Ductile fracture by vacancy condensation in f.c.c. single crystals
Abstract
We explore the feasibility of vacancy condensation as the void-nucleating mechanism underlying ductile fracture by void growth and coalescence in single crystals at room temperature. Vacancies are presumed to be primarily generated by the dragging of intersection jogs. The equations governing the rate of growth of voids by vacancy condensation are derived. These equations are used to follow the evolution of vacancy concentrations and void sizes in the Wang and Anderson [Acta metall. 39, 779 (1991)] [1] ⩞9 test. We find that, when pipe diffusions are taken into account, the time required for the nucleation of a macroscopic void in the near-tip region is of the order of one minute, which is well within the time-scale of quasistatic fracture tests.
References (48)
- J.-S. Wang et al.
Acta metall.
(1991) - H.G.F. Wilsdorf
Mater. Sci. Engng
(1983) - N. Aravas et al.
J. Mech. Phys. Solids
(1985) - R.L. Lyles et al.
Acta metall.
(1975) - H.G.F. Wilsdorf
Acta metall.
(1982) - R.W. Bauer et al.
Scripta metall.
(1973) - P. Franciosi et al.
Acta metall.
(1980) - P. Franciosi et al.
Acta metall.
(1982) - P. Franciosi
Acta metall.
(1983) - P. Franciosi
Acta metall.
(1985)
Acta metall.
Mech. Mater.
Trans. Metall. Soc. A.I.M.E.
Trans. Am. Soc. Metals
Metall. Trans.
Trans. Am. Soc. Metals
Metall. Trans.
Metal Sci.
Int. J. Fract.
Engng Fract. Mech.
Cited by (140)
Multi-scale spallation model for single-crystal ductile metals incorporating microscopic mechanism of void nucleation
2024, Journal of the Mechanics and Physics of SolidsSpall strength characterizes the tensile performance of materials under high strain rates. However, theoretical prediction of the spall strength has long been a big challenge since it involves information on the damage evolution at multiple length scales. In this work, a multi-scale model is proposed for the spallation of single-crystal ductile metals, which includes both a microscopic model of damage nucleation and an effective correlation between the microscopic physical mechanisms and the macroscopic mechanical behaviors. An energy criterion to predict the threshold stress for damage nucleation is firstly proposed based on a near-realistic three-dimensional configuration of dislocation emission. The statistical characteristics of the damage nucleation threshold are analyzed, based on which a multi-scale spall model is proposed to couple the physical essence at the micro-scale to the macro-scale, revealing the influences of temperature, vacancy concentration, and strain rate on spall strength. An approximate form of the multi-scale model is proposed by dimensional analysis and reasonable approximation, which is consistent with the empirical model summarized from experimental results, and further deduced to a simple scaling law that predicts the transition in the strain rate-sensitivity of spall strength.
Void nucleation at dislocation boundaries aided by the synergy of multiple dislocation pile-ups
2023, International Journal of PlasticityVoid nucleation is of great significance in understanding ductile fracture. Recent experiments have shown that voids are nucleated via vacancy condensation and dislocation boundaries are the main nucleation sites. However, it is unclear what role is played exactly by dislocation boundaries in promoting void nucleation. Here we propose a new mechanism for dislocation boundary-induced void nucleation and develop a corresponding model based on the classical nucleation theory and vacancy diffusion theory. The model suggests that void nucleation is mainly influenced by hydrostatic stress, temperature, and relative vacancy concentration, whose contributions are systematically studied. It is also suggested that the vacancy formation energy and the interaction energy of hydrostatic stress and vacancy, which are absent in the previous models and introduced in ours, exhibit a clear tendency to lower the activation free energy barrier. Analysis of the nucleation kinetic suggests that the growth rate of void depends on the vacancy diffusion coefficient and vacancy concentration; the higher the values of these parameters, the faster the growth rate of the void. The kinetic feasibility of the newly proposed mechanism is examined using three-dimensional discrete dislocation dynamics simulations. The results predict that the size of incipient voids nucleated at the dislocation boundary is ∼35 nm, which is consistent with the experimental characterization value of ∼50 nm. Finally, when the relaxation of the dislocation boundary is considered, the synergistic effect is weakened.
A coupled diffusional-mechanical model accounting for hydrogen enhancements of strain-induced dislocations and vacancies
2023, Mechanics of MaterialsInformed by the current understanding of hydrogen-dislocations/vacancies interactions, a coupled diffusional-mechanical model accounting for hydrogen-enhanced strain-induced dislocations and vacancies is developed. This model is applied to capture hydrogen diffusion and trapping in the uniaxially tensioned column and type-I loaded crack specimens of nickel alloy, with special attentions paid to the influence of hydrogen-vacancies interaction on them, which is seldom discussed in previous studies. The results show that the hydrogen-enhanced hardening rate and the hydrogen-promoted vacancy enrichment for the nickel alloys observed in experiments can be addressed well by the present model. The strain-induced vacancies rather than dislocations dominate the hydrogen trapping behavior, due to their higher hydrogen binding energies for the nickel alloy. The hydrogen-saturated state of vacancies can heavily impact hydrogen diffusion/trapping, which could be characterized by the effective trap concentration. The supersaturated vacancies caused by hydrogen-enhanced strain-induced vacancies can promote void growth through vacancy condensation, thus accelerating plastic localization or interface rupture. For the type-I loaded blunt crack specimen, the hydrogen-enhanced dislocation multiplication contributes to intergranular cracking in the pressure valley, while hydrogen-enhanced vacancy generation facilitates void growth in the plastic zone, both of which can exacerbate plastic localization ahead of crack tip. A quantitative model for plasticity localization that accounts for the influences of hydrogen-induced IG cracking and void growth would be helpful in physically based modeling of hydrogen embrittlement.
Dynamic fracture processes in hydrogen embrittled iron
2023, Acta MaterialiaMechanistic understanding of hydrogen embrittlement is critical to the transport and storage of hydrogen as a sustainable fuel. Experimental observation of dynamic fracture processes in hydrogen environments has been challenging. Here, in-situ transmission X-ray microscopy is used to image polycrystalline iron foils that are concurrently strained and electrochemically charged with hydrogen. Using this technique, voids and microcracks down to ∼30 nm in size are identified at or near the crack tip and tracked as strain is increased. We observe both hydrogen-induced transgranular failure and hydrogen-induced intergranular failure with distinct fracture processes. We find that transgranular fracture occurs through the formation of sharp branched structures at the main crack tip that are reminiscent of slip band formation. This is followed by void growth and coalescence, and interaction with secondary cracks that lead to propagation of the main crack. Intergranular fracture is found to occur through void coalescence along grain boundaries, along with significant secondary cracking near the crack tip. The crack growth rate is greater for void-mediated intergranular failure than for slip-mediated transgranular failure. Additionally, the removal of hydrogen results in recovered ductility for a crack initially propagated under hydrogen charging.
Hydrogen-induced failure in a partially-recrystallized Al-Zn-Mg-Cu alloy with different aging conditions: Influence of deformation behavior dominated by microstructures
2023, Materials and DesignHydrogen-induced failure in a partially-recrystallized Al-Zn-Mg-Cu alloy with different aging conditions was studied by in-situ electrochemical hydrogen charging method, and the hydrogen-induced cracking mechanism was elucidated by investigating the microstructure-dominated deformation behavior. It was found that in naturally-aged and peak-aged samples, cracks initiate at sample surfaces, and deformation dominated by shearing facilitates hydrogen diffusion, resulting in a high hydrogen embrittlement susceptibility. However, in the over-aged sample, deformation dominated by bypassing cannot transport hydrogen efficiently, which exerts no effect on crack initiation at the sample center. In addition, the same cracking pattern exists on all samples in silicone oil and in-situ hydrogen charging environments. The grain boundary of recrystallized grains is prone to strain localization, leading to intergranular cracking. In unrecrystallized grains, transgranular cracks propagate along intersections of slip lines and subgrain boundaries. This study improves the understanding of hydrogen embrittlement in new generation Al-Zn-Mg-Cu alloy by linking the existing hydrogen embrittlement mechanism to the deformation behavior dominated by microstructures.
Void nucleation during ductile rupture of metals: A review
2023, Progress in Materials ScienceDuctile rupture in metals is a phenomenon that affects a wide range of applications from forming of automotive body panels to failure of pressure vessels. The incipient stage involves the formation of nanoscale internal voids, a critical transition state that is difficult to predict. Early experiments on ductile rupture led to several conflicting or competing models that describe the nucleation phase. The present review distinguishes the nucleation process based on the microstructural features that can trigger nucleation, e.g. vacancies, second-phase particles, grain boundaries, and dislocation cell boundaries; the conditions that drive nucleation, e.g. stress level, stress state, and temperature; and the materials properties that govern nucleation, e.g. modulus, yield strength, and work hardening. This review of observations and models leads to a critical assessment of the state of knowledge and provides guidance for future research directions, including a brief summary of the potential mechanistic changes to void nucleation processes in emerging material classes such as bulk metallic glasses, high entropy alloys, and nanostructured metals. This assessment also defines critical experiments and model developments that will enable improved prediction of ductile rupture processes and design of damage-tolerant materials. Such improvements in the understanding of the incipient phase of ductile rupture can lead to better materials, improved manufacturing and inspection protocols, more precise predictive models, more efficient engineering practices, and safer engineered structures.