To investigate the dispersibility of dried cellulose nanofibers (CNFs), various additions (glycerol, octanol, glycol, and sodium perchlorate) were added to CNFs prior to drying. Glycerol was the only species to show any significant effect on re-dispersibility. The sedimentation was slower, and the transmittance of the solution was comparable to that of its undried counterpart. Increasing the amount of glycerol showed a clear trend with regard to dispersibility. The mechanical properties of films were maintained for samples that were dried and redispersed in the presence of glycerol.
Acknowledgments
We would like to thank Adrian Bacaj, Elizaveta Kim, Jean-Christian Zirignon, Matilda Helgesson, Wafa Qasim, Samuel Emilsson, Tim Mokvist and Tamara Patranika for their help with performing the screening study.
Conflict of interest: The authors declare no conflict of interest.
References
Butchosa, N., Zhou, Q. (2014) Water redispersible cellulose nanofibrils adsorbed with carboxymethyl cellulose. Cellulose 21(6):4349–4358.10.1007/s10570-014-0452-7Search in Google Scholar
Eyholzer, C., et al. (2009) Preparation and characterization of water-redispersible nanofibrillated cellulose in powder form. Cellulose 17(1):19–30.10.1007/s10570-009-9372-3Search in Google Scholar
Fernandes Diniz, J.M.B., Gil, M.H., Castro, J.A.A.M. (2004) Hornification—its origin and interpretation in wood pulps. Wood Sci. Technol. 37(6):489–494.10.1007/s00226-003-0216-2Search in Google Scholar
Hietala, M., Sain, S., Oksman, K. (2017) Highly redispersible sugar beet nanofibers as reinforcement in bionanocomposites. Cellulose 24(5):2177–2189.10.1007/s10570-017-1245-6Search in Google Scholar
Jayme, G. (1943) Über die Reaktionsfähigkeit von Zellstoffen. Cellulosechemie 21:73–86.Search in Google Scholar
Laine, J., et al. (2003) Studies on topochemical modification of cellulosic fibres Part 4. Toposelectivity of carboxymethylation and its effects on the swelling of fibres. Nord. Pulp Pap. Res. J. 18(3):316–324.10.3183/npprj-2003-18-03-p316-324Search in Google Scholar
Missoum, K., Bras, J., Belgacem, M.N. (2012) Water redispersible dried nanofibrillated cellulose by adding sodium chloride. Biomacromolecules 13(12):4118–4125.10.1021/bm301378nSearch in Google Scholar PubMed
Moser, C., Henriksson, G., Lindström, M.E. (2016) Specific Surface Area Increase during Cellulose Nanofiber Manufacturing Related to Energy Input. BioResources 11(3):7124–7132.10.15376/biores.11.3.7124-7132Search in Google Scholar
Peng, Y., Gardner, D.J., Han, Y. (2011) Drying cellulose nanofibrils: in search of a suitable method. Cellulose 19(1):91–102.10.1007/s10570-011-9630-zSearch in Google Scholar
Quispe, C.A.G., Coronado, C.J.R., Carvalho Jr, J.A. (2013) Glycerol: Production, consumption, prices, characterization and new trends in combustion. Renew. Sustain. Energy Rev. 27:475–493.10.1016/j.rser.2013.06.017Search in Google Scholar
Takaichi, S., Saito, T., Tanaka, R., Isogai, A. (2014) Improvement of nanodispersibility of oven-dried TEMPO-oxidized celluloses in water. Cellulose 21:4093–4103.10.1007/s10570-014-0444-7Search in Google Scholar
Zimmermann, M.V.G., et al. (2016) Drying techniques applied to cellulose nanofibers. J. Reinf. Plast. Compos. 35(8):628–643.10.1177/0731684415626286Search in Google Scholar
© 2018 Walter de Gruyter GmbH, Berlin/Boston