Abstract
This study investigated the sorption of Pb(II) in aqueous solution onto hydroxyapatite (HA) surfaces. Batch experiments were carried out using synthetic HA. The effect of contact time, HA dosage, and initial pH on removal efficiency were also investigated. The adsorption equilibrium and kinetics of Pb(II) on this adsorbent were then examined at 25 °C. Kinetic data were analyzed by pseudo first, second, and intra-particle diffusion models. The sorption data were then correlated with the Langmuir, Freundlich, Halsey, and Harkins–Jura adsorption isotherm models. The optimum dose of HA for Pb(II) removal is found to be 0.12 g/l with the removal efficiency of 97.3 % at an equilibrium contact time of 1 h. It is found that the adsorption kinetics of the Pb(II) on HA follow the pseudo second-order reaction. All the isotherms fitted well for experimental data. Capacity of HA is found as 357.14 mg Pb(II)/g of HA. The Pb(II) immobilization mechanism was studied. The results indicated that HA can be used as an effective adsorbent for removal of Pb(II) from aqueous solution.
Similar content being viewed by others
Introduction
Heavy metals are generally recognized to be a threat toward humans and ecosystems because of their high-potential toxicity. They could not be biologically decomposed into harmless materials and, to matters worse, were accumulated in the organisms (Adewunmi et al. 1996). In particular, Pb(II) has been classified as a serious hazardous heavy metal with high priority in the context of environmental risk (Volesky 2001). This metal is extremely toxic and can damage the kidney, liver, brain, nervous, and reproductive systems; among other adverse effects to humans (Godwin 2001). Drinking water containing Pb(II) ions for a long term, even if in a very low concentration, cause a wide range of spectrum health problems, such as renal failure, coma, nausea, cancer, convulsions and subtle effects on metabolism and intelligence (Rashed 2001; Li et al. 2005). It can cause mental retardation and semi-permanent brain damage in young children (Mohammad and Najar 1997). Pb(II) has the ability to replace calcium in the bone to form sites for long-term release (King et al. 2007).
At present, Pb(II) pollution is considered a worldwide problem because this metal is commonly detected in several industrial wastewaters (Davydova 2005). Examples of these wastewaters are those produced by processes, such as mining, smelting, printing, metal plating, explosive manufacture, and dying. In this context, local legislations have established rigorous standards for Pb(II) concentrations in industrial effluents. Therefore, special attention has been given to develop proper methods for removal of Pb(II) from water (De la Rosa et al. 2008).
Among the various water-treatment techniques described, adsorption is generally preferred for the removal of heavy metal ions due to its high efficiency, easy handling, availability of different adsorbents, and cost effectiveness (Beauvais and Alexandratos 1998). The most widely studied adsorbent is activated carbon, while the application of other adsorbent materials for metal-ion removal is now receiving considerable attention (Corami et al. 2007).
The present study focuses on the removal Pb(II) from aqueous solution by hydroxyapatite (HA) [Ca10(PO4)6(OH)2]. HA is a major inorganic constituent of bone and teeth, which belongs to the family of apatite’s (Elayaraja et al. 2012). It is one such material with excellent biocompatibility, osteointegrity, and osseous inductivity (Gopi et al. 2012). HA is the most commonly used ceramics in dentistry and bone-repair applications since they show a very good performance due to its similarity with the inorganic component of the bone (Vila et al. 2012). In addition, HA has been used as an adsorbent for removing heavy metals (Ramesh et al. 2012; Corami et al. 2007; Lee et al. 2005), fluoride (Sairam Sundaram et al. 2008), nicotinic acid (Dancu et al. 2011) and phenol (Lin et al. 2009). The study includes an evaluation of the effects of various operational parameters, such as contact time, dose of HA, and pH on the Pb(II) adsorption process. The adsorption kinetic models and equilibrium isotherm models related with the process were also investigated.
Materials and methods
Adsorbent characterization
The laboratory prepared hydroxyapatite (Ramesh et al. 2012) was characterized by using the X-ray diffraction (XRD), transmission electron microscope (TEM) and Fourier Transform Infrared (FTIR) analyzer.
The point of zero charge (PZC) was determined using the solid addition method (Oladoja and Aliu 2009) viz: a series of 100 mL conical flasks, 45 mL of 0.1 M KNO3 solution was transferred. The pH0 values of the solution were roughly adjusted from 3.5 to 8.1 by adding either 0.1 N HNO3 or NaOH. The total volume of the solution in each flask was made exactly to 50 mL by adding the KNO3 solution. The pH0 of the solutions were then accurately noted. HA (1 g) was added to each flask and securely capped, immediately. The suspension was then manually agitated. The pH values of the supernatant liquid were noted. The difference between the initial and final pH (pHf) values (ΔpH = pH0 − pHf) was plotted against the pH0. The point of intersection of the resulting curve at which pH0 gave the PZC.
Sorption experiments
Metal salt of Pb(NO3)2 was used to prepare metal ion (Pb(II)) solution. The stock solution (1,000 mg/L) was prepared by dissolving appropriate amounts of metal salt in double distilled water. The working solution (10 mg/L) was prepared by diluting the stock solution to appropriate volume.
Kinetic study was conducted with the known dosage of HA (0.006 g) for the 100 mL of metal ion solution. The samples were shaken at an agitation rate of 250 rpm. The samples were taken out at different time intervals. The sorbent solution mixtures were then centrifuged for 5 min and the supernatant was analyzed for the Pb(II) concentration. After the removal of Pb(II), the HA samples were separated by filtering and dried at 120 °C in an oven.
The batch sorption studies were carried out by shaking a series of bottles containing different amounts of HA dosage between 0.002 and 0.2 g in 100 mL of metal ions solution prepared in the laboratory. The samples were stirred at room temperature at 250 rpm for 1 h (equilibrium time), and their content was then centrifuged for 5 min and the supernatant liquid was analyzed for Pb(II) concentration. Initial and equilibrium metal ion concentration in the aqueous solution was determined by using a Thermo Scientific S-series model flame atomic absorption spectrometer.
The effect of the pH of the initial solution on the adsorption process was analyzed by adjusting the pH the aqueous solution between 2 and 10 with 0.5 N HCl or 0.5 N NaOH. An Orion EA 940 expandable ion analyzer was used to adjust a desired pH value.
Results and discussion
Characterization of HA
XRD and TEM images of nano-sized HA have been given in our previous work (Ramesh et al. 2012). The estimated crystallite size was 28 nm for the HA sample. The HA particles are found to be of nano-sized with needle-like morphology, with width ranging from 15 to 20 nm and length around 50–60 nm, the size comparable to that of bone apatite (Ramesh et al. 2012). Figure 1 shows the infrared spectra of HA before and after Pb(II) adsorption in the 4,000–400 cm−1 region. The various bands of HA is given in Table 1. The pH of PZC of the HA is shown in Fig. 2. The PZC of HA was found to be 6.86. It was observed that at pH <6.86, the surface of the HA is predominated by positive charges while at pH >6.86, the surface is predominated by negative charges.
Effect of contact time
The time-dependent behavior of Pb(II) adsorption was measured by varying the contact time between adsorbate and adsorbent in the range of 5–120 min. The percentage adsorption of Pb(II) with different contact time is shown in Fig. 3. From Fig. 3, it can be observed that the rate of removal of Pb(II) ions was higher at the initial stage, due to the availability of more active sites on the surface of HA and became slower at the later stages of contact time, due to the decreased or lesser number of active sites (Kannan and Karrupasamy 1998). It is apparent from Fig. 3 that until 1 h, the percentage removal of Pb(II) from aqueous solution increases rapidly and reaches up to 89 %. A further increase in contact time has a negligible effect on the percentage removal. Therefore, a 1 h shaking time was considered as equilibrium time for maximum adsorption. The decrease in rate of removal of Pb(II) with time may also be due to aggregation of Pb(II) around the HA particles. This aggregation may hinder the migration of adsorbate, as the adsorption sites become filled up, and also resistance to diffusion of Pb(II) molecules in the adsorbents increases (Mittal et al. 2010). The equilibrium time for Pb(II) removal using various adsorbents reported by various researchers was compared with present study (Table 2). From Table 2, it was found that the contact time for Pb(II) removal using HA is comparable to other adsorbents.
Effect of mass of adsorbent on Pb(II) removal
The effect of HA dosage on Pb(II) removal was analyzed by varying the dosage of HA and the result is shown in Fig. 4. It was observed that the removal efficiency increases with the increase in HA dosage. This reveals that the instantaneous and equilibrium sorption capacities of Pb(II) are functions of the HA dosage. The percentage removal of Pb(II) from aqueous solution by HA increases rapidly up to 67.5 % for a dose of 0.01 g/L. This is mainly due to increase in sportive surface area and availability of more adsorption sites. After that the removal efficiency increases slowly up to a value of 97.3 %. A further increase in HA dose has a negligible effect on the percentage removal. The decrease in the amount sorbed per unit mass with increasing sorbent dosage is due to the split in the flux or the concentration gradient between solute concentration in solution and the solute in the surface of the adsorbent (Vadivelan and Kumar 2005).
Effect of pH
The pH is a significant factor for determining the form of the metallic species in aqueous media. It influences the adsorption process of metal ions, as it determines the magnitude and sign of the charge on ions (Gupta et al. 2011). The effect of solution pH on the sorption of Pb(II) ions from the aqueous solution using HA was investigated in the pH range of 2–10 with the initial Pb(II) concentration of 10 mg/L. The result is shown in Fig. 5. It was found that the adsorption capacity of HA increases with increase in pH in acidic medium. But in alkaline conditions, the removal efficiency remains constant. This is because at low pH (<6), positively charged Pb(II) species are dominant and adsorption on HA takes place in faster rate. But in case of high pH values (pH = 7–11), there are several lead species with different charges like Pb(OH)+ and Pb(OH)2 and thus the removal of lead is possibly accomplished by simultaneous precipitation of Pb(OH)2 and sorption of Pb(OH)+ (Gupta et al. 2011).
Adsorption kinetics
The kinetic studies of a sorption process are paramount because the data obtained from such studies are necessary to understand the variables that influence the sorption of solutes. The results can also be used to determine the equilibrium time and the rate of adsorption can be used to develop predictive models for column experiments (Oladoja et al. 2008a). For this purpose, Lagergren’s pseudo first-order kinetic model, pseudo second-order kinetic model, and intra-particle diffusion model were considered and fitted with the experimental data.
The pseudo first-order equation is generally expressed as (Lagergren 1898),
where qe and q t are the adsorption capacity at equilibrium and at timet, respectively (mg/g), k1 is the rate constant of pseudo first-order adsorption (1/min). The values of log (qe − q t ) were linearly correlated with t. The plot of log (qe − q t ) versus t should give a linear relationship from which k1 and qe can be determined from the slope and intercept of the plot, respectively.
The second-order Lagergren equation was given by (Ho and McKay 1999). It is expressed as:
where k2 is the rate constant of pseudo second-order adsorption (g/mg/min). The plot of (t/q t ) and t should give a linear relationship from which qe and k2 can be determined from the slope and intercept of the plot, respectively.
Though there is a high possibility for pore diffusion to be the rate limiting step in a batch process, the adsorption rate parameter, which controls the batch process for most of the contact time, is the intraparticle diffusion (Weber and Morris 1963; Allen et al. 1989). The most widely applied intraparticle diffusion equation for sorption system is given by Weber and Morris (1963) as follows:
where k i is the intraparticle rate constant (mg/g mm0.5).
Figure 6 shows the plot of the kinetic model for adsorption of Pb(II) on HA. Experimental and theoretically calculated adsorption capacities (qe) at equilibrium and coefficients related to kinetic plots are listed in Table 3. It can be seen from Table 3 that the linear correlation coefficients for first-order and second-order model are good and based on the comparison between experimental and theoretically calculatedqe values, it was found that the pseudo second-order model fitted better than pseudo first-order model for removal of Pb(II) by HA.
Intraparticle diffusion plot (Fig. 6) shows multi-linearity between t0.5 and q t for the removal of Pb(II) by HA. It was also found that the intra-particle diffusion of Pb(II) within HA occurred in two stages. The first straight portion is attributed to the macro-pore diffusion and the second linear portion to micro-pore diffusion (Allen et al. 1989).
Adsorption isotherms
Equilibrium isotherm is described by a sorption isotherm, characterized by certain constants whose values express the surface properties and affinity of the sorbent sorption equilibrium is established when the concentration of sorbate in the bulk solution is in dynamic balance with that at the sorbent interface (Oladoja et al. 2008b). The adsorption isotherm study is carried out on well-known isotherms, such as Langmuir, Freundlich, Halsey, and Harkins–Jura adsorption isotherm models. The linear form of Langmuir isotherm is expressed as (Langmuir 1915):
where b is the constant that increases with increasing molecular size, qmax is the amount adsorbed to form a complete monolayer on the surface (mg/g), X is weight of substance adsorbed (mg), M is weight of adsorbent (g), and Ce is the concentration remaining in solution (mg/L).
The essential features of the Langmuir isotherm may be expressed in terms of equilibrium parameter RL, which is a dimensionless constant referred to as separation factor or equilibrium parameter (Weber and Chakkravorti 1974):
The value of RL indicates the type of the isotherm to be either unfavorable (RL > 1), linear (RL = 1), favorable (0 < RL < 1) or irreversible (RL = 0).
The Freundlich isotherm is expressed as (Freundlich 1906).
where K and n are the constants depending on temperature.
The Harkin–Jura (Harkins and Jura 1944) adsorption isotherm can be expressed as:
where B and A are the isotherm constants. The isotherm equation accounts for multilayer adsorption and can be explained by the existence of a heterogeneous pore distribution (Venckatesh et al. 2010). The plot between log Ce and 1/q 2e gives a straight line with slope of 1/A and intercept of B/A.
The Halsey (1948) adsorption isotherm can be given as:
where nH and k are Halsey isotherm constants. This equation is suitable for multilayer adsorption and the fitting of the experimental data to this equation attest to the heteroporous nature of the adsorbent. The Halsey isotherm parameters are obtained from the plot of ln (qe) versus ln (Ce).
An isotherm plot for sorption of Pb(II) by HA is shown in Fig. 7. The intercept and slope of each straight line were used to obtain the isotherm constants and given in Table 4. The value of ‘n’ indicates that the Freundlich isotherm is favorable for removal of Pb(II) by HA. The value of RL also indicates that Langmuir isotherm is favorable. From Fig. 7, it can be concluded that Langmuir isotherm is the best fit among other isotherms. The adsorption capacity of HA was 357.14 mg Pb(II)/g of HA. The adsorption capacity of HA for Pb(II) is compared with other adsorbents (Table 5). The value of Pb(II) uptake by HA found in this work is significantly higher than that of other adsorbents. From the Table 5, it can be seen that HA is an efficient biosorbent for the uptake of Pb(II) from aqueous solution.
Mechanism
Three types of reactions may control Pb(II) immobilization by HA: surface adsorption, cation substitution or precipitation. The first mechanism is the adsorption of Pb(II) ions on the HA surfaces and following ion exchange reaction between Pb(II) ions adsorbed and Ca2+ ions of HA (Suzuki et al. 1984). This ion exchange reaction mechanism is expressed as:
Ma et al. (1994) showed that HA dissolution and hydroxypyromorphite (HP) precipitation were the main mechanisms for Pb(II) immobilization by HA in the absence of other metals. These chemical reactions can be described as follows:
Information about the sorption mechanisms have been inferred by the values of molar ratios (Qs) of cations bound by HA to Ca desorbed from HA (Aklil et al. 2004). The Ca desorbed from HA with Pb(II) adsorption is shown in Fig. 8. The values of metal disappearance, solution Ca and molar ratio were found as 8.79 (mg/L), 10 (mg/L) and 0.879, respectively. Since the value of molar ratio is less than 1, dissolution and precipitation are the main mechanisms for Pb(II) adsorption by HA (Corami et al. 2007).
Conclusions
The capability of HA for Pb(II) adsorption was examined using equilibrium and kinetic analysis. The result shows that HA is a powerful adsorbent for removing Pb(II) from aqueous solution. The optimum dose of HA for Pb(II) removal is found to be 0.12 g/L with the removal efficiency of 97.3 %. It is found that the adsorption kinetics of the Pb(II) on HA follow the pseudo second-order reaction. Langmuir isotherm had best fit than Freundlich, Halsey, and Harkins–Jura isotherms for experimental data. The adsorption capacity of HA was found to be 357.14 mg/g. HA dissolution and hydroxypyromorphite precipitation were the main mechanisms for Pb(II) immobilization by HA.
References
Abdel-Ghani NT, Hefny MF, El-Chaghaby GA (2007) Removal of lead from aqueous solution using low cost abundantly available adsorbents. Int J Environ Sci Tech 4(1):67–73
Adewunmi CO, Becker W, Kuehnast O, Oluwole F, D¨orfler G (1996) Accumulation of copper, Pb(II) and cadmium in freshwater snails in southwestern Nigeria. Sci Total Environ 193:69–73
Aklil M, Mouflih M, Sebti S (2004) Removal of heavy metal ions from water by using calcined phosphate as a new adsorbent. J Hazard Mater 112:183–190
Allen SJ, McKay G, Khader KYH (1989) Intraparticle diffusion of a basic dye during adsorption onto Sphagnum peat. Environ Pollut 56:39–50
Beauvais RA, Alexandratos SF (1998) Polymer-supported reagents for the selective complexation of metal ions: an overview. React Funct Polym 36:113–121
Corami A, Mignardi S, Ferrini V (2007) Copper and zinc decontamination from single- and binary-metal solutions using hydroxyapatite. J Hazard Mater 146:164–170
Dahiya S, Tripathi RM, Hegde AG (2007) Biosorption of lead and copper from aqueous solutions by pre-treated crab and arca shell biomass. Bioresour Tech 99:179–187
Dancu AC, Barabas R, Bogya ES (2011) Adsorption of nicotinic acid on the surface of nanosized hydroxyapatite and structurally modified hydroxyapatite. Cent Eur J Chem 9(4):660–669
Davydova S (2005) Heavy metals as toxicants in big cities. Microchem J 79:133–136
De la Rosa G, Reynel-Avila HE, Bonilla-Petriciolet A, Cano-Rodríguez I, Velasco-Santos C, Martínez-Hernández AL (2008) Recycling poultry feathers for Pb(II) removal from wastewater: kinetic and equilibrium studies. Int J Chem Biol Eng 1(4):185–193
Elayaraja K, Rajesh P, Ahymah Joshy MI, Sarath Chandra V, Suganthi RV, Kennedy J, Kulriya PK, Sulania I, Asokan K, Kanjilal D, Avasthi DK, Varma HK, Narayana Kalkura S (2012) Enhancement of wettability and antibiotic loading/release of hydroxyapatite thin film modified by 100 MeV Ag7+ ion irradiation. Mater Chem Phys 134:464–477
Freundlich H (1906) U¨ ber die adsorption in lo¨sungen [Adsorption in solution]. Z Phys Chem 57:384–470
Godwin HA (2001) The biological chemistry of Pb(II). Curr Opin Chem Biol 5:223–227
Gopi D, Indira J, Kavithab L, Sekar M, Kamachi Mudali U (2012) Synthesis of hydroxyapatite nanoparticles by a novel ultrasonic assisted with mixed hollow sphere template method. Spectrochim Acta A 93:131–134
Gupta VK, Agarwal S, Saleh TA (2011) Synthesis and characterization of alumina-coated carbon nanotubes and their application for lead removal. J Hazard Mater 185:17–23
Halsey G (1948) Physical adsorption on non-uniform surfaces. J Chem Phys 16:931–937
Harkins WD, Jura EJ (1944) The decrease of free surface energy as a basis for the development of equations for adsorption isotherms; and the existence of two condensed phases in films on solids. J Chem Phys 12:112–113
Ho YS, McKay G (1999) Pseudo-second-order model for sorption processes. Process Biochem 34:451–465
Huang YH, Hsueh CL, Huang CP, Su LC, Chen CY (2007) Adsorption thermodynamic and kinetic studies of Pb(II) removal from water onto a versatile Al2O3-supported iron oxide. Sep Purif Technol 55:23–29
Jang SH, Min BG, Jeong YG, Lyoo WS, Lee SC (2008) Removal of lead ions in aqueous solution by hydroxyapatite/polyurethane composite foams. J Hazard Mater 152:1285–1292
Jiang MQ, Jin XY, Lu XQ, Chen ZL (2010) Adsorption of Pb(II), Cd(II), Ni(II) and Cu(II) onto natural kaolinite clay. Desalination 252:33–39
Kannan N, Karrupasamy K (1998) Low cost adsorbents for the removal of phenyl acetic acid from aqueous solution. Indian J Environ Protect 18(9):683–690
Kannan N, Veemaraj T (2009) Removal of lead (II) ions by adsorption onto bamboo dust and commercial activated carbons—a comparative study. Electron J Environ Agric Food Chem 6(2):247–256
King P, Rakesh N, Beenalahari S, Prasanna Kumar Y, Prasad VSRK (2007) Removal of lead from aqueous solution using Syzygium cumini L.: equilibrium and kinetic studies. J Hazard Mater 142:340–347
Lagergren S (1898) About the theory of so-called adsorption of soluble substances. Kungl Sven Veten Akad Handl 24:1–39
Langmuir I (1915) Chemical reactions at low pressures. J Am Chem Soc 27:1139–1143
Lee CK, Kim HS, Kwon JH (2005) The removal of heavy metals using hydroxyapatite. Environ Eng Res 10(5):205–212
Li YH, Di Z, Ding J, Wu D, Luan Z, Zhu Y (2005) Adsorption thermodynamic, kinetic and desorption studies of Pb(II) on carbon nanotubes. Water Res 39:605–609
Lin K, Pan J, Chen Y, Cheng R, Xu X (2009) Study the adsorption of phenol from aqueous solution on hydroxyapatite nanopowders. J Hazard Mater 161:231–240
Ma QY, Traina SJ, Logan TJ, Ryan JA (1994) Effect of aqueous Al, Cd, Cu, Fe(II), Ni, and Zn on Pb(II) immobilization by hydroxyapatite. Environ Sci Technol 28:1219–1228
Manjubala I, Sivakumar M, Najma Nikkath S (2001) Synthesis and characterisation of hydroxy/fluoropatite solid solution. J Mater Sci 36:5481–5486
Martínez M, Miralles S, Hidalgo N, Fiol I, Villaescusa JP (2006) Removal of lead(II) and cadmium(II) from aqueous solutions using grape stalk waste. J Hazard Mater 133:203–211
Matheickal JT, Yu Q (1996) Proceedings of the 10th national convention of Royal Australian Chemical Institute. Adelaide, Australia
Mittal A, Mittal J, Malviya A, Gupta VK (2010) Removal and recovery of Chrysoidine Y from aqueous solutions by waste materials. J Colloid Interf Sci 344:497–507
Mohammad A, Najar M (1997) Physico-chemical adsorption treatments for minimization of heavy metal contents in water and wastewaters. J Sci Ind Res 51:523–532
Mouflih M, Aklil A, Sebti S (2005) Removal of lead from aqueous solutions by activated phosphate. J Hazard Mater 119:183–188
Muraleeddharan TR, Iyengar L, Venkobavhar C (1995) Screening of tropical wood-rotting mushrooms for lead biosorption. Appl Environ Microbiol 61:3507–3508
Oladoja NA, Aliu YD (2009) Snail shell as coagulant aid in the alum precipitation of malachite green from aqua system. J Hazard Mater 164:1496–1502
Oladoja NA, Aboluwoye CO, Oladimeji YB (2008a) Kinetics and isotherm studies on methylene blue adsorption onto ground palm kernel coat. Turkish J Eng Env Sci 32:303–312
Oladoja NA, Asia IO, Aboluwoye CO, Oladimeji YB, Shogbon AO (2008b) Studies on the sorption of basic dye by rubber (Hevea brasiliensis) seed shell. Turkish J Eng Env Sci 32:143–152
Ramesh ST, Rameshbabu N, Gandhimathi R, Nidheesh PV, Srikanth Kumar M (2012) Kinetics and equilibrium studies for the removal of heavy metals in both single and binary systems using hydroxyapatite. Appl Water Sci. doi:10.1007/s13201-012-0036-3
Rashed MN (2001) Pb(II) removal from contaminated water using mineral adsorbents. Environmentalist 21:187–195
Reddy DHK, Seshaiah K, Reddy AVR, Madhava Rao M, Wang MC (2010) Biosorption of Pb2+ from aqueous solutions by Moringa oleifera bark: equilibrium and kinetic studies. J Hazard Mater 174:831–838
Rehman I, Bonfield W (1997) Characterization of hydroxyapatite and carbonated apatite by photo acoustic FTIR Spectroscopy. J Mater Sci-Mater M 8:1–4
Sairam Sundaram C, Viswanathan N, Meenakshi S (2008) Defluoridation chemistry of synthetic hydroxyapatite at nano scale: equilibrium and kinetic studies. J Hazard Mater 155:206–215
Say R, Birlik E, Denizli A, Ersöz A (2006) Removal of heavy metal ions by dithiocarbamate-anchored polymer/organosmectite composites. Appl Clay Sci 31:298–305
Singh R, Chadetrik R, Kumar R, Bishnoi K, Bhatia D, Kumar A, Bishnoi NR, Singh N (2010) Biosorption optimization of lead(II), cadmium(II) and copper(II) using response surface methodology and applicability in isotherms and thermodynamics modeling. J Hazard Mater 174:623–634
Suzuki T, Ishigaki K, Miyake M (1984) Synthetic hydroxyapatites as inorganic cation exchangers exchange characteristics of Pb(II) ions. J Chem Soc Faraday Trans 80:3157–3165
Tofighy MA, Mohammadi T (2011) Adsorption of divalent heavy metal ions from water using carbon nanotube sheets. J Hazard Mater 185:140–147
Vadivelan V, Kumar KV (2005) Equilibrium, kinetics, mechanism, and process design for the sorption of methylene blue onto rice husk. J Colloid Interf Sci 286:90–100
Venckatesh R, Amudha T, Sivaraj R, Chandramohan M, Jambulingam M (2010) Kinetics and equilibrium studies of adsorption of Direct Red-28 onto Punica granatum carbon. Int J Eng Sci Technol 2(6):2040–2050
Vila M, Fernández-Lanas T, González B, Vallet-Regí M (2012) Macroporous sol–gel hydroxyapatite moulding via confinement into shaped acrylate–acrylamide copolymers. J Eur Ceram Soc 32:2121–2127
Volesky B (2001) Detoxification of metal-bearing effluents: biosorption for the next century. Hydrometallurgy 59:203–216
Weber TW, Chakkravorti RK (1974) Pore and solid diffusion models for fixed bed adsorbers. AIChE J 20:228–238
Weber WJ, Morris JC (1963) Kinetics of adsorption on carbon from solution. J Sanit Eng Div ASCE 89:31
Wehrheim B, Wettern M (1994) Biosorption of cadmium, copper and lead by isolated mother cell walls and whole cells of Chlorella fusca. Appl Microbiol Biotechnol 41:725–728
Yavuz Ö, Guzel R, Aydin F, Tegin I, Ziyadanogullari R (2007) Removal of cadmium and lead from aqueous solution by calcite. Polish J Environ Stud 16(3):467–471
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Ramesh, S.T., Rameshbabu, N., Gandhimathi, R. et al. Adsorptive removal of Pb(II) from aqueous solution using nano-sized hydroxyapatite. Appl Water Sci 3, 105–113 (2013). https://doi.org/10.1007/s13201-012-0064-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13201-012-0064-z