Phase transitions in ternary caesium lead bromide

Abstract

Phase transitions in ternary caesium lead bromide (CsPbBr₃) were studied by means of DSC, TMA and high temperature X-ray diffraction. The samples were prepared from the solution by water evaporation and from the melt. on the DSC curves as well as on the temperature dependence of the lattice constants of CsPbBr₃ only two effects were found belonging to the earlier published phase transitions at 88 and 130°C and no further effects. Linear thermal expansion coefficient α of individual CsPbBr₃ modifications were calculated from both TMA and high temperature X-ray diffraction. The structural parameters of the room temperature orthorhombic phase were refined and the results are presented. CsPbBr₃ prepared from the solution contained about 10% of CsPb₂Br₅ and so the DSC curve of pure CsPb₂Br₅ was also measured and an effect at a temperature of 68.5°C was found.