Rare Earth Doped Zinc Oxide Nanowires
Zinc oxide (ZnO) nanowires were grown via thermal transport and subsequently doped with different concentrations of Tm, Yb, and Eu using ion implantation and post annealing. High ion fluences lead to morphology changes due to sputtering; however, freestanding nanowires become less damaged
compared to those attached to substrates. No other phases like rare earth (RE) oxides were detected, no amorphization occurs in any sample, and homogeneous doping with the desired concentrations was achieved. Photoluminescence measurements demonstrate the optical activation of trivalent RE-elements
and the emission of the characteristic intra-4f-luminescence of the respective RE atoms, which could be assigned according to the Dieke-diagram. An increasing RE concentration results into decreasing luminescence intensity caused by energy transfer mechanisms to non-radiative remaining implantation
defect sites. Furthermore, low thermal quenching was observed due to the considerable wide band gap of ZnO.
Keywords: DOPED; ION IMPLANTATION; RARE EARTH; ZNO NANOWIRES
Document Type: Research Article
Publication date: 01 January 2008
- Journal for Nanoscience and Nanotechnology (JNN) is an international and multidisciplinary peer-reviewed journal with a wide-ranging coverage, consolidating research activities in all areas of nanoscience and nanotechnology into a single and unique reference source. JNN is the first cross-disciplinary journal to publish original full research articles, rapid communications of important new scientific and technological findings, timely state-of-the-art reviews with author's photo and short biography, and current research news encompassing the fundamental and applied research in all disciplines of science, engineering and medicine.
- Editorial Board
- Information for Authors
- Subscribe to this Title
- Terms & Conditions
- Ingenta Connect is not responsible for the content or availability of external websites
- Access Key
- Free content
- Partial Free content
- New content
- Open access content
- Partial Open access content
- Subscribed content
- Partial Subscribed content
- Free trial content