Modified polyol synthesis of bulk-scale nanostructured bismuth antimony telluride

M. E. Anderson,a   S. S. N. Bharadwayabc  and  R. E. Schaak*ac  

* Corresponding authors

a Department of Chemistry, The Pennsylvania State University, University Park, PA, USA
E-mail: schaak@chem.psu.edu

b Center for Dielectric Studies, The Pennsylvania State University, University Park, PA, USA

c Materials Research Institute, The Pennsylvania State University, University Park, PA, USA

Abstract

Bismuth antimony telluride, Bi0.5Sb1.5Te3, is a prototype thermoelectric alloy for which nanostructuring has been shown to improve the thermoelectric figure of merit. Most bulk-scale nanostructured thermoelectric materials are synthesized using either traditional solid-state routes or “top-down” physical methods such as ball milling, sputtering, etc. “Bottom-up” chemical methods represent an important alternative route to nanostructured thermoelectrics, but often produce small sample sizes that make transport measurements difficult. Here, nanostructured Bi0.5Sb1.5Te3 has been synthesized in half-gram quantities using a simple and scalable modified polyol process. Stoichiometric amounts of appropriate metal salts were combined in tetraethylene glycol with and without poly(vinylpyrrolidone) (PVP), reduced with sodium borohydride, and heated in solution and in powder form to obtain samples of crystalline Bi0.5Sb1.5Te3. The structure, composition, and morphology of the products were characterized using powder XRD, TEM, SEM, and EDS mapping data. The Seebeck coefficient, measured from 300–500 K for 1 cm sintered pellets of Bi0.5Sb1.5Te3, increased with temperature and was found to be +256 µV K−1 at 500 K. Bulk-scale nanostructured powders of other thermoelectrics could also be synthesized, including Bi2Te3, PbTe, Sb2Te3, AgSbTe2, and Pb1−xSnxTe.

Graphical abstract: Modified polyol synthesis of bulk-scale nanostructured bismuth antimony telluride

About
Cited by
Related
Download options Please wait...

Article information

DOI
https://doi.org/10.1039/C0JM01424A
Article type
Paper
Submitted
12 May 2010
Accepted
10 Jul 2010
First published
26 Aug 2010

J. Mater. Chem., 2010,20, 8362-8367

Permissions

Request permissions

Modified polyol synthesis of bulk-scale nanostructured bismuth antimony telluride

M. E. Anderson, S. S. N. Bharadwaya and R. E. Schaak, J. Mater. Chem., 2010, 20, 8362 DOI: 10.1039/C0JM01424A

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Spotlight

Advertisements