Abstract
We report here the field emission studies of a layered WS2-RGO composite at the base pressure of ~1 × 10−8 mbar. The turn on field required to draw a field emission current density of 1 μA/cm2 is found to be 3.5, 2.3 and 2 V/μm for WS2, RGO and the WS2-RGO composite respectively. The enhanced field emission behavior observed for the WS2-RGO nanocomposite is attributed to a high field enhancement factor of 2978, which is associated with the surface protrusions of the single-to-few layer thick sheets of the nanocomposite. The highest current density of ~800 μA/cm2 is drawn at an applied field of 4.1 V/μm from a few layers of the WS2-RGO nanocomposite. Furthermore, first-principles density functional calculations suggest that the enhanced field emission may also be due to an overalp of the electronic structures of WS2 and RGO, where graphene-like states are dumped in the region of the WS2 fundamental gap.
Similar content being viewed by others
Introduction
Following the graphene1,2,3,4 revolution, graphene analogues of other inorganic layered materials have received significant attention from the scientific community due to their interesting and useful properties as well as their direct applications in various nanoelectronic devices. Among all the layered compounds: MoS24,5,6,7,8,9,10,11,12, MoSe213,14,15,16, WS26,17,18, WSe219,20,21, GaS7,22,23, GaSe7,22,24, TaS225,26, RhTe227, PdTe228 are semiconductors; h-BN29,30 and HfS231 are insulators; NbS232, NbSe233, NbTe234 and TaSe226,35,36 are superconductors; while Bi2Te337,38 and Bi2Se339,40 act as topological insulators with good thermoelectric properties.
Field electron emission is the extraction of electrons from conducting/semiconducting materials via tunneling through the surface potential barrier by applying a very strong electric field of the order of 106–107 V/cm. Field emission has technological applications in various micro/nano-electronic devices. There is a great interest in the development of field emission based cathodes using various 1-dimesnional (1D) and 2-dimesional (2D) nanostructured materials. 1D and 2D materials such as carbon nanotubes (CNTs)41,42, ZnO43,44,45, LaB646,47,48, graphene49,50, reduced graphene oxide (RGO)51 and MoS252 have emerged as potential field emitter candidates. 2D materials are known for their atomically thin planar structure, which is already utilized in flat technology such as flat panel field emission displays. Amongst all 2D materials, graphene, GO and layered MoS2 sheets have been recently explored by researchers for their field emission properties. Graphene analogues of other 2D layered materials have emerged in material science and nanotechnology due to the enriched physics and novel enhanced properties they present. There are several advantages of using 2D nanomaterials in field emission based devices, including a thickness of only a few atomic layers, high aspect ratio (the ratio of lateral size to sheet thickness), excellent electrical properties, extraordinary mechanical strength and ease of synthesis. Furthermore, the presence of edges can enhance the tunneling probability for the electrons in layered nanomaterials similar to that seen in nanotubes41,42.
The inorganic chalcogenide material WS2 is a naturally occurring tungstite compound formed by 2D covalently bonded S-W-S layers separated by a van der Waals gap. Weak van der Waals interactions also hold the adjacent sulphur sheets together with a layer sequence S-W-S6,17,18,53. WS2 possesses hexagonal crystal structure with space group P63/mmc and each WS2 monolayer contains an individual layer of W atoms with 6-fold coordination symmetry, which are then hexagonally packed between two trigonal atomic layers of S atoms6,17,18,53. The WS2 material has attracted attention for diverse applications in future nanoelectronic devices because of its 2D layered structure and direct-band gap6,17,18. Whereas bulk WS2 has an indirect band gap of 1.35 eV, when it is thinned to a single layer it becomes direct band gap semiconductor with a gap of 2.05 eV17,18.
We have recently reported field emission properties of layered MoS2 sheets exhibiting a turn on field of 3.5 V/μm to draw a current density of 10 μA/cm2 52. This has generated interest in field emission studies of other transition metal dichalcogenides such as WS2. Furthermore, in an attempt to enhance the field emission properties of WS2, we have prepared a composite of WS2 on RGO by a low-temperature hydrothermal method. We report here for the first time field emission studies on a layered WS2 and WS2-RGO nanocomposite, where the RGO supported system exhibits superior field emission. We relate this superior performance to ehanced electric fields at the sheet edges and surface protrusions in the WS2-RGO composite. In addition, first-principles density functional theory (DFT) calculations show that the enhanced emission may also be due in part to the overlapping nature of the electronic structure of the composite system.
Results
Fig. 1 shows a field emission scanning electron microscope (FE-SEM) image of single-layer to a few-layered WS2 sheets (Fig. 1a) and WS2-RGO nanocomposite sheets deposited on a Si substrate (Fig. 1b). The FE-SEM images reveal that the thickness of stacked WS2 sheets is ~1–5 nm and their length is in the range of ~1–3 μm. These images also reveal that the Si substrate was completely covered with WS2 sheets and that the sheets possess a rough morphology along with vertical aligmnement (see Fig. S1, Supplementary Information). The FE-SEM images of composite WS2-RGO exhibit a large number of protruding edges on the surface as compared to WS2 and RGO sheets (see Supplementary Information, Fig. S1). Fig. 1c shows the typical X-Ray diffraction (XRD) pattern of WS2 sheets and the WS2-RGO nanocomposite. XRD analysis of the WS2 sheets and WS2-RGO nanocomposite shows high crystalline hexagonal structure [Powder diffraction file (PDF) no. 84-1398] without any other impurities. The XRD data of WS2 sheets shows the direction of sheet growth is along the (002) direction. The XRD pattern of the WS2-RGO composite shows a broad (002) peak and a more intense (100) peak as compared to the WS2 sheets. The broadness of the (002) peak indicates both smaller size and fewer layers for the WS2 sheets. Also, it confirms the growth of a large number of protrusion edges along the (100) direction on RGO. Raman spectroscopy reveals the characteristic peaks of WS2 in the 200–500 cm−1 range and the D (1348 cm−1) and G (1587 cm−1) bands of RGO in the WS2-RGO composite (Fig. 1d). In both the WS2 sheets and the WS2-RGO composite three bands are observed at 312, 345 and 415 cm−1 which corresponds to the E1g, E2g1 and A1g modes, respectively54,55.
Transmission Elecron micrscopy (TEM) analysis demonstrates the formation of single crystalline, few-layered WS2 sheets (Fig. 2 and Supplementary Information, Fig. S2). The high-resultion Transmission Elecron micrsocopy (HRTEM) image revealed stacking of WS2 (002) layers with an Interplanar spacing of 0.62 nm and periodic arrays of (100) planes with a spacing of 0.27 nm (Fig. 2c). In the planar orientation, lattice fringes along (100) and (110) planes of the hexagonal WS2 are clearly observed (Fig. 2c, d). Fig. 2e, f show TEM images of WS2-RGO sheets, which indicate uniform coverage of WS2 on RGO. HRTEM analysis reveals epitaxial growth of thin layered, hexagonal WS2 on RGO (Fig. 2g, h and Supplementary Information S3). HRTEM analysis near the edge of the WS2 sheets shows an interlayer spacing of ~0.34 nm, which confirms the growth of WS2 from that of the graphene sheet (Fig. 2c and Supplementary Information, Fig. S3). Since GO sheets exhibit enormously active edges and functional groups on their basal plane, they act as a novel substrate for the nucleation and subsequent growth of WS2. Hence during hydrothermal reaction with a GO solution, the tungsten precursor was reduced to form WS2 on GO and GO transformed to RGO.
Discussion
As described above, the hybrid nanostructures of 2D materials can be controllably prepared by the simple hydrothermal method. The hybrid nanostructures consisting of two 2D materials have numerous sharp edges and a huge proportion of nano-protrusions. Due to the unique morphologies, the hybrid nanostructures should have enhanced field emission properties. For comparison, we also show the field emission properties of pure RGO and WS2 sheets.
The Fowler-Nordehim (F-N) equation for field emitters deposited on flat substrates has been suitably modified to yield an equation in terms of current density (J) and the applied electric field (E = V/d, where V is the voltage applied between the flat cathode and the anode screen and d is their separation). The modified F-N equation is as follows56,57,
where a and b are constants (a = 1.54 × 10−6 AeV V−2, b = 6.83 eV−3/2 Vnm−1), J is the current density, E is the local electric field (surface field) and β is the local electric field enhancment factor.
The plot of the field emission current density J versus applied electric field E for WS2 is shown in Fig. 3a. The F-N plot [a plot of ln (J/E2) versus 1/E] for the WS2 sheets is shown in Fig. 3b with a calculated field enhancement factor of ~1182 (calculated from slope of the linear region of F-N plot). The F-N plot for the WS2 field emitter is nearly linear and shows a tendency for saturation at high electric fields. Fig. 3c shows the typical long term current stability from a WS2 nanosheet field emitter. Fig. 3d shows the typical field emission micrograph of the WS2 nanosheet field emitter recorded at a current density of 50 μA/cm2. The field emission from RGO sheets is shown in Fig. 4a as a function of applied electrical field versus emission current density. Fig. 4b shows the corresponding F-N plot showing linear behaviour. Fig. 4c shows the long term field emission current stabilty for RGO sheets, indiacting a stable emission current. Fig. 4d shows the field emission pattern for RGO sheets taken during long-term current stability measurments of the emitter.
Fig. 5a shows a J-E plot for the WS2-RGO nanocomposite. Fig. 5b depicts the corresponding F-N plot for the WS2-RGO nanocomposite with a field enhancement factor of 2994. Fig. 5c shows the long term current stability measurements for WS2-RGO nanocomposites. Fig. 5d shows the typical field emission micrograph of WS2-RGO sheets recored at a current density 50 μA/cm2. The field emission micrograph of the WS2-RGO composite consists of a large number of tiny bright spots and more uniform emission as compared to the WS2 and RGO field emitter.
The field enhancement factor can provide a quantitative idea of the degree of enhancement of the electric field at the emitter (WS2 and WS2-RGO) sheet edges due to their nanometric dimension. In the present case, the field enhancement factor is calculated from the slope of the F-N plots using
where β represnts the field enhacment factor, m is slope of F-N plot and ϕ is the workfunction of the emitter, which is determined from density functional theory (DFT) calculations to be 5.89 eV for WS2 and 4.48 eV for RGO (see discussion below and Computational Methods section for details). The field enhacment factor values calculated from equation (2) are found to be 2468, 2619 and 2978 for WS2, RGO and the WS2-RGO nanocomposite field emitters, respectively. Table 1 in the Supplementary Information shows a comparison of electric field values required to draw an emission current density of 1 μA/cm2, 10 μA/cm2 and 100 μA/cm2 (See. Supplementary Information).The observed turn on and threshold values for the WS2-RGO nanocomposite are significantly lower than that of the few-layered WS2 field emitter. The low turn on values in the case of WS2-RGO are attributed to the atomically sharp edges of the WS2-RGO nanocomposite sheets, which are reflected by the high value of the field ehnacment factor as compared to the WS2 field emitter. This can be explained on the basis of FE-SEM imaging which shows a higher concentration of protruding edges in the case of the WS2-RGO composite than in case of WS2 sheets. Also, the observed field emission image for WS2-RGO clearly depicts a higher density of emission spots for the emitter, corroborating with the estimated values of β as explained above. Furthermore, the DFT calculations show that in addition to the surface protrusions and edge effects, the enhanced field emission may also be partly attributed to the overlapping electronic structure of the composite.
The geometry of the composite system is featured in Fig. 6a, b. As mentioned in the Computational Methods section, for simplicity, the composite system is taken as WS2 atop graphene and in order to match the two lattices the strain is shared between the two monolayers. The strained WS2 lattice constant is taken as 3.09 Å (−1.18%) and graphene as 2.48 Å (+1.21%). Here we have defined the strain relative to the theoretically predicted lattice constants. This relatively small amount of strain has minor effects on the geometry and electronic structure of WS2 and graphene. For example, optimization of the pristine WS2 unit cell yields bond lengths of W-S = 2.39 Å and S-S = 3.12 Å, in agreement with ref. 58, whereas in the strained cell W-S = 2.38 Å and S-S = 3.15 Å. Quadrupling (Quintupling) the WS2 (graphene) lattice then gives the supercell lattice constant of 12.37 Å for the composite system. To combine the two monolayers, WS2 is simply placed atop graphene at a separation of 3.33 Å (Fig. 6b). Note that rotational and other lattice mismatch effects have not been considered in this work and are not suspected to alter the conclusions.
From our self-consistent energy calculations the work function φ of the free-standing systems can be calculated using
where Evac is the converged electrostatic potential in the vacuum region and EF is the Fermi energy. The work functions of strained WS2 φWS2 and graphene φG are computed using Equation 3. Our methodology is verified by the calculation of the work function for pristine graphene φG = 4.48 eV, which is in perfect agreement with ref. 59. For the strained WS2 monolayer it is found that φWS2 = 5.89 eV, whereas for strained graphene the work function, compared to WS2, is predicted to be significantly smaller: φG = 4.58 eV. The change in the respective work functions when the composite is formed is negligible.
The projced density of states (PDOS) analysis is featured in Fig. 6c, where only the states which give major contributions to the bands near the Fermi energy are shown, i.e. W d-states, S p-states and C p-states (Fig. 6c, left, middle and right, respectively). Note that for the freestanding WS2 system the DOS has been centered on the band gap, whereas for the composite system the Fermi energy is determined by graphene. The presence of the graphene substrate essentially has no appreciable effect on the WS2 DOS and vice-versa, besides dumping states in the band gap region of WS2. This addition of states, combined with the unappreciable change in work function, suggests that the composite system takes advantage of the best of both worlds in terms of the field emission properties of WS2 and graphene. When an electric field is applied to the system electrons will first be removed from states nearest the Fermi energy, which in the composite system are due to graphene. Although the DOS is very low near EF for graphene the work function is small, compared to WS2, so that electrons are able to escape at a lower applied field. Eventually though, after continually increasing the bias, electrons will be also be emitted by WS2. The work function of WS2 is larger than that of graphene, by 1.31 eV, but now the DOS has dramatically increased and there are more electrons available for emission. Therefore the combined effect of the relative DOS and relative work functions of WS2 and graphene also may play a role in the experimentally observed enhanced field emission.
In addition to increased performance, the applications of field emitters also require emission current stability, so it is a decisive and important parameter in the fabrication of field emission based nanoelectronic devices. Fig. 3c and Fig. 5c show the field emission current stability traces for WS2 and the WS2-RGO nanocomposite field emitters at different preset values for a sampling interval of 10 seconds recorded over a period of 3 hours. It has been observed that both WS2 and WS2-RGO show spike type fluctuations in the field emission current. The main cause of these spike-like fluctuations in emission current is adsorption/desorption and ion bombardment due to residual gas molecules8. Thus, during adsorption/desorption events the local work function varies slightly, depending upon the nature of the molecule (either electropositive or electronegative), on the emitter surface. The ion bombardment with residual gas molecules due to the presence of high electrostatic fields results in mechanical damage, further causing creation and destruction of emission sites, which in turn causes the fluctuations in the field emission current.
In summary, the field emission properties of WS2 and WS2-RGO have been investigated at the base pressure of ~1 × 10−8 mbar. The turn on field required to draw a current density of 1 μA/cm2 is found to be 3.5 V/μm and 2 V/μm for WS2 and the WS2-RGO composite, respectively. Enhanced field emission behavior is observed for WS2-RGO due to a high field enhancement factor associated with surface protrusions. In addition, the DFT results show that the enhanced field emission may be compounded by the overlapping electronic structures of WS2 and RGO. Owing to the low turn on field and planar (sheet-like) structure morphology, the WS2-RGO emitter can be utilized for new generation vacuum microelectronics/nanoelectronics and flat panel display applications.
Methods
The preparation of few layered WS2 sheets
WS2 sheets were synthesized by a one-step hydrothermal reaction. In a typical experiment, 3 mM WCl6 (Sigma-aldrich, 99.98%) and 15 mM thioacetamide (C2H5NS, Sigma-Aldrich, ≥99%) were dissolved in 40 mL DI water and stirred for 1 hour at room temperature by using a magnetic stirrer. The solution was transferred to a 50 mL stainless steel autoclave, heated up to 265°C and kept for 24 hours. After cooling naturally, the product was filtered, washed with DI water and dried in vacuum at 60°C for 6 hours.
The preparation of WS2-RGO composite
The WS2-RGO composite was synthesized by the same hydrothermal reaction condition as that for WS2 sheets. 8 mL of 5 mg/mL GO solution (see Supplementary Information) was added to the mixture of WCl6 and thioacetamide and the total volume of the solution was maintained at 40 mL. The same processes mentioned for WS2 sheets were followed. During the hydrothermal process, smaller size WS2 sheets were epitaxially formed on GO and subsequently GO transformed to RGO (see Supplementary Information, Scheme 1). Carbon content in the final product was 3 wt%, which was confirmed by elemental analysis.
Materials characterization
The samples were characterized with X-ray diffraction equipped with the following: Ni filtered Cu Kα radiation (40 kV, 100 mA, λ = 0.15418 nm), field emission scanning electron microscopy and high resolution transmission electron microscopy. The samples were also characterzied by a Micro Raman spectrometer with a laser excitation wavelength of 532 nm.
Field emission
The field emission studies of few-layered WS2/Si, RGO/Si and WS2-RGO/Si nanocomposite were investigated independently in an ultra high vacuum (UHV) chamber at the base pressure of ~1 × 10−8 mbar. The UHV chamber is equipped with a rotary backed turbo molecular pump, sputter ion pump and titanium sublimation pump. For achieving base pressure of ~1 × 10−8 mbar, the chamber was baked at 200°C for 12 hours. The field emission studies were carried out in close proximity setup, which was mounted in the UHV chamber. The close proximity setup consisted of specimens (WS2/Si, WS2-RGO/Si independently) acting as the cathode and a copper rod as the anode. Inter-electrode separation could be varied from 500 μm to 1500 μm using an insulating alumina spacer. The field emission current (I) versus applied voltage (V) was measured using Keithley 6514 electrometer and Spellman high voltage DC power supply. The field emission current stability was investigated using a computer controlled data acquisition system with a sampling interval of 10 seconds. The field emission micrographs were seen on a transparent ITO coated glass with a phosphor screen (anode) and were recorded using a digital camera (Canon SX150IS).
Computational methods
To model the WS2-RGO system we consider the composite system of a monolayer of WS2 deposited on graphene (Fig. 6a, b) within first-principles density functional theory (DFT). The DFT based Vienna ab intio simulation package (VASP)60,61,62,63 was employed with projector-augmented wave (PAW) pseudopotentials64,65 to describe the electron-ion interaction. The exchange-correlation energy is described using the local density approximation (LDA)66 and it was found that the generalized gradient approximation (GGA)67,68 produces similar results. In order to match the WS2 lattice to that of graphene, both monolayers are strained between 1–2%. To begin, the strained unit cell geometries are optimized until the forces on each atom are less than 0.01 eV/Å. For WS2 (graphene), a plane-wave basis energy cutoff of 400 eV (600 eV), a 12 × 12 × 1 (18 × 18 × 1) Monkhorst-Pack k-point sampling69 and at least 12.5 Å (10 Å) of vacuum is necessary to see convergence in the total energy on the order of 1 meV per atom for the strained unit cells. Next, the strained unit cells are expanded and combined to form the composite supercell: WS2 by 4× and graphene by 5× for a total of 98 atoms (32 S, 16 W and 50 C). WS2 is placed atop graphene at a fixed distance of 3.33 Å (Fig. 6b), representative of the van der Waals interaction between the two monolayers. Note that any further optimization of the geometry of the supercell does not affect the reported results. The strained supercell for the composite system employs similar parameters, except the k-point sampling is reduced to 6 × 6 × 1. The energy of both the unit/super-cell is relaxed until differences in total energy are less than 10−4 eV and Gaussian smearing with a width of 0.05 eV is used to describe the partial occupancies of the orbitals. From our self-consistent energy calculations the work function φ of the free-standing systems can be calculated using Equation (3) above. Note that in order for the electrostatic potential to converge smoothly in the vacuum region for the composite system, dipole corrections must be included to treat the dipole interactions which arise between periodic images in the asymmetric slab model70. Finally, the results are also accompanied by a partial density of states (PDOS) analysis for the dominant states near the Fermi energy (Fig. 6c) in order to interpret the field emission properties of WS2-RGO.
References
Geim, A. K. Graphene: Status and prospects. Science 324, 1530–1534 (2009).
Novoselov, K. S. et al. Two-dimensional atomic crystals. Proc. Nat. Acad. Sci. USA 102, 10451–10453 (2005).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Rao, C. N. R., Sood, A. K., Subrahmanyam, K. S. & Govindaraj, A. Graphene: the new two-dimensional nanomaterial. Angew. Chem. Int. Ed. 48, 7752–7777 (2009).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nature Nanotech. 6, 147–150 (2011).
Matte, H. S. S. R. et al. MoS2 and WS2 analogues of graphene. Angew. Chem. Int. Ed. 122, 4153–4156 (2010).
Late, D. J., Liu, B., Matte, H. S. S. R., Rao, C. N. R. & Dravid, V. P. Rapid characterization of ultrathin layers of chalcogenides on SiO2/Si substrates. Adv. Func. Mater. 22, 1894–1905 (2012).
Late, D. J. et al. Hysteresis in single-layer MoS2 field effect transistors. ACS Nano 6, 5635–5641 (2012).
Late, D. J. et al. Sensing behavior of atomically thin-layered MoS2 transistors. ACS Nano 7, 4879–4891 (2013).
Jariwala, D. et al. Band-like transport in high mobility unencapsulated single-layer MoS2 transistors. Appl. Phys. Lett. 102, 173107 (2013).
Yin, Z. et al. Single-layered MoS2 phtotransistor. ACS Nano 6, 74–80 (2012).
Li, H. et al. Fabrication of single-multilayer MoS2 film-based field-effect transistors for sensing NO at room temperature. Small 8, 63–67 (2012).
Tongay, S. et al. Thermally driven crossover from indirect toward direct bandgap in 2D semiconductors: MoSe2 versus MoS2 . Nano Lett. 12, 5576–5580 (2012).
Ross, J. S. et al. Electrical control of neutral and charged excitons in a monolayer semiconductor. Nature Comm. 4, 1474, 10.1038/ncomms2498 (2013).
Larentis, S., Fallahazad, B. & Tutuc, E. Field-effect transistors and intrinsic mobility in ultra-thin MoSe2 layers. Appl. Phys. Lett. 101, 223104 (1–4) (2013).
Kong, D. et al. Synthesis of MoS2 and MoSe2 Films with vertically aligned layers. Nano Lett. 13, 1341–1347 (2013).
Braga, D., Lezama, I. G., Berger, H. & Morpurgo, A. F. Quantitative determination of the band Gap of WS2 with ambipolar Ionic Liquid-gated transistors. Nano Lett. 12, 5218–5223 (2012).
Georgiou, T. et al. Vertical field-effect transistor based on graphene-WS2 heterostructures for flexible and transparent electronics. Nature Nanotech. 8, 100–103 (2013).
Fang, H. et al. High-performance single layered WSe2 p-FETs with chemically doped contacts. Nano Lett. 12, 3788–3792 (2012).
Liu, W. et al. Role of metal contacts in designing high-performance monolayer n-Type WSe2 field effect transistors. Nano Lett. 13, 1983–1990 (2013).
Zhao, W. et al. Evolution of electronic structure in atomically thin sheets of WS2 and WSe2. . ACS Nano 7, 791–797 (2013).
Late, D. J. et al. GaS and GaSe ultrathin layer transistors. Adv. Mater. 24, 3549 (2012).
Hu, P. et al. Highly Responsive Ultrathin GaS Nanosheet Photodetectors on Rigid and Flexible Substrates. Nano Lett. 13, 1649–1654 (2013).
Hu, P., Wen, Z., Wang, L., Tan, P. & Xiao, K. Synthesis of few-layer GaSe nanosheets for high performance photodetectors. ACS Nano 7, 5988–5994 (2012).
Sipos, B., Kusmartseva, A. F., Berger, A. H., FORR'O, L. & Tutis, E. From Mott state to superconductivity in 1T-TaS2. Nature Mater. 7, 96–965 (2008).
Li, H. et al. Mechanical Exfoliation and Characterization of Single- and Few-Layer Nanosheets of WSe2, TaS2 and TaSe2 . Small 9, 1974–1981 (2013).
Geller, S. J. Am. Chem. Soc. The crystal structures of RhTe and RhTe2. 77, 2641–2644 (1955).
Jan, J. P. & Skriver, H. L. Relativistic bandstructure and Fermi surface of PdTe2 by the LMTO method. J. Phys. F: Met. Phys. 7, 1719–1730 (1977).
Gorbachev, R. V. et al. Hunting for monolayer Boron Nitride: Optical and Raman signatures. Small 7, 465–468 (2011).
Kim, K. K. et al. Synthesis and characterization of hexagonal boron nitride film as a dielectric layer for graphene devices. ACS Nano 6, 8583–8590 (2012).
Kreis, C., Werth, S., Adelung, R., Kipp, L. & Skibowski, M. Valence and conduction band states of HfS2: From bulk to a single layer. Phys. Rev. B 68, 235331 (1–6) (2003).
Liu, C. & Frindt, R. F. Anisotropic optical-absorption studies of NbS2 single-layer suspensions aligned in a magnetic field. Phys. Rev. B 31, 4086–4088 (1985).
Ayari, A., Cobas, E., Ogundadegbe, O. & Fuhrer, M. S. Realization and electrical characterization of ultrathin crystals of layered transition-metal dichalcogenides. J. Appl. Phys. 101, 014507 (1–5) (2007).
Brown, B. E. The crystal structures of NbT2 and TaT2 . Acta Cryst. 20, 264–267 (1966).
Castellanos-Gomez, A. et al. Fast and reliable identification of atomically thin layers of TaSe2 crystals. Nano Research 10.1007/s12274-013-0295-9 (2013).
Galvis, J. A. et al. Scanning tunneling measurements of layers of superconducting 2H-TaSe2: Evidence for a zero-bias anomaly in single layers. Phys. Rev. B 87, 094502 (1–9) (2013).
Teweldebrhan, D., Goyal, V. & Balandin, A. A. Exfoliation and characterization of bismuth telluride atomic quintuples and quasi-two dimensional crystals. Nano Lett. 10, 1209–1218 (2010).
Teweldebrhan, D., Goyal, V., Rahman, M. & Balandin, A. A. Atomically-thin crystalline films and ribbons of bismuth telluride. Appl. Phys. Lett. 96, 053107 (1–3) (2010).
Steinberg, H., Gardner, D. R., Lee, Y. S. & Jarillo-Herrero, P. Surface state transport and ambipolar electric field effect in Bi2Se3 nanodevices. Nano Lett. 10, 5032–5036 (2010).
Xia, Y. et al. Observation of a large-gap topological-insulator class with a single Dirac cone on the surface. Nat. Phys. 5, 398–402 (2009).
de Heer, W. A., Châtelain, A. & Ugarte, D. A carbon nanotube field-emission electron source. Science 270, 1179–1180 (1995).
Sharma, R. B., Late, D. J., Joag, D. S., Govindaraj, A. & Rao, C. N. R. Field emission properties of boron and nitrogen doped carbon nanotubes. Chem. Phy. Lett. 428, 102–108 (2006).
Banerjee, D., Jo, S. H. & Ren, Z. F. Enhanced Field Emission of ZnO Nanowires. Adv. Mater. 16, 2028–2032 (2004).
Ramgir, N. S. et al. Ultralow threshold field emission from a single multipod structure of ZnO. Appl. Phys. Lett. 88, 042107 (1–3) (2006).
Late, D. J. et al. Enhanced field emission from pulsed laser deposited ZnO thin films on Re and W. Appl. Phys. A 95, 613–620 (2009).
Late, D. J. et al. Field emission studies on well adhered pulsed laser deposited LaB6 on W tip. Appl. Phys. Lett. 89, 123510 (1–3) (2006).
Late, D. J. et al. Some aspects of pulsed laser deposited nanocrystalline LaB6 film: atomic force microscopy, constant force current imaging and field emission investigations. Nanotechnology 19, 265605 (2008).
Late, D. J. et al. Synthesis of LaB6 micro/nano structures using picosecond (Nd:YAG) laser and its field emission investigations. Applied Physics A 97, 905–909 (2009).
Palnitkar, U. A. et al. Remarkably low turn-on field emission in undoped, nitrogen-doped and boron-doped grapheme. Appl. Phys. Lett. 97, 063102 (1–3) (2010).
Santandrea, S. et al. Field emission from single and few-layer graphene flakes. Appl. Phys. Lett. 98, 163109 (1–3) (2011).
Ye, D., Moussa, S., Ferguson, J. D., Baski, A. A. & Samy Ei-Shall, M. Highly efficient electron field emission from graphene oxide sheets supported by nickel nanotip arrays. Nano Lett. 12, 1265–1268 (2012).
Kashid, R. V. et al. Enhanced field-emission behavior of layered MoS2 sheets. Small 9, 2730–2734 (2013).
Tenne, R., Margulis, L., Genut, M. & Hodes, G. Polyhedral and cylindrical structures of tungsten disulfide. Nature 360, 444 (1992).
Verble, J. L. & Wieting, T. J. Lattice Mode Degeneracy in MoS2 and Other Layer Compounds. Phys. Rev. Lett. 25, 362–365 (1970).
Virsek, M., Jesih, A., Milosevic, I., Damnjanovic, M. & Remskar, M. Raman scattering of the MoS2 and WS2 single nanotubes. Surface Science 601, 2868–2872 (2007).
[Fursey G. (ed.)] Field emission in vacuum microelectronics. (Kluwer Academic/Plenum publishers, New York, 2005).
Fowler, R. H. & Nordheim, L. Proceedings of the Royal Society of London, Electron emission in intense electric field. 119, 173–181 (1928).
Ding, Y. et al. First principles study of structural vibrational and electronic properties of graphene-like MX2 (M = Mo, Nb, W, Ta; X = S, Se, Te) monolayers. Physica B-Condensed Matter. 406, 2254–2260 (2011).
Giovannetti, G. et al. Doping Graphene with Metal Contacts. Phys. Rev. Lett. 101, 026803 (1–4) (2008).
Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab-initio total energy calculations using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal–amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).
Blochl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P. & Zunger, A. Self-interaction correction to density-functional approximations for many-electron systems. Phys. Rev. B 23, 5048–5079 (1981).
Perdew, J. P. et al. Atoms, molecules, solids and surfaces: Applications of the generalized gradient approximation for exchange and correlation. Phys. Rev. B 46, 6671–6687 (1992).
Perdew, J. P. et al. Erratum: Atoms, molecules, solids and surfaces: Applications of the generalized gradient approximation for exchange and correlation. Phys. Rev. B 48, 4978–4978 (1993).
Monkhorst, H. J. & Pack, J. D. Special points for brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Neugebauer, J. & Scheffler, M. Adsorbate-substrate and adsorbate-adsorbate interactions of Na and K adlayers on Al(111). Phys. Rev. B 46, 16067–16080 (1992).
Acknowledgements
Authors C.S. Rout and D.J. Late would like to thank DST for the Ramanujan fellowship and Prof. C.N.R. Rao (FRS), for support and encouragement. P.D.J. would like to thank UGC for fellowship. D.S.J. and R.V.K. would like to thank CSIR (Government of India) for Emeritus Scientist Scheme and SRF respectively. This work is supported by the Interconnect Focus Center (MARCO program), State of New York; the National Science Foundation (NSF) Integrative Graduate Education and Research Traineeship (IGERT) program, Grant No. 0333314; the NSF Petascale Simulations and Anaylsis (PetaApps) program, Grant No. 0749140; the Army Research Laboratory under cooperative agreement number W911NF-12-2-0023; an anonymous gift from Rensselaer and CSIR-National Chemical Laboratory, Pune (India) MLP project Grant No. 028626. Computing resources of the Computational Center for Nanotechnology Innovations (CCNI) at Rensselaer, partly funded by the State of New York, have been used for this work.
Author information
Authors and Affiliations
Contributions
C.S.R., D.J.L. and S.K.N. designed experiment. C.S.R., P.D.J., R.V.K. carried out experiment. A.J.S. performed computational calculation. C.S.R., D.S.J., M.A.M., M.W., S.K.N. and D.J.L. carried out data analysis and co-wrote the manuscript. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by/3.0/
About this article
Cite this article
Rout, C., Joshi, P., Kashid, R. et al. Superior Field Emission Properties of Layered WS2-RGO Nanocomposites. Sci Rep 3, 3282 (2013). https://doi.org/10.1038/srep03282
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep03282
This article is cited by
-
Printed transistors made of 2D material-based inks
Nature Reviews Materials (2023)
-
Copper, Palladium, and Reduced Graphene Oxide Co-doped Layered WS2/WO3 Nanostructures for Electrocatalytic Hydrogen Generation
Electronic Materials Letters (2023)
-
Fabrication of platinum-doped WS2 hollow spheres catalyst for high-efficient hydrogen evolution reaction
Journal of Applied Electrochemistry (2022)
-
Printable Highly Stable and Superfast Humidity Sensor Based on Two Dimensional Molybdenum Diselenide
Scientific Reports (2020)
-
High capacitive rGO/WO3 nanocomposite: the simplest and fastest route of preparing it
Applied Nanoscience (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.