Abstract
3 Mol% of europium doped strontium aluminate (SrAl2O4:Eu2 + ) coatings on silicon substrates were prepared by electrostatic spray deposition method using a salted sol–gel derived solution as a starting material. As-deposited films at 100°C for 5 h were heated at 1100°C for 2 h under a reducing ambient atmosphere of 95%N2 + 5%H2. Nanocrystalline SrAl2O4 film was confirmed by surface morphological and crystallographic analyses. Monitored at 520 nm, the excitation spectrum showed a broad band from 300 ~ 500 nm and the emission intensity showed a maximum yellow peak intensity at 512 nm with a broad band from 460 ~ 610 nm.
References
Avdeev M, Yakolev S, Yaremchenko A and Kharton V 2007 J. Solid State Chem. 180 3535
Chergn I and Chen T M 2001 J. Mater. Res. 16 644
Choi S H, Kim N H, Yun Y H and Choi S C 2006 J. Ceram. Proc. Res. 7 62
Clabau F, Rocquefelte X, Jobic S, Deniard P, Whangbo M H, Garcia A and Le Mercier T 2005 Chem. Mater. 17 3904
Escribano P, Marchal M, Sanjuán M L, Alonso-Gutiérrez P, Julián B and Cordoncillo E 2005 J. Solid State Chem. 178 1978
Haranath D, Shanker V, Chander H and Sharma P 2003 J. Phys. D: Appl. Phys. 36 2244
Henderson C M B and Taylor D 1982 Miner. Mag. 45 111
Hwang K S, Jeong J H, Jeon Y S, Jeon K O and Kim B H 2007 Ceram. Int. 33 505
Jia D 2003 Opt. Mater. 22 65
Katsumata T, Nabae T, Sasajima K and Matsuzawa T 1998 J. Cryst. Growth 183 361
Zhang R, Han G, Zhang L and Yang B 2009 Mater. Chem. & Phys. 113 255
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
HWANG, KS., KANG, BA., KIM, SD. et al. Cost-effective electrostatic-sprayed SrAl2O4:Eu2 + phosphor coatings by using salted sol–gel derived solution. Bull Mater Sci 34, 1059–1062 (2011). https://doi.org/10.1007/s12034-011-0128-y
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-011-0128-y