Abstract
We report a large entropy change (ΔS) below 300 K, peaking near T C = 220 K, due to isothermal change of magnetic field, for Gd4Co3, with a refrigeration capacity higher than that for, say, LaFe11.4Si1.6, ordering magnetically in the same temperature range. A noteworthy finding is that the isothermal magnetization is nonhysteretic — an important criterion for magnetic refrigeration without loss. ΔS behavior is also compared with that of magnetoresistance.
Similar content being viewed by others
References
See, a review, K.A. Gschneidner Jr, V.K. Pecharsky, A.O. Tsokol, Rep. Prog. Phys. 68, 1479 (2005)
A.M. Tishin, J. Magn. Magn. Mater. 316, 351 (2007)
V. Provenzano, A.J. Shapiro, R.D. Shull, Nature 429, 853 (2004)
R. Lemaire, J. Schweizer, J. Yakinthos, Acta Cryst. B 25, 710 (1969)
E. Gratz, V. Sechovsky, E.P. Wohlfarth, H.R. Kirchmayr, J. Phys. F: Metal Physics 10, 2819 (1980)
E. Burzo, Phys. Rev. B 6, 2882 (1972)
T.M. Seixas, J.M. Machado da Silva, T.P. Papageorgiou, H.F. Braun, G. Eska, Physica B 353, 34 (2004)
K.A. Gschneidner, Jr., V.K. Pecharsky, A.O. Pecharsky, C.B. Zimm, Mater. Sci. Forum 315, 69 (1999)
M.E. Wood, W.H. Potter, Cryogenics 25, 667 (1985)
V. Franco, J.S. Blazquez, A. Conde, J. Appl. Phys. 55, 4336 (1984); V. Franco, A. Conde, V.K. Pecharsky, K.A. Gschneidner Jr. Europhys. Lett. 79, 47009 (2007)
Q.-y. Dong, H.-w. Zhang, J.-l. Shen, J.-r. Sun, B.-g. Shen, J. Magn. Magn. Mater. 319, 56 (2007)
K. Sengupta, K.K. Iyer, E.V. Sampathkumaran, Phys. Rev. B 72, 054422 (2005)
R. Rawat, I. Das, J. Phys. Cond. Mat. 13, L379 (2001)
K. Sengupta, K.K. Iyer, E.V. Sampathkumaran, Solid State Commun. 139, 351 (2006); K. Sengupta, S. Rayaprol, E.V. Sampathkumaran, Europhys. Lett. 69, 454 (2005)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mohapatra, N., Iyer, K.K. & Sampathkumaran, E.V. Large magnetocaloric effect and magnetoresistance behavior in Gd4Co3 . Eur. Phys. J. B 63, 451–454 (2008). https://doi.org/10.1140/epjb/e2008-00266-x
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1140/epjb/e2008-00266-x