Abstract
In this project, the sheet of Ti–6Al–4V alloy (annealed) with a thickness of 1 mm was welded with butt joints by means of pulsed current micro-plasma arc welding without using a filler metal. The purpose of this study is to optimize parameters in the event of increasing tensile strength by using pulse current and its comparison with the pulse-free system. Optical microscope and scanning electron microscope were used to investigate the type of phases, microstructure of weld metal, base metal and heat-affected zone. Results illustrated that due to the low thickness of the sheet, the non-use of filler metal in the welding process and the lower heat input of this process, all contributed to a higher cooling rate of the molten pool.
Similar content being viewed by others
Notes
Pre-gas.
Post-gas.
References
Cheng D H, Trans China Weld Inst 30 (2009) 103.
Kumar A, Sapp M, Vincelli J, and Gupta M C, J Mater Process Technol 210 (2010) 64.
Lin Y C, and Lin Y C, J Coat Technol Res 8 (2011) 247.
Rokhlin S I, and Guu A C, Weld J 72 (1993) 381.
Yuan B G, Li C F, Yu H P, and Sun D L, Trans Nonferrous Metals Soc China 19 (2009) 423.
Zhao H, Han Z, and Chen X F, Trans China Weld Inst 26 (2005) 78.
Mohandas T, Banerjee D, and Kutumba Rao V V, Metall Mater Trans A 30 (1999) 789.
Wu K C, Weld J 60 (1981) 219.
Rao K P, Angamuthu K, and Bala Srinivasan P, J Mater Process Technol 199 (2008) 185.
Kishore B N, Ganesh S R S, Mythili R, and Saroja S, Mater Charact 58 (2007) 581.
Chen J, and Pan C, Trans Nonferrous Metals Soc China 21 (2011) 1506.
Beaslack W A, Selection and Weldability of Conventional Titanium Alloys, Vol. 6. ASM Handbook, Metals Park (1992), p 507.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Rahimi, A., Shamanian, M., Rahimi, A. et al. A Comparative Study on Direct and Pulsed Current Micro-plasma Arc Welding of Alloy Ti–6Al–4V. Trans Indian Inst Met 71, 3103–3110 (2018). https://doi.org/10.1007/s12666-018-1501-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-018-1501-y