Abstract
Alloy Ti–6Al–4V was subjected to ultrasonic shot peening (USP) for 1 min (min) and 5 min to examine the effect of surface nanostructure on corrosion resistance of this alloy in simulated body fluid (SBF). USPed samples were also subjected to stress relieving (SR) treatment at 400 °C for 1 h in the argon atmosphere (AR). The surface nanostructure and constituted phases were characterized by TEM, and the effect of USP was examined on electrochemical corrosion resistance in SBF solution. It has been observed that corrosion resistance is enhanced due to USP. The development of the resistance to corrosion is attributed to the quick formation of protective oxide scale due to extensive increase in number of grain boundaries and the associated compressive residual stress induced by USP. The relatively lower corrosion resistance and higher tendency of pitting following SR treatment of the USPed specimens are due to decreasing the associated residual stress.
Similar content being viewed by others
References
Kumar S, Chattopadhyay K, Singh S R, and Singh V, Int J Surf Sci Eng 11 (2017) 23.
Bhola R, Bhola M S, Mishra B, Olson D L, Trends Biomater Artif Organs 25 (2011) 34.
Elsener B, Rota A, and Bohni H, Mater Sci Forum 44 (1989) 29.
Xiea Y, Liua X, Huang A, Dinga C, and Chu P K, Biomaterials 26 (2005) 6129.
Lee C K, Tribol Int 55 (2012) 7.
Yue T M, Yu J K, and Mei Z, Mater Lett 52 (2002) 206.
Ahmed A A, Mhaede M, and Wollmann M, Appl Surf Sci 363 (2016) 50.
Jelliti S, Richard C, Retraint D, and Roland T, Surf Coat Technol 224 (2013) 82.
Singh V, Pandey V, and Chattopadhyay K, Trans Indian Inst Met 69 (2016) 295.
Ailor W H, J Electrochem Soc 120 (1973) 50.
Oliveira N T C, and Guastaldi A C, Acta Biomater 5 (2009) 399.
Wen M, Liu G, Gu J F, Guan W M, and Lu J, Appl Surf Sci 255 (2009) 6097.
Yu J K, Han E H, Lu L, Wei X J, and Leung M, J Mater Sci 40 (2005) 1019.
Kumar S, Chattopadhyay K, and Singh V, Mater Charact 121 (2016) 23.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kumar, S., Pandey, V., Chattopadhyay, K. et al. Surface Nanocrystallization Induced by Ultrasonic Shot Peening and Its Effect on Corrosion Resistance of Ti–6Al–4V Alloy. Trans Indian Inst Met 72, 789–792 (2019). https://doi.org/10.1007/s12666-018-1531-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-018-1531-5