Modeling the temperature dependent effect of twinning on the behavior of magnesium alloy AZ31B sheet
Introduction
Stress conditions during sheet metal forming operations are complex and can invoke responses that are not adequately characterized by common in-plane tension testing. In other words, a simple yield criterion such as Von Mises J2 flow rule, even when coupled with a strain hardening description, is inadequate for predicting the forming behavior of sheet metals that exhibit significant anisotropy and/or asymmetry. Rolled magnesium alloy sheets typically display strong in-plane tension–compression asymmetry, i.e., the material yields at a significantly lower stress in compression than in tension [1]. This behavior has been connected with mechanical twinning on the planes in the directions during compression but not during tension, due to the strong textures that are present in magnesium alloy sheets (e.g., [2]) and the polar nature of twinning [3]. (For hexagonal crystals with , the twinning mode produces tensile strains along the c-axis of the lattice, but not compressive [3].) After a low stress plateau in the flow curve, the material hardens rapidly resulting in a sigmoidal (S-shaped) compressive flow curve, and this has been connected with the radical texture evolution that attends extensive mechanical twinning (e.g., [4]). Both of these phenomena (asymmetry and sigmoidal hardening) are similar to those observed in the case of tension and compression along the axis of magnesium alloy extrusions [5]. Thus, in order to perform accurate secondary deformation process modeling for magnesium, it is important to develop constitutive models which can account for these effects of twinning under complex loading conditions. Different approaches for modeling the effect of twinning have been proposed, including polycrystal models [6], [7] such as the predominant twin reorientation [6] scheme employed in the present work as well as the recently developed analytical model which accounts for the aforementioned tension–compression asymmetry [8].
In addition to the need for improved modeling capability, there is also a need to develop efficient experimental approaches to characterize the constitutive response. It is noted that the dominant stress condition within the flange during deep drawing involves in-plane compression (actually in-plane pure shear) [9]. Additionally, through-thickness compression enforces the same strain path as biaxial tension, the dominant stress condition during sheet stretching operations. While some metals exhibit significantly higher strains to failure during compression than during tension, magnesium alloys can have the same or lower strains to failure in compression, as compared to those obtained in tension. Similarly, while most deep drawing failures occur in tension within the cup wall, magnesium alloys often fail in the flange. Thus, developing a better understanding of the compressive deformation of magnesium alloys sheet material could yield important insights regarding the poor overall sheet formability at low temperatures.
Historically, the poor cold forming properties of magnesium alloys have been attributed to the inadequate number of independent slip systems [10]. For instance, extensive studies involving slip trace analysis of single crystals, established that pure magnesium crystals possess only two independent slip systems at room temperature, both involving the slip of dislocations with type 〈a〉 Burgers vectors on the basal plane [10]. However, recent experimental and modeling investigations have called this understanding into question, because the significant activity of so-called hard deformation mechanisms, i.e., non-basal slip of 〈a〉 and 〈c + a〉 dislocations, has been established [11], [12], [13].
At mildly elevated temperatures, the ductility and formability of Mg alloys improve drastically [14]. It has been suggested that mechanical twinning is athermal, i.e., the stress to activate twinning is relatively insensitive to temperature or strain rate [15]. If so, thermally activated deformation mechanisms will be increasingly competitive with mechanical twinning at elevated temperatures. This raises fundamental questions about the role of twinning in determining the ductility and formability of magnesium alloys since, on the one hand, twinning may help fulfill the requirement for an increased number of independent deformation mechanisms [16], while on the other hand, there is the observation that conditions leading to improved ductility (i.e., higher temperatures or slower rates) also lead to less mechanical twinning. The present investigation focuses on measuring and modeling the temperature dependent role of mechanical twinning in determining the deformation response of the most common wrought magnesium alloy.
Section snippets
Material and sample preparation
Commercial magnesium alloy AZ31B (3 wt.% Al, 1 wt.% Zn, balance Mg) sheet material with 0.125″ (3.17 mm) thickness was received in the stress relieved (H24) temper. The material was then annealed for 1 h at 345 °C to minimize the presence of mechanical twins prior to deformation. The test samples were cut by electro-discharge machining (EDM) to avoid the mechanical damage associated with conventional machining. The compression test specimens were essentially cubes of ∼3.2 mm dimension. For
Flow properties
Fig. 2 shows the flow curves obtained from RD and TD compression tests at different temperatures. The samples were strained to ɛ ∼ 1.0 or failure, whichever occurred first. The TD samples are stronger at every temperature, as was observed for tensile deformation previously [13]. Strong sigmoidal hardening is observed at room temperature and mildly elevated temperature tests, while little hardening is observed at the higher temperatures (200 and 250 °C). Significantly, there is no softening in the
Discussion
The polycrystal modeling technique allows for an indirect assessment of the grain-level plastic deformation mechanisms in terms of their CRSS, τ0, and back-extrapolated flow stress, τ0 + τ1, values as a function of temperature (Fig. 9). In the aforementioned single crystal studies [10], [24], [25], [26], [27], [28], [29], [30], the CRSS ratios of non-basal to basal slip are reported to be of order 40:1–80:1 at room temperature, while those of the present polycrystal model are of order 2:1–5:1
Summary and conclusions
A working model for the temperature dependent role of deformation twinning in determining the mechanical behavior of magnesium alloy sheet has been developed. There are implications for both material development (alloy and microstructure design) and sheet forming process optimization.
- (i)
In-plane compression results in profuse twinning, which is shown to result in very low r-values (i.e., the Poisson strains are much larger in the thickness direction than transverse to it).
Acknowledgements
This research was supported by the National Science Foundation, Grant Number DMI-0322917. We would like to acknowledge many helpful discussions with our colleagues Ozgur Duygulu (formerly University of Virginia), Carlos Tomé (Los Alamos National Lab), Matthew Barnett (Deakin University), and Carlos Cáceres (University of Queensland).
References (34)
- et al.
Mater. Sci. Eng. A
(2005) - et al.
Acta Mater.
(2004) - et al.
Acta Mater.
(1991) - et al.
Int. J. Plasticity
(2004) - et al.
Acta Mater.
(2003) - et al.
Scripta Mater.
(2003) - et al.
Int. J. Plasticity
(2005) - et al.
J. Mater. Process. Technol.
(2001) - et al.
Acta Metall.
(1985) - et al.
Acta Metall. Mater.
(1993)
Scripta Mater.
Int. J. Plasticity
Acta Metall.
Acta Metall.
Acta Metall.
Magnesium and Magnesium Alloys
Trans. Metall. Soc. AIME
Cited by (476)
Significant improvement of bending properties for WE43 magnesium alloys under the coupling effects of weak basal texture and high deformation temperature
2024, Journal of Materials Research and TechnologyA visco-plastic self-consistent analysis of the compression anisotropy in extruded rare earth magnesium alloy
2024, Journal of Materials Research and TechnologyExperimental study on temperature-dependent ratchetting-fatigue interaction of extruded AZ31 magnesium alloy
2024, International Journal of FatigueMicrostructural effects in rate-dependent responses of smooth and notched magnesium bars
2024, Mechanics of MaterialsInvestigation of enhanced strength anisotropy in an extruded Mg–Al–Ca–Mn alloy at cryogenic temperature
2024, Materials Science and Engineering: AEffect of deformation mode on double-peak texture evolution in pre-twinning Mg-3Al-1Zn alloy during high-speed impacting loading
2023, Journal of Alloys and Compounds