Abstract
In this work, ionic liquid (IL) intercalated V2O5 (IL-V2O5) nanorods have been synthesized through the IL-assisted hydrothermal method using imidazolium-based functionalized IL at 130 ∘C for 3 days. The structure and morphology of the obtained product was characterized using various techniques. X-ray diffraction pattern reveals the intercalation of IL at 2 𝜃=7∘ in orthorhombic V2O5. The Fourier transform infrared spectrum shows a band at 1044 cm−1, which could be assigned to stretching vibration of terminal vanadyl (V =O), sensitive to cation intercalation between vanadium oxide layers. UV–vis absorption spectrum of IL-V2O5 nanorods and calcined V2O5 nanoparticles show a maximum absorbance at 402 and 420 nm, respectively. The morphology of the product was investigated by scanning electron microscopy and transition electron microscopy (TEM). TEM analysis reveals the nanorods with thickness of 30–50 nm.
Similar content being viewed by others
References
Schlesser R, Dalmau R, Zhuang D, Collazo R and Sitar Z 2005, J. Cryst. Growth 281 75
Chandrappa G T, Chithaiah P, Ashoka S and Livage J 2011, Inorg. Chem. 50 7421
Duan X, Niu C, Sahi V, Chen J, Parce J, Empedocles S and Goldman J 2003, Nature 425 274
Zhong Z, Wang D, Cui Y, Bockrath M and Lieber C M 2003, Science 302 1377
Livage J 1991, Chem. Mater. 3 578
Moshfegh A Z and Ignatiev A 1991, Thin Solid Films 198 251
Sphar M E, Stoschitzki B P, Nesper R, Hass O and Novak P 1999, J. Electrochem. Soc. 146 2780
Cao J, Musfeldt J L, Mazumdar S, Chernova N A and Whittingham M S 2007, Nano Lett. 7 2351
Barboux P, Baffier N, Morineau R, Livage J, Goodenough J B, Jensen J and Poiter A 1985 Solid state protonic conductors III (Paris: Odense University Press) p 173
Livage J 1984, Mater. Res. Soc. Symp. Proc. 32 125
Nagaraju G and Chandrappa G T 2012, Mater. Res. Bull. 47 3216
Wang N, Chen W and Mail D Y 2008, J. Solid State Chem. 181 652
Zoubi M A, Hala K F and Endres F. 2009, J. Mater. Sci. 44 1363
Durupthy O, Steunou N, Coradin T, Maquet J, Bonhomme C and Livage J 2005, J. Mater. Chem. 15 1090
Han W, Fan S, Li Q and Hu Y 1997, Science 277 1287
Li Y D, Liao H W, Ding Y, Fan Y, Zhang Y and Qian Y T 1999 Inorg. Chem. 381
Pinna N, Wild U, Urban J and Schlogl R 2003, Adv. Mater. 15 329
Ribeiro W A C, Leite E R and Mastelaro V R 2009, Cryst. Growth Des. 9 3626
Rothschild A, Sloan J and Tenne R 2000, J. Am. Chem. Soc. 122 5169
Wang Y and Cao G 2006, Chem. Mater. 18 2787
Zhou F, Zhao X, Yuan C and Li L 2008, Cryst. Growth Des. 8 7
Nagaraju G 2012, Z. Anorg. Allg. Chem. 638 2286
Zhou Y, Bao Q, Tang L L, Zhong Y and Loh K P 2009, Chem. Mater. 2 2950
Dupont J, De Souza R F and Suarez P A Z 2002, Chem. Rev. 102 3667
Dupont J and Jackson D S 2010, Chem. Soc. Rev. 39 1780
Hu H, Yang H, Huang P, Cui D, Peng Y, Zhang J, Lu F, Lian J and Shi D 2010, Chem. Commun. 46 3866
Cassol C C, Ebeling G, Ferrera B and Dupont J 2006, Adv. Synth. Catal. 348 243
Israel E and Waches 2001 Raman spectroscopy of catalysis, Hand book of Raman spectroscopy (Pennsylvania: CRC Press, Lehigh University) p 799
Nagaraju G, Ebeling G, Goncalves R V, Teixeira S R, Weibel D E and Dupont J 2013, J. Mol. Catal. A – Chem. 378 213
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
MANJUNATH, K., D’SOUZA, V., DUPONT, J. et al. Ionic liquid intercalated V2O5 nanorods: synthesis and characterization. Bull Mater Sci 38, 1309–1313 (2015). https://doi.org/10.1007/s12034-015-1015-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-015-1015-8