Abstract
Heat treatment (HT) enhances various properties of wood (W), but it takes a relatively long time and WHT is a source of fire hazard. To improve the properties of WHT, Populus beijingensis W. Y. Hsu wood was impregnated with nitrogen-phosphorus (NP) fire retardant (10% aqueous solution) and the effects of the combined NP treatment and HT were observed. Control groups included native wood and samples from WHT200°C, 120 min and WHT220°C, 120 min. The surface color, dimensional stability, and combustion properties of the treated samples were examined. NP pre-treatment intensified the effectivity of HT150°C, where the treatment time decreased by 75%. The decomposition and catalytic dehydration of NP treatment enhanced the dimensional stability and darkened the wood surface. After HT, the NP fire retardant was transformed from dispersive particles into a uniform layer on the inner surfaces of wood. The heat release rate (HRR) decreased by 60.3% and the residual mass (RM) increased by 61.1% in WNP, HT compared to normal WHT200°C poplar.
Acknowledgements
The authors are grateful for the support of the Forestry Public Welfare Project Foundation of China (201404502).
References
ASTM 1354-04A (2004). Standard test method for heat and visible smoke release rates for materialsand products using an oxygen consumption calorimeter.Search in Google Scholar
Awoyemi, L. (2008) Determination of optimum borate concentration for alleviating strength loss during heat treatment of wood. Wood Sci. Technol. 42:39–45.10.1007/s00226-007-0139-4Search in Google Scholar
Awoyemi, L., Westermark, U. (2005) Effects of borate impregnation on the response of wood strength to heat treatment. Wood Sci. Technol. 39:484–491.10.1007/s00226-005-0001-5Search in Google Scholar
Awoyemi, L., Jarvis, M.C., Hapca, A. (2009) Effects of preboiling on the acidity and strength properties of heat-treated wood. Wood Sci. Technol. 43:97–103.10.1007/s00226-008-0231-4Search in Google Scholar
Awoyemi, L., Femi-Ola, T.O., Aderibigbe, E.Y. (2010) Pre-freezing as a pre-treatment for thermal modification of wood. Part 2: surface properties and termite resistance. J. Ind. Acad. Wood Sci. 7:19–24.10.1007/s13196-010-0004-1Search in Google Scholar
Aytin, A., Korkut, S. (2015) Effect of thermal treatment on the swelling and surface roughness of common alder and wych elm wood. J. For. Res.27:1–5.10.1007/s11676-015-0136-7Search in Google Scholar
Aytin, A., Korkut, S., Ünsal, Ö., Çakicier, N. (2015). The effects of heat treatment with the thermowood® method on the equilibrium moisture content and dimensional stability of wild cherry wood. Bioresources 10:2083–2093.10.15376/biores.10.2.2083-2093Search in Google Scholar
Bekhta, P., Niemz, P. (2003) Effect of high temperature on the change in color, dimensional stability and mechanical properties of spruce wood. Holzforschung 57:539–546.10.1515/HF.2003.080Search in Google Scholar
Bekhta, P., Proszyk, S.A., Krystofiak, T. (2014) Colour in short-term thermo-mechanically densified veneer of various wood species. Eur. J. Wood Prod. 72:785–797.10.1007/s00107-014-0837-1Search in Google Scholar
Boonstra, M.J., Rijsdijk, J.F., Sander, C., Kegel, E., Tjeerdsma, B., Militz, H., van Acker, J., Stevens, M. (2005) Microstructural and physical aspects of heat treated wood. Part 1.Softwoods. Maderas Cienc. Tecnol. 8:193–208.Search in Google Scholar
Boonstra, M.J., Rijsdijk, J.F., Sander, C., Kegel, E., Tjeerdsma, B., Militz, H., van Acker, J., Stevens, M. (2006) Microstructural and physical aspects of heat treated wood. Part 2. Hardwoods. Maderas Cienc. Tecnol. 8:209–217.10.4067/S0718-221X2006000300007Search in Google Scholar
Bourgois, J., Janin, G., Guyonnet, R. (1991) The color measurement: a fast method to study and to optimize the chemical transformations undergone in the thermically treated wood. Holzforschung 45:377–382.10.1515/hfsg.1991.45.5.377Search in Google Scholar
Brischke, C., Welzbacher, C.R., Brandt, K., Rapp, A.O. (2007) Quality control of thermally modified timber: interrelationship between heat treatment intensities and CIE L*a*b* color data on homogenized wood samples. Holzforschung 61:19–22.10.1515/HF.2007.004Search in Google Scholar
Dubey, M.K., Pang, S., Walker, J. (2012) Changes in chemistry, color, dimensional stability and fungal resistance of Pinus radiata D. Don wood with oil heat-treatment. Holzforschung 66:49–57.10.1515/HF.2011.117Search in Google Scholar
Esteves, B.M., Pereira, H.M. (2009) Wood modification by heat treatment: a review. Bioresources 4:370–404.10.15376/biores.4.1.EstevesSearch in Google Scholar
Fabian, T.Z. (2014) Fire performance properties of solid wood and lignocellulose-plastic composite deck boards. Fire. Technol. 50:125–141.10.1007/s10694-012-0307-4Search in Google Scholar
Gu, B. (2007) Study on the effects of properties of UF plywood treated with BL-environmental-friendly flame retardant. In: Composition Analysis of BL Environmental Protection Flame Retardant. Doctoral thesis, Beijing Forestry University, Beijing, China, pp. 50–56.Search in Google Scholar
Guo, J., Song, K.L., Salmén, L., Yin, Y.F. (2015) Changes of wood cell walls in response to hygro-mechanical steam treatment. Carbohydr. Polym. 115:207–214.10.1016/j.carbpol.2014.08.040Search in Google Scholar PubMed
Gunduz, G., Korkut, S., Aydemir, D., Bekar, Í. (2009) The density, compression strength and surface hardness of heat treated hornbeam (Carpinus betulus) wood. Maderas Cienc. Tecnol. 11:61–70.10.4067/S0718-221X2009000100005Search in Google Scholar
Günther, B., Gebauer, K., Barkowski, R., Rosenthal, M., Bues, C. (2012) Calorific value of selected wood species and wood products. Eur. J. Wood Prod. 70:755–757.10.1007/s00107-012-0613-zSearch in Google Scholar
Hill, C.A.S. Wood modification: chemical, thermal and other processes. John Wiley & Sons, Chichester, 2006.10.1002/0470021748Search in Google Scholar
Huang, X., Kocaefe, D., Kocaefe, Y., Boluk, Y., Pichette, A. (2012) A spectrocolorimetric and chemical study on color modification of heat-treated wood during artificial weathering. Appl. Surf. Sci. 258:5360–5369.10.1016/j.apsusc.2012.02.005Search in Google Scholar
Huang, X., Kocaefe, D., Kocaefe, Y., Boluk, Y., Krause, C. (2013) Structural analysis of heat-treated birch (Betula papyrifera) surface during artificial weathering. Appl. Surf. Sci. 264:117–127.10.1016/j.apsusc.2012.09.137Search in Google Scholar
Hyttinen, M., Masalin-Weijo, M., Kalliokoski, P., Pasanen, P. (2010) Comparison of VOC emissions between air-dried and heat-treated Norway spruce (Picea abies), Scots pine (Pinus sylvestris) and European aspen (Populus tremula) wood. Atmos. Environ. 44:5028–5033.10.1016/j.atmosenv.2010.07.018Search in Google Scholar
Inari, G.N., Petrissans, M., Lambert, J., Ehrhardt, J.J., Gerardin, P. (2006) XPS characterization of wood chemical composition after heat-treatment. Surf. Interface Anal. 38:1336–1342.10.1002/sia.2455Search in Google Scholar
ISO (1993) 5660-1 Fire tests.Reaction to fire. Part 1: Rate of heat release from building products (cone calorimeter method).Search in Google Scholar
Kačíková, D., Kačík, F., Cabalová, I., Durkovič, J. (2013) Effects of thermal treatment on chemical, mechanical and colour traits in Norway spruce wood. Bioresour. Technol. 144:669–674.10.1016/j.biortech.2013.06.110Search in Google Scholar PubMed
Kookandeh, M.G., Taghiyari, H.R., Siahposht, H. (2014). Effects of heat treatment and impregnation with zinc-oxide nanoparticles on physical, mechanical, and biological properties of beech wood. Wood Sci. Technol. 48:727–736.10.1007/s00226-014-0627-2Search in Google Scholar
Korkut, S., Aytin, A. (2015) Evaluation of physical and mechanical properties of wild cherry wood heat-treated using the thermowood process. Maderas Cienc. Tecnol. 17:171–178.10.4067/S0718-221X2015005000017Search in Google Scholar
Korkut, D.S., Guller, B. (2008) The effects of heat treatment on physical properties and surface roughness of red-bud maple (Acer trautvetteriMedw.) wood. Bioresour. Technol. 99:2846–2851.10.1016/j.biortech.2007.06.043Search in Google Scholar PubMed
Korkut, S., Hiziroglu, S. (2009) Effect of heat treatment on mechanical properties of hazelnut wood (Corylus colurna L.). Mater. Des. 30:1853–1858.10.1016/j.matdes.2008.07.009Search in Google Scholar
Korkut, S., Akgül, M., Dündar, T. (2008) The effects of heat treatment on some technological properties of Scots pine (Pinus sylvestris L.) wood. Bioresour. Technol. 99:1861–1868.10.1016/j.biortech.2007.03.038Search in Google Scholar PubMed
Kwon, J.H., Shin, R., Ayrilmis, N., Han, T.H. (2014) Properties of solid wood and laminated wood lumber manufactured by cold pressing and heat treatment. Mater. Des. 62:375–381.10.1016/j.matdes.2014.05.032Search in Google Scholar
Martinka, J., Hroncová, E., Chrebet, T., Balog, K. (2014) The influence of spruce wood heat treatment on its thermal stability and burning process. Eur. J. Wood Prod. 72:477–486.10.1007/s00107-014-0805-9Search in Google Scholar
Matsuo, M., Umemura, K., Kawai, S. (2014) Kinetic analysis of color changes in keyaki(Zelkovaserrata) and sugi (Cryptomeria japonica) wood during heat treatment. J. Wood Sci. 60:12–20.10.1007/s10086-013-1369-8Search in Google Scholar
Militz, H., Tjeerdsma, B. (2001) Heat treatment of wood by the PLATO-process. Proceedings of COST E22 environmental optimization of wood prorection, Antibes, France.Search in Google Scholar
Olarescu, C.M., Campean, M. (2014) Color change – mass loss correlation for heat-treated wood. CBU International conference on innovation, technology transfer and education, Prague, Czech Republic.10.12955/cbup.v2.483Search in Google Scholar
Ozcan, S., Ozcifci, A., Hiziroglu, S., Toker, H. (2012) Effects of heat treatment and surface roughness on bonding strength. Constr. Build. Mater. 33:7–13.10.1016/j.conbuildmat.2012.01.008Search in Google Scholar
Pan, J., Mu, J., Wu, Z.X., Zhang, X.T. (2014) Effect of nitrogen-phosphorus fire retardant blended with Mg(OH)2/Al(OH)3 and nano-SiO2 on fire-retardant behavior and hygroscopicity of poplar. Fire. Mater. 38:817–826.10.1002/fam.2224Search in Google Scholar
Pelit, H., Budakçı, M., Sönmez, A., Burdurlu, E. (2015) Surface roughness and brightness of scots pine (Pinus sylvestris) applied with water-based varnish after densification and heat treatment. J. Wood Sci. 61:1–9.10.1007/s10086-015-1506-7Search in Google Scholar
Pétrissans, M., Gérardin, P., EI Bakali. I., Serraj, M. (2003) Wettability of heat-treated wood. Holzforschung 57: 301–307.10.1515/HF.2003.045Search in Google Scholar
Rekola, J., Lassila, L.V.J., Nganga, S., Ylä-Soininmäki, A., Fleming, G.J.P., Grenman, R., Aho, A.J., Vallittu, P.K. (2014) Effect of heat treatment of wood on the morphology, surface roughness and penetration of simulated and human blood. Biomed. Mater. Eng. 24:1595–1607.10.3233/BME-140964Search in Google Scholar PubMed
Şahin, K.H., Yusuf, S. (2011) The thermal conductivity of fir and beech wood heat treated at 170, 180, 190, 200, and 212°C. J. Appl. Polym. Sci. 121:2473–2480.10.1002/app.33885Search in Google Scholar
Salca, E., Hiziroglu, S. (2014) Evaluation of hardness and surface quality of different wood species as function of heat treatment. Mater. Des. 62:416–423.10.1016/j.matdes.2014.05.029Search in Google Scholar
Salman, S., Pétrissans, A., Thévenon, M.F., Dumarçay, S., Perrin, D., Pollier, B., Gérardin, P. (2014) Development of new wood treatments combining boron impregnation and thermo modification: effect of additives on boron leachability. Eur. J. Wood Prod. 72:355–365.10.1007/s00107-014-0787-7Search in Google Scholar
Salman, S., Pétrissans, A., Thévenon, M.F., Dumarçay, S., Gérardin, P. (2016) Decay and termite resistance of pine blocks impregnated with different additives and subjected to heat treatment. Eur J. Wood Prod.74:37–42.10.1007/s00107-015-0972-3Search in Google Scholar
Sun, W.L., Li, J. (2010). Analysis and characterization of dimensional stability and crystallinity of heat-treated Larix spp. Sci. Sil. Sin. 46:114–118.Search in Google Scholar
Sun, B.L., Wang, X.H., Liu, J.L. (2013) Changes in dimensional stability and mechanical properties of Eucalyptus pellita by melamine–urea–formaldehyde resin impregnation and heat treatment. Eur. J. Wood Prod. 71:557–562.10.1007/s00107-013-0700-9Search in Google Scholar
Taghiyari, H.R. (2011) Study on the effect of nano-silver impregnation on mechanical properties of heat-treated Populus nigra. Wood Sci. Technol. 45:399–404.10.1007/s00226-010-0343-5Search in Google Scholar
Taghiyari, H.R. (2013) Effects of heat-treatment on permeability of untreated and nano silver-impregnated native hardwoods. Maderas Cienc. Tecnol. 15:183–194.10.4067/S0718-221X2013005000015Search in Google Scholar
Taghiyari, H.R., Enayati, A., Gholamiyan, H. (2013) Effects of nano-silver impregnation on brittleness, physical and mechanical properties of heat-treated hardwoods. Wood Sci. Technol. 47:467–480.10.1007/s00226-012-0506-7Search in Google Scholar
Tjeerdsma, B.F., Boonstra, M., Pizzi, A., Tekely, P., Militz, H. (1998) Characterisation of thermally modified wood: molecular reasons for wood performance improvement. Holz Roh Werkst. 56:149–153.10.1007/s001070050287Search in Google Scholar
Todaro, L., Rita, A., Cetera, P., D Auria, M. (2015) Thermal treatment modifies the calorific value and ash content in some wood species. Fuel 140:1–3.10.1016/j.fuel.2014.09.060Search in Google Scholar
Tomak, E.D., Ustaomer, D., Yildiz, S., Pesman, E. (2014) Changes in surface and mechanical properties of heat treated wood during natural weathering. Measurement 53:30–39.10.1016/j.measurement.2014.03.018Search in Google Scholar
Weiland, J.J., Guyonnet, R. (2003) Study of chemical modifications and fungi degradation of thermally modified wood using DRIFT spectroscopy. Holz Roh Werkst. 61:216–220.10.1007/s00107-003-0364-ySearch in Google Scholar
Xie, Y.J., Fu, Q.L., Wang, Q.W., Xiao, Z.F., Militz, H. (2013) Effects of chemical modification on the mechanical properties of wood. Eur. J. Wood Prod. 71:401–416.10.1007/s00107-013-0693-4Search in Google Scholar
Xue, L., Zhao, Z.J., Zhang, Y., Chu, D.M., Mu, J. (2016) Analysis of gas ghromatography-mass spectrometry coupled with dynamic headspace sampling on volatile organic compounds of heat-treated poplar at high temperatures. Bioresources 1:3550–3560.10.15376/biores.11.2.3550-3560Search in Google Scholar
Yu, L.P., Li, G.P. (2006) Study on processing conditions of spruce with nitrogen-phosphorus-boron environmentally friendly fire retardant. China Wood Based Panels 13:14–16.Search in Google Scholar
Zhang, X.T., Mu, J., Chu, D.M., Zhao, Y. (2015) Synthesis of fire retardants based on N and P and poly(sodium silicate-aluminum dihydrogen phosphate) (PSADP) and testing the flame-retardant properties of PSADP impregnated poplar wood. Holzforschung 70:341–350.10.1515/hf-2014-0362Search in Google Scholar
©2017 Walter de Gruyter GmbH, Berlin/Boston