Roll-to-roll coated PBI membranes for high temperature PEMfuel cells

Abstract

We employed roll-to-roll coating in the preparation of 40 μm thick poly[2,2′(m-phenylene)-5,5′bibenzimidazole] (PBI) films for fuel cells using both knife-coating (KC) and slot-die (SD) coating. The films were coated directly from a 9% (w/w) solution of PBI in dimethylacetamide onto a sacrificial low cost paper or plastic based carrier substrate and dried using a hot air oven with a length of 1 m at 140 °C. A web width of 305 mm, a working width of 250 mm and a web speed of 0.2 m min−1 were explored to ensure efficient drying of the thick wet film. A large air flow was found to efficiently avoid skinning. Films were prepared by a single coating step and by two subsequent coating steps in order to explore whether two coating steps gave films with fewer defects. A significant development towards upscaling the PEM fuel cell technology was that the PBI membrane was coated onto a sacrificial carrier substrate allowing for easy recoating on top of the firstly prepared film. It was thus possible to prepare free-standing films by a simple coating procedure followed by delamination from the carrier substrate post-film formation and drying. We finally carried out systematic membrane characterization with respect to solubility, phosphoric acid doping and fuel cell performance. Our results showed that the PBI membranes prepared in this work have identical properties compared to traditionally cast membranes while enabling an increase of a factor of 100 in manufacturing speed.

Graphical abstract: Roll-to-roll coated PBI membranes for high temperature PEM fuel cells

Article information

Article type
Paper
Submitted
19 Oct 2011
Accepted
22 Dec 2011
First published
25 Jan 2012

Energy Environ. Sci., 2012,5, 6076-6080

Roll-to-roll coated PBI membranes for high temperature PEM fuel cells

T. Steenberg, H. A. Hjuler, C. Terkelsen, M. T. R. Sánchez, L. N. Cleemann and F. C. Krebs, Energy Environ. Sci., 2012, 5, 6076 DOI: 10.1039/C2EE02936G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements