Abstract
By methods of modern physical materials science the investigations analysis of phase composition, defect substructure, mechanical and tribological properties of Cr–Nb–C–V containing coatings formed in surfacing on martensitic wear resistant steel Hardox 450 were carried out. It was shown that surfacing resulted in the formation of high strength surface layer 6 mm in thinness. This layer had wear resistance 138 times greater than that of the base and friction coefficient 2.5 times less. On the basis of the investigations by methods of X-ray structural analysis and transmission diffraction electron microscopy it was shown that increase strength and tribological properties of surfacing metal were caused by its phase composition and state of defect substructure, namely, availability of interstitial phases (more than 36%) and martensitic type of α-phase structure.
Similar content being viewed by others
References
E. K. Mussada and P. K. Patowari, Int. J. Mach. Machinability Mater. 17 (1), 65 (2007). doi 10.1504/IJMMM.2015.069230
X. Qi, S. Zhu, H. Ding, Z. Zhu, and Z. Han, Appl. Surf. Sci. 282, 672 (2013). doi 10.1016/j.apsusc.2013.06.032
X. Chen, Y. Fang, P. Li, Z. Yu, X. Wu, and D. Li, Mater. Des. 65, 1214 (2015). doi 10.1016/j.matdes. 2014.10.013
E. V. Kapralov, S. V. Raykov, E. A. Budovskikh, V. E. Gromov, E. S. Vashchuk, and Yu. F. Ivanov, Bull. Russ. Acad. Sci.: Phys. 78 (10), 1015 (2014). doi 10.3103/S1062873814100098
S. V. Raikov, E. V. Kapralov, Yu. F. Ivanov, E. A. Budovskikh, and V. E. Gromov, Steel Transl. 45 (2), 120 (2015). doi 10.3103/S0967091215020126
V. G. Kurdyumov, A. M. Utevskii, and R. I. Entin, Transformations in Iron and Steel (Nauka, Moscow, 1977).
Yu. N. Petrov, Defects and Diffusion: Free Transformation in Steel (Naukova Dumka, Kiev, 1978).
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Konovalov, S.V., Kormyshev, V.E., Gromov, V.E. et al. Formation features of structure-phase states of Cr–Nb–C–V containing coatings on martensitic steel. J. Surf. Investig. 10, 1119–1124 (2016). https://doi.org/10.1134/S1027451016050098
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1027451016050098