Improved hydrophilicity, permeability, antifouling and mechanical performance of PVDF composite ultrafiltration membranes tailored by oxidized low-dimensional carbon nanomaterials

Abstract

Polyvinylidene fluoride (PVDF)–oxidized carbon nanotubes (OMWCNTs), PVDF–graphene oxide (GO) and PVDF–OMWCNTs–GO composite ultrafiltration membranes were prepared by solution-blending the ternary mixture of PVDF–oxidized low-dimensional carbon nanomaterials–dimethylacetamide in combination with the phase inversion method. The microscope images of the PVDF matrix microstructure showed that the composite membranes exhibited a bigger mean pore size and higher roughness parameters than pristine membranes. The contact angle of the membranes decreased from 78.5° (PVDF) to 66.8° (PVDF–OMWCNTs), 66.4° (PVDF–GO) and 48.5° (PVDF–OMWCNTs–GO). For the PVDF–OMWCNTs, PVDF–GO and PVDF–OMWCNTs–GO composite membranes, there was a 99.33%, 173.03% and 240.03% increase in permeation flux and a 21.71%, 17.23% and 14.29% increase in bovine serum albumin (BSA) rejection, respectively, compared with those of the pristine membranes. The newly developed composite ultrafiltration membranes demonstrate an impressive prospect for the anti-irreversible fouling performance in multi-cycle operations from BSA treatment. Additionally, the addition of OMWCNTs and GO increased the tensile strength of composite membranes from 1.866 MPa to 2.106 MPa and 2.686 MPa, respectively. Conspicuously, the PVDF composite ultrafiltration membranes endowed with oxidized low-dimensional carbon nanomaterials demonstrated fascinating hydrophilicity, permeability, antifouling and mechanical performance and promising application prospects owing to the rich oxygen-containing functional groups, high specific surface and synergistic effect of inorganic additive.

Graphical abstract: Improved hydrophilicity, permeability, antifouling and mechanical performance of PVDF composite ultrafiltration membranes tailored by oxidized low-dimensional carbon nanomaterials

Article information

Article type
Paper
Submitted
08 Sep 2012
Accepted
02 Jan 2013
First published
04 Jan 2013

J. Mater. Chem. A, 2013,1, 3101-3111

Improved hydrophilicity, permeability, antifouling and mechanical performance of PVDF composite ultrafiltration membranes tailored by oxidized low-dimensional carbon nanomaterials

J. Zhang, Z. Xu, W. Mai, C. Min, B. Zhou, M. Shan, Y. Li, C. Yang, Z. Wang and X. Qian, J. Mater. Chem. A, 2013, 1, 3101 DOI: 10.1039/C2TA01415G

To request permission to reproduce material from this article, please go to the Copyright Clearance Center request page.

If you are an author contributing to an RSC publication, you do not need to request permission provided correct acknowledgement is given.

If you are the author of this article, you do not need to request permission to reproduce figures and diagrams provided correct acknowledgement is given. If you want to reproduce the whole article in a third-party publication (excluding your thesis/dissertation for which permission is not required) please go to the Copyright Clearance Center request page.

Read more about how to correctly acknowledge RSC content.

Social activity

Spotlight

Advertisements