Oxidation behavior of Ni- and Fe- based superalloys has been studied in air at 900°C under cyclic conditions. The mass change measurement with time was used to establish the oxidation kinetics. The oxide scales formed on the surface of the superalloys were characterised by various techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDAX) analyses. The oxide scales formed on the superalloys contained NiO, Cr2O3 and Fe2O3. The scales were adherent and only microspalling was observed. Superfer 800 has provided best resistance to oxidation among the alloys studied.
Similar content being viewed by others
References
Pettit F S and Meier G H, Oxidation and Hot corrosion of Superalloys, Superalloys 85, Eds. Gell M, Kartovich C S, Bricknel R H, Kent W B and Radovich J F, Met. Soc. of AIME, Warrendale, Pensylvania, (1985) 651.
Pint B A, DiStefano J R and Wright I G, Mater. Sci. Eng. A 415 (2006) 255.
Erickson G L, JOM, TMS, Warrendale, PA, 47(4) (1995) 36.
Duhl D N, Directionally solidified superalloys. In: Sims C T, Stoloff N S and Hagel W C, Editors, Superalloys II, Wiley and Sons, Inc., New York (1987) 189.
Durand-Charee M. In: The microstructure of superalloys, Gordon and Breach Science Publishers, Canada (1997) 60.
Fuchs G. E, Mater. Sci. Eng. A 300 (2001) 52.
Chen K, Zhao L R and John S. Tse. Mater. Sci. Eng. A 365 (2004) 80.
Zhou H, Ro Y, Harada H, Aoki Y and Arai M, Mater. Sci. Eng. A, 381 (2004) 20.
Fuchs G E and Boutwell B A, Mater. Sci. Eng. A 333 (2002) 72.
Czech N, Schmitz F and Stamm W, Surf. Coat. Technol. 68/69, (1994) 17.
Liu C T, Sun X F, Guan H R, Hu Z Q, Surf. Coat. Technol. 194, (2005) 111.
Greene G A and Finfrock C C, Oxid. Met. 55(5/6) (2001) 505.
Holloway P H, J. Vac. Sci. Technol. 18 (1981) 653.
Stott F H, Trib. Int. 31(1–3) (1998) 61.
Khalid F A, Hussain N and Shahid K A, Mater. Sc. & Eng. A, 265 (1999) 87.
Sadique S E, Mollah A H, Islam M S, Ali M M, Megat M H, and Basri S, Oxid. Met. 54(5–6) (2000) 385.
Kofstad P, Rahmel A, Rapp R A, and Douglass D L, Oxid. Met., 32 (1989) 125.
Hussain N, Shahid K A, Khan I H, and Rahman S, Oxid. Met., 41(3/4) (1994) 251.
Bornstein N S, Decrescente M A and Roth H A, Proc. in conf. on Gas turbine Mater. In the Marine environment, MMIC-75-27, Columbus, Ohio, USA (1975) 115.
Sidhu B.S, Ph.D Thesis, Met. & Mat. Engg. Deptt, IITR, Roorkee, India, (2003).
Harpreet Singh, Puri D and Prakash S, Anti-Corrosion Methods and Materials, 52(2) (2005) 84.
Choi H, Yoon B, Kim H and Lee C, Surf. Coat. Technol. 150(2–3) (2002) 297.
UI-Hamid A, Mater. Chem. Phys. 80 (2003) 135.
Sundararajan S, Kuroda S, Nishida K, Itagaki T and Abe F, ISIJ Int. 44 (2004) 139.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mahesh, R.A., Jayaganthan, R. & Prakash, S. Oxidation behaviour of selected Ni- and Fe- based superalloys in air at 900°C under cyclic conditions. Trans Indian Inst Met 61, 45–49 (2008). https://doi.org/10.1007/s12666-008-0064-8
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-008-0064-8