Abstract
The use of duplex stainless steels (DSS) in nuclear power generation systems is limited by thermal instability that leads to embrittlement in the temperature range of 204°C to 538°C. New lean-grade alloys, such as 2101, offer the potential to mitigate these effects. Thermal embrittlement was quantified through impact toughness and hardness testing on samples of alloy 2101 after aging at 427°C for various durations (1–10,000 h). Additionally, atom probe tomography (APT) was utilized in order to observe the kinetics of α–α′ separation and G-phase formation. Mechanical testing and APT data for two other DSS alloys, 2003 and 2205, were used as a reference to 2101. The results show that alloy 2101 exhibits superior performance compared to the standard-grade DSS alloy 2205 but inferior to the lean-grade alloy 2003 in mechanical testing. APT data demonstrate that the degree of α–α′ separation found in alloy 2101 closely resembles that of 2205 and greatly exceeds 2003. Additionally, contrary to what was observed in 2003, 2101 demonstrated G-phase like precipitates after long aging times, although precipitates were not as abundant as was observed in 2205.
Similar content being viewed by others
References
R. Gunn, Duplex Stainless Steels: Microstructure, Properties and Applications (New York: Elsevier, 1997), pp. 14–47.
H.D. Solomon and T.M. Devine, Duplex Stainless Steels: A Tale of Two Phases (Materials Park: American Society for Metals, 1982), pp. 693–756.
J.D. Tucker, M.K. Miller, and G.A. Young, Acta Mater. 87, 15 (2015).
I. Shuro, H.H. Kuo, T. Sasaki, K. Hono, Y. Todaka, and M. Umemoto, Mater. Sci. Eng., A 552, 194 (2012).
S.L. Li, H.L. Zhang, Y.L. Wang, S.X. Li, K. Zheng, F. Xue, and X.T. Wang, Mater. Sci. Eng., A 564, 85 (2013).
D.H. Kang and W.H. Lee, Metall. Mater. Trans. A 43, 4678 (2012).
J.D. Tucker, G.A. Young Jr, and D.R. Eno, Solid State Phenom. 172–174, 331 (2011).
S. Lee, C.-Y. Lee, and Y.-K. Lee, J. Alloys Compd. 628, 46 (2015).
G.A. Young, J.D Tucker, N. Lewis, E. Plesko, and P. Sander, Proceedings of the 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, Colorado Springs, CO (2011), pp. 2369–2380.
ASTM Standard E23, 12c, Standard Test Methods for Notched Bar Impact Testing of Metallic Materials, 2012.
ASTM Standard E384, 11e1, Standard Test Method for Knoop and Vickers Hardness of Materials, 2011.
K. Thompson, D. Lawrence, D. Larson, J. Olson, and T. Kelly, Ultramicroscopy 107, 131 (2007).
J. Zhou, J. Odqvist, N. Thuvander, and P. Hedstom, Microsc. Microanal. 19, 665 (2013).
P. Hedström, F. Huyan, J. Zhou, S. Wessman, M. Thuvander, and J. Odqvist, Mater. Sci. Eng., A 574, 123 (2013).
J. Charles, Duplex Stainless Steel—a Review after DSS ’07 held in Grado, presented at the Revue de Me´tallurgie, Grado, Italy (2008).
Acknowledgements
This research was supported by ORNL’s Center for Nanophase Materials Sciences (CNMS), which is a DOE Office of Science User Facility.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Garfinkel, D.A., Poplawsky, J.D., Guo, W. et al. Phase Separation in Lean-Grade Duplex Stainless Steel 2101. JOM 67, 2216–2222 (2015). https://doi.org/10.1007/s11837-015-1581-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-015-1581-7