Issue 39, 2014

Single phase, electrically insulating, multiferroic La-substituted BiFeO3 prepared by mechanosynthesis

Abstract

Single phase, electrically insulating samples of Bi1−xLaxFeO3 solid solutions have been prepared by mechanosynthesis over the whole compositional range for the first time. Lanthanum substitution influenced the kinetics of the mechanochemical reaction and crystallite size of the products. For 0 ≤ x ≤ 0.15, an increase in the La content produced a significant decrease in the weight-normalized cumulative kinetic energy required to obtain the final product and an increase in the resulting crystallite size. Larger La contents did not affect either the reactivity or the crystallite size. The effect of x on the structure has been identified. Samples in the ranges x ≤ 0.15 and x ≥ 0.45 gave single phase solid solutions with R3c and Pnma space groups, respectively, while for the intermediate range, a non-centrosymetric Pn21a(00γ)s00 super structure was obtained. For 0 ≤ x ≤ 0.30, differential scanning calorimetry showed two endothermic effects corresponding to the Néel temperature (TN, antiferromagnetic–paramagnetic transition) and the Curie temperature (TC, ferroelectric–paraelectric transition), demonstrating their multiferroic character. Compositions with a larger La content only showed TN. Dilatometric and permittivity measurements confirmed the results obtained by DSC for the ferroelectric–paraelectric transition. The composition dependence of TN and TC showed that, at low x, TN < TC, but a cross-over, or isoferroic transition occurred at x ∼0.28, when TN = TC = 386 °C. Ceramics with 0 ≤ x ≤ 0.15 were highly insulating at room temperature with a resistivity, extrapolated from the Arrhenius plots, of ∼7 × 1016 to 8 × 1014 Ω cm and an activation energy ∼1.14–1.20 eV. Magnetization of the samples improved with La substitution.

Graphical abstract: Single phase, electrically insulating, multiferroic La-substituted BiFeO3 prepared by mechanosynthesis

Supplementary files

Article information

Article type
Paper
Submitted
02 Jul 2014
Accepted
08 Aug 2014
First published
08 Aug 2014

J. Mater. Chem. C, 2014,2, 8398-8411

Author version available

Single phase, electrically insulating, multiferroic La-substituted BiFeO3 prepared by mechanosynthesis

A. Perejón, P. E. Sánchez-Jiménez, L. A. Pérez-Maqueda, J. M. Criado, J. Romero de Paz, R. Sáez-Puche, N. Masó and A. R. West, J. Mater. Chem. C, 2014, 2, 8398 DOI: 10.1039/C4TC01426J

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements