Abstract
TiB2 reinforced in-situ titanium aluminide matrix composite was made through reaction synthesis process using high purity elemental powders of Ti, Al, Cr, Nb and B. XRD of the synthesized block showed presence of mainly Al3Ti and TiB2 phases. To obtain γ Ti aluminide based matrix, the material was homogenized in two phase region (α2+γ). Presence of γ phase matrix alongwith α2 was confirmed through XRD, SEM and TEM. Uniform distribution of TiB2 phase was confirmed through elemental mapping and by analyzing specimens of different locations. Differential scanning calorimetry of powder mixture showed presence of endothermic peak for Al melting and exothermic peak of Ti aluminide and TiB2 formation.
Similar content being viewed by others
References
Uenishi K, Matsubara T, Kambara M and Kobayashi K F, Scripta Mater., 44 (2001) 2093.
Mabuchi H, Tsuda H and Nakayama Y, Scripta Metall. Mater. 32 (1995) 253.
Ramaseshan R, Kakitsuji A, Seshadri S K, Nair N G, Mabuchi H, Tsuda H, Matsui T and Morii K, Intermetallics, 7 (1999) 571.
Yang S H, Kim W Y, Kim M S, Intermetallics, 11 (2003) 849.
Alman D E, Intermetallics, 13 (2005) 572.
Sohn H Y, Wang X, Mater. and Manuf. Process, 9(1) (1994) 75.
Rawers J C and Wrzesinski R R, Journal of Mater Sci., 27 (1992) 2877.
Pant Bhanu, Agarwala V, Agarwala R C and Sinha P P, Trans. IIM, 60 (2007) 925.
Gupta R K, Pant Bhanu, Agarwala Vijaya, Agarwala R C, Sinha P P, Journal of Mater Sci. and Tech (in-press).
Yang W Y and Weather G C, J. Mater. Sci., 31 (1996) 3707.
Orru R, Cao G and Munir Z A, Chem. Eng. Sci., 54 (1999) 3349.
Yeh C L and Su S H, Journal of alloys & compounds, 407(1–2) (2006) 150.
Gupta R K, Pant B, Agarwala V, Agarwala R C, Sinha P P, Trans. IIM, 62(1) (2009) 21.
Panda K B, Ravichandran K S, Metall. & Mater. Trans. A, 34A (2003) 1371.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Gupta, R.K., Pant, B., Agarwala, V. et al. Development of TiB2 reinforced in-situ Ti aluminide matrix composite through reaction synthesis. Trans Indian Inst Met 63, 715–718 (2010). https://doi.org/10.1007/s12666-010-0110-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-010-0110-1