Abstract
In this work, a cutting tool for sand-mold milling was fabricated by powder injection molding (PIM) technology using 90WC-10Co alloy powder for machining sand molds in patternless sand-casting technology. The work included design of cutting tool tip, injection mold and binder system. Also, for the PIM process, mixing, injection molding, debinding and sintering process were investigated experimentally. Finally, the properties for final products were tested, such as micro structures, element composition, wear resistance and so on. The cutting tool fabricated by PIM had a final density of 14.21 g/cm3 (95% of theoretical density) and a dimension accuracy over 98%. Also, in sand-mold machining test, it showed an abrasion loss of 0.16 mm after working for 3 hrs. The results showed that a whole cutting tool was fabricated using PIM technology successfully, and it showed out good mechanical performances.
Similar content being viewed by others
References
Kim, H. C., Jeong, I. K., Shon, I. J., Ko, I. Y., and Doh, J. M., “Fabrication of WC-8 wt.%Co Hard Materials by Two Rapid Sintering Processes,” International Journal of Refractory Metals and Hard Materials, vol. 25, no. 4, pp. 336–340, 2007.
Dong, X., Li, X., Shan, Z., and Liu, F., “Rapid Manufacturing of Sand Molds by Direct Milling,” Tsinghua Science and Technology, Vol. 14, No. S1, pp. 212–215, 2009.
Acchar, W., Gomez, U. U., Kaysser, W. A., and Goring, J., “Strength Degradation of a Tungsten Carbide-Cobalt Composite at Elevated Temperature,” Materials Characterization, vol. 43, no. 1, pp. 27–32, 1999.
Jia, K., Fischer, T. E., and Gallois, G., “Microstructure, Hardness, and Toughness of Nanostructured and Conventional WC-Co Composites,” Nanostructured Materials., vol. 10, no. 5, pp. 875–891, 1998.
Hirata, A., Zheng, H., and Yoshikawa, M., Adhesion Properties of CVD Diamond Film on Binderless Sintered Tungsten Carbide Prepared by the Spark Sintering Method, Diamond and Related Materials, vol. 7, no. 11, pp. 1669–1674, 1998.
Srivatsan, T. S., Woods, R., Petraroli, M., and Sudarsahn, T. S., “An Investigation of the Influence of Powder Particle Size on Microstructure and Hardness of Bulk Samples of Tungsten Carbide,” Powder Technology, vol. 122, no. 1, pp. 54–60, 2002.
Jia, C., Tang, H., Mei, X., Yin, F., and Qu, X., “Spark Plasma Sintering on Nanometer Scale WC-Co Powder,” Materials Letters, vol. 59, no. 19, pp. 2566–2569, 2005.
Park, S. J., Martin, J. M., Guo, J. F., and Johnson, J. L., “Densification Behavior of Tungsten Heavy Alloy based on Master Sintering Curve Concept,” Metallurgical and Materials Transactions A, vol. 37, no. 9, pp. 2837–2848, 2006.
Egashira, K., Hosono, S., Takemoto, S., and Masao, Y., “Fabrication and Cutting Performance of Cemented Tungsten Carbide Microcutting Tools,” Precision Engineering, vol. 35, no. 4, pp. 547–553, 2011.
Onishi, O., Onikura, H., Min, S-K., Aziz, F. M., Wahdi, A., and Koga, T., “Fabrication of Micro Flat Drills Composed of 90 nm WC Grain with a Diameter Less than 10 Micrometers and Their Drilling Performance,” Proc. of the 5th Euspen International Conference, pp. 585–588, 2005.
Fayyaz, A., Muhamad, N., Sulong, A. B., Rajabi, J., and Wong, Y. N., “Fabrication of Cemented Tungsten Carbide Components by Micro-Powder Injection Moulding,” Journal of Materials Processing Technology, vol. 214, no. 7, pp. 1436–1444, 2014.
Zhang, H., “Production Practice of Ester Hardening Water Glass Sand,” Machinist Metal Forming, vol. 9, pp. 74–76, 2004. (in Chinese)
Rota, A., Duong, T. V., and Hartwig, T., “Wear Resistant Tools for Reproduction Technologies Produced by Micro Powder Metallurgy,” Microsystem Technologies, vol. 7, no. 5–6, pp. 225–228, 2002.
Merz, L., Rath, S., and Zeep, B., “Powder Injection Molding of Cemented Carbides for The Production of Micro Parts and Micro Structured Parts,” PIM International, vol. 1, no. 3, pp. 56–58, 2007.
Liu, S., Huang, Z. L., Liu, G., and Yang, G. B., “Preparing Nano-Crystalline Rare Earth Doped WC/Co Powder by High Energy Ball Milling,” International Journal of Refractory Metals and Hard Materials, vol. 24, no. 6, pp. 461–464, 2006.
Eskandarany, M. S., Mahday, A. A., Ahmed, H. A., and Amer, A. H., “Synthesis and Characterizations of Ball-Milled Nanocrystalline WC and Nanocomposite WC-Co Powders and Subsequent Consolidations,” Journal of Alloys and Compounds, vol. 312, no. 1, pp. 315–325, 2000.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lin, D., Xu, J., Shan, Z. et al. Fabrication of WC-Co cutting tool by powder injection molding. Int. J. Precis. Eng. Manuf. 16, 1435–1439 (2015). https://doi.org/10.1007/s12541-015-0189-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12541-015-0189-8