suzuki: Intennetallics, 1996, vol. 4, p. S41.
I.G. Korsunov, N.B. Puskareva, C.G. Taluc, and V.I. Gorbatov: Eizika Metallov i Metallovedenije, 1998, vol. 85, p. 182.
A.C. Lilly, S.C. Deevi, and Z.P. Gibbs: Mater. Sci. Eng., 1998, vol. A258, p. 42.
Y. Nishimo: Mater. Sci. Eng., 1998, vol. A258, p. 50.
Y. Terada, J. Nakata, T. Mohri, and T. Suzuki: Intermetallics, 1998, vol. 6, p. 479.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Rudajevová, A., Buriánek, J. Determination of thermal diffusivity and thermal conductivity of Fe-Al alloys in the concentration range 22 to 50 at.% Al. JPE 22, 560–563 (2001). https://doi.org/10.1007/s11669-001-0075-1
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11669-001-0075-1