Abstract
We propose an analytical model for investigation of the processes of fracture of a near-surface layer of bodies in the case of their unidirectional rolling under conditions of limit lubrication. The step-by-step calculation of trajectories of propagation of fatigue cracks using the criteria of local fracture in a complicated stressed state and with regard for the specific features of loading in a contact cycle is a key element of the model. We investigate trajectories of propagation of an edge crack depending on the angle of its initial inclination to the boundary of the body, the friction coefficient between the contacting bodies, and the pressure of lubricant on the crack lips. The theoretical results confirm the experimental data and the known hypothesis of Way, according to which a lubricant plays the decisive role in the appearance of a pit.
Similar content being viewed by others
References
B. I. Kostetskii, I. G. Nosovskii, L. I. Bershadskii, and A. K. Karaulov, Reliability and Durability of Machines [in Russian], Tekhnika, Kiev (1975).
Y. Murakami, C. Sakae, and S. Hamada, “Mechanism of rolling contact fatigue and measurement of ΔK II th for steels,” in: J. H. Beynon, M. W. Brown, T. C. Lindley, et al. (editors), Engineering Against Fatigue, A. A. Balkema, Rotterdam (1999), pp. 473–485.
S. Way, “Pitting due to rolling contact,” J. Appl. Mech. Trans. ASME, 2, A49–A58 (1935).
L. M. Keer and M. D. Bryant, “A pitting model for rolling contact fatigue,” J. Lubric. Technol. Trans. ASME, Ser. F 105, 198–205 (1983).
M. Kaneta and Y. Murakami, “Effects of oil hydraulic pressure on surface crack growth in rolling/sliding contact,” Tribol. Int., 20, No. 4, 210–217 (1987).
A. F. Bower, “The influence of crack face friction and trapped fluid on surface initiated rolling contact fatigue cracks,” J. Tribol., Trans. ASME, Ser. F 110, 704–711 (1988).
P. E. Bold, M. W. Brown, and R. J. Allen, “Shear mode crack growth and rolling contact fatigue,” Wear, 144, 307–317 (1991).
V. V. Panasyuk, O. P. Datsyshyn, and H. P. Marchenko, “On the growth of cracks in bodies of rolling under conditions of dry friction and humidification,” Fiz.Khim. Mekh. Mater., 37, No. 1, 7–16 (2001).
V. V. Panasyuk (editor), Fracture Mechanics and Strength of Materials. A Handbook [in Russian], Vols. 1-4, Naukova Dumka, Kiev (1988-1990).
V. V. Panasyuk, M. P. Savruk, and A. P. Datsyshyn, Distribution of Stresses in the Vicinity of Cracks in Plates and Shells [in Russian], Naukova Dumka, Kiev (1976).
M. P. Savruk, TwoDimensional Problems of Elasticity for Cracked Bodies [in Russian], Naukova Dumka, Kiev (1981).
V. V. Panasyuk, O. P. Datsyshyn, and H. P. Marchenko, “On crack propagation theory under rolling contact,” Eng. Frac. Mech., 52, No. 1, 179–191 (1995).
O. P. Datsyshyn, H. P. Marchenko, O. D. Zynyuk, and P. M. Hrytsyshyn, “On the residual durability of a surface layer of rollerbearing ShKh15 steel,” Fiz.Khim. Mekh. Mater., 31, No. 2, 42–50 (1995).
O. P. Datsyshyn, “Fracture and wear processes simulating under cyclic contact of solid bodies,” in: J. Petit (editor), ECF11. Mechanism and Mechanics of Damage and Failure, Vol. 2, EMAS, Warley (1996), pp. 1411–1416.
O. P. Datsyshyn and H. P. Marchenko, “On the propagation of edge cracks,” Fiz.Khim. Mekh. Mater., 31, No. 5, 42–48 (1995).
O. P. Datsyshyn, R. E. Pryshlyak, S. V. Prykhods'ka, et al., “Influence of the form of a model contact loading on the stress intensity factors for an edge crack,” Probl. Tribol., No. 3, 3–16 (1998).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Datsyshyn, O.P., Panasyuk, V.V., Pryshlyak, R.E. et al. Paths of Edge Cracks in Rolling Bodies under the Conditions of Boundary Lubrication. Materials Science 37, 363–373 (2001). https://doi.org/10.1023/A:1013243719026
Issue Date:
DOI: https://doi.org/10.1023/A:1013243719026