Abstract
A novel and easy route for preparing submicrometer particles of zinc oxide, involving hydrolysis of zinc salt in a polyol medium, is proposed. Zinc acetate dihydrate and diethyleneglycol appear to be the best candidates for obtaining a high yield of particles with well-defined morphological characteristics. Monodisperse spherical particles in the submicrometer range (0.2−0.4 μm) have been obtained for a salt concentration less than 0.1 mol 1−1. The particle size depends mainly on the heating rate. The particles are microporous (surface area: 80 m2 g−1) and are formed by aggregation of small crystallites (10 nm). Calcination at moderate temperature drastically reduces this porosity without significant interparticle sintering. At higher concentration, no aggregation occurs and tiny single crystallite particles are obtained.
Similar content being viewed by others
References
T. Q. Liu, O. Sakurai, N. Mizutani, and M. Kato, J. Mater. Sci. 21, 3698 (1986).
S. M. Haile, D. W. Johnson, Jr., G. H. Wiseman, and H. K. Bowen, J. Am. Ceram. Soc. 72, 2004 (1989).
M. Andrés Vergés and M. Martinez-Gallego, J. Mater. Sci. 27, 3756 (1992).
D. W. Sproson, G. L. Messing, and T. J. Gardner, Ceram. Int. 12, 3 (1986).
R. H. Heistand II and Y. H. Chia, in Better Ceramics Through Chemistry II, edited by C. J. Brinker, D. E. Clark, and D. R. Ulrich (Mater. Res. Soc. Symp. Proc. 73, Pittsburgh, PA, 1986), p. 93.
M. Andrés Vergés, A. Mifsud, and C. J. Serna, J. Chem. Soc. Faraday Trans. 86, 959 (1990).
R. S. Sapieszko and E. Matijević, Corrosion 36, 522 (1980).
M. Castellano and E. Matijević, Chem. Mater. 1, 78 (1989).
K. Kamata, H. Hosono, Y. Maeda, and K. Miyokawa, Chem. Lett., 2021 (1984).
F. Fiévet, J. P. Lagier, and M. Figlarz, MRS Bull. XIV, 29 (1989).
F. Fiévet, J. P. Lagier, B. Blin, B. Beaudoin, and M. Figlarz, Solid State Ionics 32/33, 198 (1989).
M. Figlarz, C. Ducamp-Sanguesa, F. Fiévet, and J. P. Lagier, in Advances in Powder Metallurgy and Particulate Materials, edited by Metal Powder Industries Federation, Princeton, NJ (P. M. World Congress Proceedings, San Francisco, CA, 1992), Vol. 1, pp. 179–192.
H. Kominami, M. Inoue, and T. Inui, Catal. Today 16, 309 (1993).
E. Matijević and S. Cimas, Colloid Polym. Sci. 265, 155 (1987).
X. Li, B. K. Xu, Z. C. Wang, F. Chi, and M. Y. Zhao, J. Mater. Sci. Lett. 11, 1476 (1992).
I. R. Collins and S. E. Taylor, J. Mater. Chem. 2, 1277 (1992).
E. Warren, X-Ray Diffraction (Addison-Wesley, Reading, MA, 1969), p. 264.
E. Matijević, Prog. Colloid Polym. Sci. 61, 24 (1976).
E. Matijević, Annu. Rev. Mater. Sci. 15, 483 (1985).
E. Matijević, Langmuir 2, 12 (1986).
E. Matijević, Chem. Mater. 5, 412 (1993).
J. Livage, C. Sanchez, M. Henry, and S. Doeuff, Solid State Ionics 32/33, 633 (1989).
E. Matijević, J. Colloid Interface Sci. 58, 374 (1977).
E. Matijević, Pure Appl. Chem. 50, 1193 (1978).
T. Sugimoto, Adv. Colloid Interface Sci. 28, 65 (1987).
H. K. Bowen, Meter. Sci. Eng. 44, 1 (1980).
M. Ocaña and E. Matijević, J. Mater. Res. 5, 1083 (1990).
W. P. Hsu, L. Rönnquist, and E. Matijević, Langmuir 4, 31 (1988).
T. C. Pluym, S. W. Lyons, Q. H. Powell, A. S. Gurav, T. T. Kodas, L. M. Wang, and H. D. Glicksman, Mater. Res. Bull. XXVIII, 369 (1993).
L. H. Edelson and A. M. Glaeser, J. Am. Ceram. Soc. 71, 225 (1988).
C. J. Brinker and G. W. Scherer, Sol-gel Science (Academic Press, New York, 1990), pp. 275–284.
J. Livage, J. Solid State Chem. 64, 322 (1986).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jézéquel, D., Guenot, J., Jouini, N. et al. Submicrometer zinc oxide particles: Elaboration in polyol medium and morphological characteristics. Journal of Materials Research 10, 77–83 (1995). https://doi.org/10.1557/JMR.1995.0077
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1995.0077