Effect of Rotary Forging on Microstructure Evolution and Mechanical Properties of Aluminum Alloy/Copper Bimetallic Material

verfasst von: S. O. Rogachev, V. A. Andreev, V. S. Yusupov, S. A. Bondareva, V. M. Khatkevich, E. V. Nikolaev

Erschienen in: Metals and Materials International | Ausgabe 4/2022

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The influence of a degree of strain by rotary forging, as well as post-deformation annealing on the structure and mechanical properties of a clad aluminum alloy/copper bimetallic material was studied. Rotary forging of the initial bimetallic billet was carried out step by step from a diameter of 20.1 mm to a diameter of 2.4 mm. Rotary forging of the aluminum alloy/copper bimetallic material to a diameter of 5.3 mm leads to the formation of a mixed fine-grained and nanocrystalline oriented structure in an aluminum shell and to a decrease in the average grain size by 4.5 times and to an increase in the density of crystalline defects in a copper core. A reduction in the aluminum alloy/copper bimetallic material diameter to 2.4 mm (with intermediate annealing) leads to the formation of a fine-grained elongated grain-subgrain oriented structure in the aluminum shell and to the formation of a mixed cellular and subgrain structure in a copper core. Rotary forging leads to a significant increase in the strength of the aluminum alloy/copper bimetallic material and to a decrease in ductility. The optimal combination of increased strength and satisfactory ductility provides post-deformation annealing.

Graphic Abstract

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat M.F. Ashby, Y.J.M. Brechet, Acta Mater. 51, 5801 (2003) M.F. Ashby, Y.J.M. Brechet, Acta Mater. 51, 5801 (2003)
2.
Zurück zum Zitat H.H. Kim, M.S. Lee, C.G. Kang, Mater. Manuf. Process. 28, 892 (2013) H.H. Kim, M.S. Lee, C.G. Kang, Mater. Manuf. Process. 28, 892 (2013)
3.
Zurück zum Zitat O. Bouaziz, Scripta Mater. 68, 28 (2013) O. Bouaziz, Scripta Mater. 68, 28 (2013)
4.
Zurück zum Zitat A. Molotnikov, R. Gerbrand, O. Bouaziz, Y. Estrin, Adv. Eng. Mater. 15, 728 (2013) A. Molotnikov, R. Gerbrand, O. Bouaziz, Y. Estrin, Adv. Eng. Mater. 15, 728 (2013)
5.
Zurück zum Zitat A.Y. Nalivaiko, A.N. Arnautova, S.V. Zmanovsky, D.Y. Ozherelkov, P.K. Shurkin, A.A. Gromov, J. Alloy. Compd. 825, 154024 (2020) A.Y. Nalivaiko, A.N. Arnautova, S.V. Zmanovsky, D.Y. Ozherelkov, P.K. Shurkin, A.A. Gromov, J. Alloy. Compd. 825, 154024 (2020)
7.
Zurück zum Zitat I.-K. Kim, S.I. Hong, Mater. Design 47, 590 (2013) I.-K. Kim, S.I. Hong, Mater. Design 47, 590 (2013)
8.
Zurück zum Zitat M. Zebardast, A.K. Taheri, J. Mater. Process. Tech. 211, 1034 (2011) M. Zebardast, A.K. Taheri, J. Mater. Process. Tech. 211, 1034 (2011)
9.
Zurück zum Zitat N. Ahmed, J. Mech. Work. Technol. 2, 19 (1978) N. Ahmed, J. Mech. Work. Technol. 2, 19 (1978)
10.
Zurück zum Zitat Y. Mitani, H. Balmori, in Strength of Metals and Alloys (ICSMA 6), Proceedings of the 6th International Conference, Melbourne, Australia, August 16-20, 1982 (Pergamon Press, Oxford, 1983), pp. 983–988 Y. Mitani, H. Balmori, in Strength of Metals and Alloys (ICSMA 6), Proceedings of the 6th International Conference, Melbourne, Australia, August 16-20, 1982 (Pergamon Press, Oxford, 1983), pp. 983–988
11.
Zurück zum Zitat R.Z. Valiev, R.K. Islamgaliev, I.V. Alexandrov, Prog. Mater. Sci. 45, 103 (2000) R.Z. Valiev, R.K. Islamgaliev, I.V. Alexandrov, Prog. Mater. Sci. 45, 103 (2000)
12.
Zurück zum Zitat R.Z. Valiev, Y. Estrin, Z. Horita, T.G. Langdon, M.J. Zehetbauer, Y.T. Zhu, Mater. Res. Lett. 4, 1 (2016) R.Z. Valiev, Y. Estrin, Z. Horita, T.G. Langdon, M.J. Zehetbauer, Y.T. Zhu, Mater. Res. Lett. 4, 1 (2016)
13.
Zurück zum Zitat R.Z. Valiev, A.P. Zhilyaev, T.G. Langdon, Bulk Nanostructured Materials: Fundamentals and Applications (Wiley, New Jersey, 2014) R.Z. Valiev, A.P. Zhilyaev, T.G. Langdon, Bulk Nanostructured Materials: Fundamentals and Applications (Wiley, New Jersey, 2014)
14.
Zurück zum Zitat I.V. Alexandrov, Met. Mater. Int. 7, 565 (2001) I.V. Alexandrov, Met. Mater. Int. 7, 565 (2001)
15.
Zurück zum Zitat Y. Beygelzimer, Y. Estrin, R. Kulagin, Adv. Eng. Mater. 17, 1853 (2015) Y. Beygelzimer, Y. Estrin, R. Kulagin, Adv. Eng. Mater. 17, 1853 (2015)
16.
Zurück zum Zitat O. Bouaziz, H.S. Kim, Y. Estrin, Adv. Eng. Mater. 15, 336 (2013) O. Bouaziz, H.S. Kim, Y. Estrin, Adv. Eng. Mater. 15, 336 (2013)
17.
Zurück zum Zitat S.O. Rogachev, S.A. Nikulin, A.B. Rozhnov, V.M. Khatkevich, T.A. Nechaykina, M.V. Gorshenkov, R.V. Sundeev, Metall. Mater. Trans. A 48, 6091 (2017) S.O. Rogachev, S.A. Nikulin, A.B. Rozhnov, V.M. Khatkevich, T.A. Nechaykina, M.V. Gorshenkov, R.V. Sundeev, Metall. Mater. Trans. A 48, 6091 (2017)
18.
Zurück zum Zitat R. Lapovok, V.V. Popov Jr., Y. Qi, A. Kosinova, A. Berner, C. Xu, E. Rabkin, R. Kulagine, J. Ivanisenko, B. Baretzky, O.V. Prokof’eva, A.N. Sapronov, D.V. Prilepo, Y. Beygelzimer, Mater. Design 187, 108398 (2020) R. Lapovok, V.V. Popov Jr., Y. Qi, A. Kosinova, A. Berner, C. Xu, E. Rabkin, R. Kulagine, J. Ivanisenko, B. Baretzky, O.V. Prokof’eva, A.N. Sapronov, D.V. Prilepo, Y. Beygelzimer, Mater. Design 187, 108398 (2020)
19.
Zurück zum Zitat Z. Gronostajski, Z. Pater, L. Madej, A. Gontarz, L. Lisiecki, A. Lukaszek-Solek, J. Luksza, S. Mróz, Z. Muskalski, W. Muzykiewicz, M. Pietrzyk, R.E. Sliwa, J. Tomczak, S. Wiewiórowska, G. Winiarski, J. Zasadzinski, S. Ziólkiewicz, Arch. Civ. Mech. Eng. 19, 898 (2019) Z. Gronostajski, Z. Pater, L. Madej, A. Gontarz, L. Lisiecki, A. Lukaszek-Solek, J. Luksza, S. Mróz, Z. Muskalski, W. Muzykiewicz, M. Pietrzyk, R.E. Sliwa, J. Tomczak, S. Wiewiórowska, G. Winiarski, J. Zasadzinski, S. Ziólkiewicz, Arch. Civ. Mech. Eng. 19, 898 (2019)
20.
Zurück zum Zitat V.A. Andreev, V.S. Yusupov, M.M. Perkas, V.V. Prosvirnin, A.E. Shelest, S.D. Prokoshkin, IYu. Khmelevskaya, A.V. Korotitskii, S.A. Bondareva, R.D. Karelin, Russ. Metall. 2017, 890 (2017) V.A. Andreev, V.S. Yusupov, M.M. Perkas, V.V. Prosvirnin, A.E. Shelest, S.D. Prokoshkin, IYu. Khmelevskaya, A.V. Korotitskii, S.A. Bondareva, R.D. Karelin, Russ. Metall. 2017, 890 (2017)
21.
Zurück zum Zitat S.A. Nikulin, T.A. Nechaikina, A.B. Rozhnov, S.O. Rogachev, VYu. Turilina, Met. Sci. Heat Treat. 60, 229 (2018) S.A. Nikulin, T.A. Nechaikina, A.B. Rozhnov, S.O. Rogachev, VYu. Turilina, Met. Sci. Heat Treat. 60, 229 (2018)
22.
Zurück zum Zitat S. Prokoshkin, I. Khmelevskaya, V. Andreev, R. Karelin, V. Komarov, A. Kazakbiev, Mater. Sci. Forum 918, 71 (2018) S. Prokoshkin, I. Khmelevskaya, V. Andreev, R. Karelin, V. Komarov, A. Kazakbiev, Mater. Sci. Forum 918, 71 (2018)
23.
Zurück zum Zitat R. Kocich, L. Kunčická, C.F. Davis, T.C. Lowe, I. Szurman, A. Macháčková, Mater. Design 90, 379 (2016) R. Kocich, L. Kunčická, C.F. Davis, T.C. Lowe, I. Szurman, A. Macháčková, Mater. Design 90, 379 (2016)
24.
Zurück zum Zitat L. Kunčická, R. Kocich, K. Dvořák, A. Macháčková, Mater. Sci. Eng. A 742, 743 (2019) L. Kunčická, R. Kocich, K. Dvořák, A. Macháčková, Mater. Sci. Eng. A 742, 743 (2019)
25.
Zurück zum Zitat E.V. Avtokratova, S.V. Krymskiy, M.V. Markushev, O.S. Sitdikov, Lett. Mater. 1, 92 (2011) E.V. Avtokratova, S.V. Krymskiy, M.V. Markushev, O.S. Sitdikov, Lett. Mater. 1, 92 (2011)
26.
Zurück zum Zitat G. Angella, P. Bassani, A. Tuissi, D. Ripamonti, M. Vedani, Mater. Sci. Forum 503-504, 493 (2006) G. Angella, P. Bassani, A. Tuissi, D. Ripamonti, M. Vedani, Mater. Sci. Forum 503-504, 493 (2006)
27.
Zurück zum Zitat M.H. Shaeri, M. Shaeri, M. Ebrahimi, M.T. Salehi, S.H. Seyyedein, Prog. Nat. Sci. Mater. Int. 26, 182 (2016) M.H. Shaeri, M. Shaeri, M. Ebrahimi, M.T. Salehi, S.H. Seyyedein, Prog. Nat. Sci. Mater. Int. 26, 182 (2016)
28.
Zurück zum Zitat S.O. Rogachev, V.A. Andreev, V.S. Yusupov, V.M. Hatkevich, E.V. Nikolaev, M.M. Perkas, S.A. Bondareva, Met. Sci. Heat Treat. 62, 748 (2021) S.O. Rogachev, V.A. Andreev, V.S. Yusupov, V.M. Hatkevich, E.V. Nikolaev, M.M. Perkas, S.A. Bondareva, Met. Sci. Heat Treat. 62, 748 (2021)
29.
Zurück zum Zitat A.M. Glezer, R.V. Sundeev, Mater. Lett. 139, 455 (2015) A.M. Glezer, R.V. Sundeev, Mater. Lett. 139, 455 (2015)
30.
Zurück zum Zitat A.M. Glezer, L.S. Metlov, Phys. Solid State 52, 1162 (2010) A.M. Glezer, L.S. Metlov, Phys. Solid State 52, 1162 (2010)
31.
Zurück zum Zitat E.D. Khafizova, I.P. Iskandarova, P.K. Islamgaliev, D.L. Pankratov, Lett. Mater. 5, 399 (2015) E.D. Khafizova, I.P. Iskandarova, P.K. Islamgaliev, D.L. Pankratov, Lett. Mater. 5, 399 (2015)
32.
Zurück zum Zitat H.J. Roven, M. Liu, J.C. Werenskiold, Mater. Sci. Eng. A 483–484, 54 (2008) H.J. Roven, M. Liu, J.C. Werenskiold, Mater. Sci. Eng. A 483–484, 54 (2008)
33.
Zurück zum Zitat B. Straumal, A. Korneva, P. Zieęba, Arch. Civ. Mech. Eng. 14, 242 (2014) B. Straumal, A. Korneva, P. Zieęba, Arch. Civ. Mech. Eng. 14, 242 (2014)
34.
Zurück zum Zitat B.B. Straumal, V. Pontikis, A.R. Kilmametov, A.A. Mazilkin, S.V. Dobatkin, B. Baretzky, Acta Mater. 122, 60 (2017) B.B. Straumal, V. Pontikis, A.R. Kilmametov, A.A. Mazilkin, S.V. Dobatkin, B. Baretzky, Acta Mater. 122, 60 (2017)
35.
Zurück zum Zitat E. Khafizova, R. Islamgaliev, G. Klevtsov, E. Merson, Mater. Phys. Mech. 24, 232 (2015) E. Khafizova, R. Islamgaliev, G. Klevtsov, E. Merson, Mater. Phys. Mech. 24, 232 (2015)
36.
Zurück zum Zitat A.A. Mazilkin, B.B. Straumal, A.R. Kilmametov, T. Boll, B. Baretzky, O.A. Kogtenkova, A. Korneva, P. Zięba, Scripta Mater. 173, 46 (2019) A.A. Mazilkin, B.B. Straumal, A.R. Kilmametov, T. Boll, B. Baretzky, O.A. Kogtenkova, A. Korneva, P. Zięba, Scripta Mater. 173, 46 (2019)
Metadaten
Titel
Effect of Rotary Forging on Microstructure Evolution and Mechanical Properties of Aluminum Alloy/Copper Bimetallic Material
verfasst von
S. O. Rogachev
V. A. Andreev
V. S. Yusupov
S. A. Bondareva
V. M. Khatkevich
E. V. Nikolaev
Publikationsdatum
08.05.2021
Verlag
The Korean Institute of Metals and Materials
Erschienen in
Metals and Materials International / Ausgabe 4/2022
Print ISSN: 1598-9623
Elektronische ISSN: 2005-4149
DOI
https://doi.org/10.1007/s12540-020-00964-7

Weitere Artikel der Ausgabe 4/2022

Metals and Materials International 4/2022 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.