Effect of SiC particulate reinforcement on the dry sliding wear of aluminium-silicon alloys (A356)

https://doi.org/10.1016/0043-1648(92)90111-KGet rights and content

Abstract

The dry sliding wear behaviour of cast aluminium 7% silicon alloys (A356) reinforced with SiC particles was investigated by means of a block-on-ring (52100 bearing steel) type wear rig. Wear rates of the composites with 10–20 vol.% SiC were measured over a load range of 1–150 N at sliding velocities of 0.16 and 0.8 m s−1. Detailed electron metallography and X-ray diffraction analyses were undertaken to clarify the effect of SiC particles on the wear mechanisms. Observations indicated the following. (1) At low loads, corresponding to stresses lower than the particle fracture strength, SiC particles acted as load-bearing elements and their abrasive action on the steel counterface caused transfer of iron-rich layers onto the contact surfaces. In this regime, SiC reinforced composites exhibited wear rates about an order of magnitude lower than those of the unreinforced alloys in which wear occurred by subsurface crack nucleation, around the silicon particles, and growth. (2) Above a critical load determined by the size and volume fraction of SiC particles, carbide particles at the contact surfaces were fractured. A subsurface delamination process by the decohesion of SiC-matrix interfaces tended to control the wear, resulting in wear rates similar to those in the unreinforced matrix alloy. (3) An abrupt increase in the wear rates (by a factor of 102) occurred in the unreinforced aluminium-silicon alloy at 95 N. SiC reinforcement was proved to be effective in suppressing the transition to severe wear rate regime.

References (39)

  • K.C. Ludema

    A review of scuffing and running in of lubricated surfaces with asperities and oxides in perspective

    Wear

    (1984)
  • J.H. Dautzenberg et al.

    Quantitative determination of deformation by sliding wear

    Wear

    (1973)
  • S. Jahanmir et al.

    Mechanics of subsurface void nucleation in delamination wear

    Wear

    (1977)
  • S. Das et al.

    Microstructure and wear of cast (Al-Si-graphite) composites

    Wear

    (1989)
  • S.F. Corbin et al.

    Effect of temperature on the mechanical behaviour of a SiC particulate reinforced Al alloy

  • F.M. Hosking et al.

    Composites of aluminum alloys: fabrication and wear behaviour

    J. Mater. Sci.

    (1982)
  • S.V. Prasad et al.

    Tribological properties of Al alloy particle composites

    J. Met.

    (1987)
  • N. Saka et al.

    Friction and wear of particle reinforced metal-ceramic composites

  • A.G. Wang et al.

    Wear of alumina fibre-aluminum metal matrix composites by two body abrasion

    Mater. Sci. Technol

    (1989)
  • Cited by (314)

    • Pressureless sintering and tribological properties of in-situ TiC-Ni<inf>3</inf>(Al,Ti)/Ni(Al,Ti) composites

      2021, International Journal of Refractory Metals and Hard Materials
      Citation Excerpt :

      NTAC10 (Fig. 11a) show more damage and pullout signs in the wear track; while NTAC30 composite experienced less damage, as shown in Fig. 11b. Several reports have pointed out to the importance of interfacial bonding between particle and matrix and its relation to wear, designing stronger interfaces will promote higher insertion rate of reinforcing second-phase and less particle detachment during the sliding process [8,54,55]. X. Wu et al. [25] showed that the in-situ TiC insertion in the Ni matrix exhibited less particle debonding phenomenon compared to the composite fabricated through ex-situ methods.

    • Tribological Properties of Light Metal Matrix Composites

      2021, Encyclopedia of Materials: Composites
    View all citing articles on Scopus
    View full text