Abstract
CoFe2O4-BaTiO3 composites were prepared using conventional ceramic double sintering process with various compositions. Presence of two phases in the composites was confirmed using X-ray diffraction. The dc resistivity and thermoemf as a function of temperature in the temperature range 300 K to 600 K were measured. Variation of dielectric constant (ɛ′) with frequency in the range 100 Hz to 1 MHz and also with temperature at a fixed frequency of 1 kHz was studied. The ac conductivity was derived from dielectric constant (ɛ′) and loss tangent (tan δ). The nature of conduction is discussed on the basis of small polaron hopping model. The static value of magnetoelectric conversion factor has been studied as a function of magnetic field.
Similar content being viewed by others
References
J Van Suchetelene, Phillips Res. Rept. 27, 28 (1972)
A M J G Van Run, D R Terrel and J H Scholing, J. Mater. Sci. 9, 1710 (1974)
A Hanumaiah, T Bhimashankaran, S V SUryanarayana and G S Kumar, Bull. Mater. Sci. 18, 93 (1995)
A E Gelyasin, V M Latetin and L I Trofimovich, Sov. Phys. Tech. Phys. 33, 11 (1998)
S V Suryanaryana, Bull. Mater. Sci. 17, 1259 (1994)
S A Patil, Ph.D. Thesis (Shivaji University, Kolhapur, 1981)
S M Otari, V B Kadam, S R Sawant and S A Patil, Int. J. Pure Appl. Phys. 28, 248 (1990)
E J W Verwey and Heilan, J. Chem. Phys. 15, 174 (1947)
Ph Tailheades, Ch Sarada, P Milard and A Rousset, J. Magn. Magn. Mater. 962, 104 (1992)
I G Austin and N F Mott, Adv. Phys. 18, 41 (1969)
C G Koops, Phys. Rev. 83, 121 (1951)
P V Reddy and T S J Rao, Less common metals 86, 255 (1982)
K Kamiyoshi, Sci. Rept. Res. Inst. Tohoku Univ. A3, 716 (1951)
Volger, Progress in Semiconductors 4, 207 (1960)
D Alder and J Feinleib, Phys. Rev. B2, 3112 (1970)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mahajan, R., Patankar, K., Kothale, M. et al. Magnetoelectric effect in cobalt ferrite-barium titanate composites and their electrical properties. Pramana - J Phys 58, 1115–1124 (2002). https://doi.org/10.1007/s12043-002-0227-9
Issue Date:
DOI: https://doi.org/10.1007/s12043-002-0227-9
Keywords
- X-ray diffraction
- CoFe2O4-BaTiO3
- dielectric constant
- ac conductivity
- hopping model
- magnetoelectric effect