Nucleation of a new phase from the interaction of two adjacent phases: Some silicides

  • Commentaries and Reviews
  • Published:
Journal of Materials Research Aims and scope Submit manuscript

Abstract

The reactions of metal layers with their silicon substrates resulting in the formation of various silicides are considered generally not only as phenomena common to all diffusion couples where new phases are formed, but also as typical of all transitions from two to three phases. The conditions under which such transitions will display the same characteristics as encountered in the usual one-to-two phase transitions (condensation, crystallization, boiling) are analyzed by comparison to the classical theory of nucleation. Because of the lack of knowledge about the exact values of the relevant parameters, the discussion is carried out mostly in descriptive thermodynamic terms. Although nucleation effects are analyzed in general terms, the main focus of attention is a class of reactions where nucleation dominates the formation of a new phase; a salient feature of these reactions is the absence of any equilibrium temperature, although the nucleation temperatures are relatively well defined within narrow limits. Nucleation effects are correlated to such material characteristics as the stability of the nucleated phases, and to such kinetic characteristics as the sequence of phase formation. The modification of the energy levels of the different phases brought about by stress, ion bombardment, or the replacement of usual phases by metastable ones, are considered with respect to their effect on nucleation processes. The nearly total absence of literature references to nucleation in metal-metal diffusion couples is discussed with respect to some specific aspects of the metal-silicon reactions.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. W. J. Dunning, in Nucleation, edited by A. C. Zettlemoyer (Marcel Dekker, New York, 1969), p. 3.

    Google Scholar 

  2. C. A. Neugebauer, in Handbook of Thin Films Technology, edited by L. Maissel and R. Glang (McGraw-Hill, New York, 1970), Chap. 8.

    Google Scholar 

  3. K. L. Chopra, Thin Film Phenomena (McGraw-Hill, New York, 1969), p. 137.

    Google Scholar 

  4. R. E. Smallman, Modern Physical Metallurgy (Butterworth, London, 1963).

    Google Scholar 

  5. P. Haasen, Physical Metallurgy (Cambridge U. P., Cambridge, 1978).

    Google Scholar 

  6. R. D. Doherty, in Physical Metallurgy, edited by R. W. Cahn and P. Haasen (North-Holland, Amsterdam, 1983), p. 933.

    Google Scholar 

  7. H. I. Aaronson and K. C. Russel, in Solid-Solid Phase Transformations, edited by H. I. Aaronson, D. E. Laughlin, R. F. Sekerka, and C. M. Wayman (The Metallurgical Society of AIME, Warrendale, PA, 1982), p. 371.

    Google Scholar 

  8. K. C. Russell, Colloid Interface Sci. 13, 205 (1980).

    Article  CAS  Google Scholar 

  9. J. W. Cahn and J. E. Hilliard, J. Chem. Phys. 31, 688 (1959).

    Article  CAS  Google Scholar 

  10. M. Hillert, Acta Metall. 9, 525 (1961).

    Article  CAS  Google Scholar 

  11. F. K. LeGoues, H. I. Aaronson, Y. W. Lee, and G. J. Fix, in Solid-Solid Phase Transformations, edited by H. I. Aaronson, D. E. Laughlin, R. F. Sekerka, and C. M. Wayman (The Metallurgical Society of AIME, Warrendale, PA, 1982), p. 427.

    Google Scholar 

  12. F. K. LeGoues, Y. W. Lee, and H. I. Aaronson, Acta Metall. 32, 1837 (1984).

    Article  Google Scholar 

  13. F. K. LeGoues, H. I. Aaronson, and Y. W. Lee, Acta Metall. 32, 1845 (1984).

    Article  Google Scholar 

  14. F. K. LeGoues and H. I. Aaronson, Acta Metall. 32, 1855 (1984).

    Article  Google Scholar 

  15. F. K. LeGoues, R. N. Wright, Y. W. Lee, and H. I. Aaronson, Acta Metall. 32, 1865 (1984).

    Article  Google Scholar 

  16. Y. Adda and J. Philibert, La Diffusion dans les Solides (Presses Universitaires de France, Paris, 1966), Vol. 1, p. 616.

    Google Scholar 

  17. G. A. Roberts and R. F. Mehl, Trans. AIME 154, 318 (1943).

    Google Scholar 

  18. G. A. Roberts and R. F. Mehl, Trans. ASM 31, 613 (1943).

    Google Scholar 

  19. G. Molinder, Acta Metall. 4, 565 (1956).

    Article  CAS  Google Scholar 

  20. J. W. Christian, The Theory of Transformations in Metals and Alloys (Pergamon, Oxford, 1965), p. 691.

    Google Scholar 

  21. P. Steinmetz, B. Dupré, and B. Roques, J. Less Common Metals 53, 43 (1977).

    Article  CAS  Google Scholar 

  22. Y. Muramatsu, F. Roux, and A. Vignes, Trans. Jpn. Inst. Met. 16, 61 (1975).

    Article  CAS  Google Scholar 

  23. M.-A. Nicolet and S. S. Lau, in VLSI Electronics Microstructure Science, edited by N. G. Einspruch and G. B. Larrabee (Academic, New York, 1983), Vol. 6, p. 330.

    Google Scholar 

  24. F. M. d’Heurle and P. Gas, J. Mater. Res. 1, 205 (1986).

    Article  Google Scholar 

  25. G. Hutchins and A. Shepela, Thin Solid Films 18, 343 (1973).

    Article  CAS  Google Scholar 

  26. J. Ziegler, J. Mayer, C. Kircher, and K. N. Tu, J. Appl. Phys. 44, 3851 (1973).

    Article  CAS  Google Scholar 

  27. C. S. Petersson, J. E. Baglin, W. Hammer, F. M. d’Heurle, T. S. Kuan, I. Odhomari, J. de Sousa Pires, and P. Tove, J. Appl. Phys. 50, 3357 (1979).

    Article  CAS  Google Scholar 

  28. C. S. Petersson, R. Anderson, J. E. Baglin, J. Dempsey, W. Hammer, F. M. d’Heurle, and S. J. La Placa, J. Appl. Phys. 51, 373 (1980).

    Article  CAS  Google Scholar 

  29. R. Anderson, J. E. Baglin, J. Dempsey, W. Hammer, F. M. d’Heurle, and C. S. Petersson, Appl. Phys. Lett. 35, 285 (1979).

    Article  CAS  Google Scholar 

  30. J. E. Baglin, F. M. d’Heurle, and C. S. Petersson, in Thin Film Interfaces and Interactions, edited by J. E. Baglin and J. Poate (The Electrochemical Society, Princeton, NJ, 1980), p. 341.

    Google Scholar 

  31. J. E. Baglin, F. M. d’Heurle, and C. S. Petersson, Appl. Phys. Lett. 36, 594(1980).

    Article  CAS  Google Scholar 

  32. R. D. Thompson, B. Y. Tsaur, and K. N. Tu, Appl. Phys. Lett. 38, 535 (1981).

    Article  CAS  Google Scholar 

  33. C. S. Petersson, J. E. Baglin, J. Dempsey, F. M. d’Heurle, and S. La Placa, J. Appl. Phys. 53, 4866 (1982).

    Article  CAS  Google Scholar 

  34. M. Eizenberg and K. N. Tu, J. Appl. Phys. 53, 6886 (1982).

    Google Scholar 

  35. C. S. Petersson and F. M. d’Heurle (unpublished).

  36. F. M. d’Heurle, IBM Research Report No. RC 10422, Yorktown Heights, New York 10598, 1983.

    Google Scholar 

  37. F. M. d’Heurle and C. S. Petersson, Thin Solid Films 128, 283 (1985).

    Article  Google Scholar 

  38. F. M. d’Heurle, D. D. Anfiteatro, V. R. Deline, and T. G. Finstad, Thin Solid Films 128, 107 (1985).

    Article  Google Scholar 

  39. T. G. Finstad, D. D. Anfiteatro, V. R. Deline, F. M. d’Heurle, P. Gas, V. L. Moruzzi, K. Schwarz, and J. Tersoff, Thin Solid Films 135, 229(1986).

    Article  CAS  Google Scholar 

  40. G. Majni, M. Costato, F. Panini, and G. Celotti, J. Phys. Chem. Solids 46, 631 (1985).

    Article  CAS  Google Scholar 

  41. P. Gas, F. M. d’Heurle, F. K. LeGoues, and S. J. LaPlaca, J. Appl. Phys. 59, 3458(1986).

    Article  CAS  Google Scholar 

  42. B. Y. Tsaur and M. A. Nicolet, Appl. Phys. Lett. 35, 225 (1979).

    Article  CAS  Google Scholar 

  43. B. Y. Tsaur and L. S. Hung, Appl. Phys. Lett. 37, 922 (1980).

    Article  CAS  Google Scholar 

  44. C.-D. Lien, M.-A. Nicolet, and S. S. Lau, Appl. Phys. A 34, 249 (1984).

    Article  CAS  Google Scholar 

  45. C.-D. Lien, M.-A. Nicolet, and S. S. Lau, Phys. Status Solidi A 8, 123 (1984).

    Article  Google Scholar 

  46. C. S. Wu, D. M. Scott, S. S. Lau, A. Wakita, T. W. Sigmon, J. A. Knapp, and J. T. Picraux, Mater. Res. Soc. Symp. Proc. 25, 93 (1984).

    Article  CAS  Google Scholar 

  47. M. Tabasky, E. S. Bulat, B. M. Ditchek, M. A. Sullivan, and S. Shatas, Mater. Res. Soc. Symp. Proc. 52, 271 (1986).

    Article  CAS  Google Scholar 

  48. F. M. d’Heurle, R. T. Hodgson, and C. Y. Ting, Mater. Res. Soc. Symp. Proc. 52, 261 (1986).

    Article  Google Scholar 

  49. I. Engström (private communication). This compound has been previously referred to as IrSi1.75, IrSi,1.5, or Ir2Si3. Now that a structure corresponding to Ir3Si5 has been indentified, this latter formulation should be preferred.

  50. H. Föil, P. S. Ho, and K. N. Tu, Philos. Mag. A 45, 31 (1982).

    Article  Google Scholar 

  51. J. M. Gibson, R. T. Tung, J. M. Philips, and J. M. Poate, Mater. Res. Soc. Symp. Proc. 25, 405 (1984).

    Article  CAS  Google Scholar 

  52. M. Liehr, P. E. Schmid, F. K. LeGoues, and P. S. Ho, J. Vac. Sci. Technol. A4, 855 (1986).

    Article  Google Scholar 

  53. C. d’Anterroches, Thin Solid Films 168, 751 (1986).

    Google Scholar 

  54. A. Nylund, Acta Chem. Scand. 20, 2381 (1966).

    Article  CAS  Google Scholar 

  55. B. Y. Tsaur and M.-A. Nicolet, Appl. Phys. Lett. 37, 708 (1980).

    Article  CAS  Google Scholar 

  56. A. Searcy and L. Finnie, J. Amer. Ceram. Soc. 45, 268 (1962).

    Article  CAS  Google Scholar 

  57. T. G. Chart, High Temp.-High Pressures 5, 241 (1973).

    CAS  Google Scholar 

  58. R. Pretorius, J. Harris, and M.-A. Nicolet, Solid State Electron. 21, 667 (1978).

    Article  CAS  Google Scholar 

  59. J. Barin and O. Knacke, Thermodynamic Properties of Inorganic Substances (Springer, Berlin, 1973).

    Google Scholar 

  60. J. Barin, O. Knacke, and O. Kubaschewski, Thermodynamic Properties of Inorganic Substances, Supplement (Springer, Berlin, 1977).

    Book  Google Scholar 

  61. O. Kubaschewski and C. B. Alcock, Metallurgical Thermochemistry (Pergamon, Oxford, 1983).

    Google Scholar 

  62. J. Burke, The Kinetics of Phase Transformations in Metals (Pergamon, Oxford, 1965), p. 113.

    Google Scholar 

  63. J. O. Olowolafe, M.-A. Nicolet, and J. W. Mayer, Thin Solid Films 38, 143 (1976).

    Article  CAS  Google Scholar 

  64. K. Schubert, Kristallstrukturen zweicomponentiger Phasen (Springer, Berlin, 1964), p. 323.

    Book  Google Scholar 

  65. R. Swalin, Thermody6namics of Metals (Wiley, New York, 1972), p. 24.

    Google Scholar 

  66. N. Eustathopoulos and S. C. Joud, in Current Topics in Materials Science, edited by E. Kaldis (North-Hplland, Amsterdam, 1980), Vol. 4, p. 281.

    Google Scholar 

  67. F. M. d’Heurle, C. S. Petersson, J. E. Baglin, S. J. LaPlaca, and C. Y. Wong, in J. Appl. Phys. 55, 4208 (1984).

    Article  Google Scholar 

  68. G. Majni, F. Delia Valle, and C. Nobili, J. Phys. D 17, L77 (1984).

    Google Scholar 

  69. W. B. Pearson, The Crystal Chemistry and Physics of Metals and Alloys (Wiley–Interscience, New York, 1972).

    Google Scholar 

  70. M. Hansen, Constitution of Binary Alloys (McGraw-Hill, New York, 1958), p. 1040.

    Google Scholar 

  71. K. N. Tu, E. Alessandrini, W. K. Chu, M. Kraütle, and J. Mayer, Jpn. J. Appl. Phys. Suppl. 2, Pt. 1, 669 (1974).

    Article  Google Scholar 

  72. R. T. Tung, J. M. Gibson, and J. Poate, Phys. Rev. Lett. 50, 429 (1983).

    Article  CAS  Google Scholar 

  73. Standard Diffraction Powder Pattern #17-881.

  74. K. N. Tu, G. Ottaviani, V. Gösele, and H. Foil, J. Appl. Phys. 54, 758 (1983).

    Article  CAS  Google Scholar 

  75. L. R. Zheng, L. S. Hung and J. W. Mayer, J. Vac. Sci. Technol. A 1, 758 (1983).

    Article  Google Scholar 

  76. J. W. Gibbs, in The Scientific Papers of J. Willard Gibbs (Dover, New York, 1961), Vol. 1, p. 55.

    Google Scholar 

  77. G. W. Lorimer, in Solid-State Phase Transformations, edited by H. I. Aaronson, D. E. Laughlin, R. F. Sekerka, and C. M. Wayman (The Metallurgical Society of AIME, Warrendale, PA, 1982), p. 613.

    Google Scholar 

  78. V. K. Semenchenko, Surface Phenomena in Metals and Alloys (Pergamon, New York, 1961), p. 35.

    Google Scholar 

  79. R. Defay and I. Prigogine, Tension superficielle et adsorption (Desoer, Liege, Belgium, 1951), p. 9.

    Google Scholar 

  80. L. S. Darken and R. W. Gurry, Physical Chemistry of Metals (McGraw-Hill, New York, 1953), p. 349.

    Google Scholar 

  81. R. W. Swalin, Thermodynamics of Solids (Wiley, New York, 1972), p. 116.

    Google Scholar 

  82. M. Hansen, Constitution of Binary Alloys (McGraw-Hill, New York, 1958), p. 1126.

    Google Scholar 

  83. H. Langer and E. Watchel, Z. Metallk. 72, 769 (1981).

    CAS  Google Scholar 

  84. W. G. Mofatt, The Handbook of Binary Phase Diagrams (General Electric, Schenectady, New York).

  85. S. Saitoh, H. Ishiwara, T. Asano, and S. Furukawa, Jpn. J. Appl. Phys. 20, 1649(1981).

    Article  CAS  Google Scholar 

  86. A. Zur, T. C. McGill, and M.-A. Nicolet, J. Appl. Phys. 57, 600 (1985).

    Article  CAS  Google Scholar 

  87. E. C. Cahoon, C. M. Comrie, and R. Pretorius, Mater. Res. Soc. Symp. Proc. 25, 57(1984).

    Article  CAS  Google Scholar 

  88. M. Hansen, Constitution of Binary Alloys (McGraw-Hill, New York, 1958), p. 1206.

    Google Scholar 

  89. R. P. Elliott, Constitution of Binary Alloys (McGraw-Hill, New York, 1965), p. 522.

    Google Scholar 

  90. J. D. Eshelby, Proc. R. Soc. A London Ser. A 241, 376 (1957).

    Article  Google Scholar 

  91. Handbook of Materials and Processes for Electronics, edited by A. Harper (McGraw-Hill, New York, 1970), p. 7–31.

    Google Scholar 

  92. Handbook of Chemistry and Physics, edited by C. D. Hodgman, R. C. Weast, and S. M. Selby (Chemical Rubber, Cleveland, 1955), p. 1985.

    Google Scholar 

  93. Engineering Properties of Selected Ceramic Materials, edited by J. F. Lynch, C. G. Ruderer, and W. H. Duckworth (The American Ceramic Society, Columbus, OH, 1966), pp. 5.7.3-2 to 5.7.3–11.

    Google Scholar 

  94. J. Angelillo, F. M. d’Heurle, C. S. Petersson, and A. Segmüller, J. Vac. Sci. Technol. 17, 471 (1980).

    Article  Google Scholar 

  95. C. Zwikker, Physical Properties of Solid Materials (Pergamon, London, 1955), p. 90.

    Google Scholar 

  96. J. A. Knapp and S. T. Picraux, Mater. Res. Soc. Symp. Proc. 54, 261 (1986).

    Article  CAS  Google Scholar 

  97. V. M. Koleshko, V. F. Belitsky, and A. A. Khodin, Thin Solid Films 141, 277(1987).

    Article  Google Scholar 

  98. G. V. Samsonov, High Temperature Compounds of the Rare-Earth Metals with Nonmetals (Consultant Bureau, New York, 1965).

    Google Scholar 

  99. R. P. Elliott, Constitution of Binary Alloys (McGraw-Hill, New York, 1965), p. 823.

    Google Scholar 

  100. J. Angilello, J. E. Baglin, F. M. d’Heurle, C. S. Petersson, and A. Segmüller, in Thin Film Interfaces and Interactions, edited by J. E. Baglin and J. Poate (The Electrochemical Society, Princeton, NJ, 1980), p. 369.

    Google Scholar 

  101. J. E. Baglin, F. M. d’Heurle, and C. S. Petersson, J. Appl. Phys. 52, 2841 (1981).

    Article  CAS  Google Scholar 

  102. S. S. Lau, C. S. Pai, and C. S. Wu, Appl. Phys. Lett. 41, 77 (1982).

    Article  CAS  Google Scholar 

  103. A. Iandelli, A. Palenzona, and G. L. Olcese, J. Less-Common Metals 64, 213 (1979).

    Article  CAS  Google Scholar 

  104. J. C. Fan and C. H. Anderson, J. Appl. Phys. 52, 4003 (1981).

    Article  CAS  Google Scholar 

  105. I. Engström, Structural Chemistry of Platinum Metal Suicides (Acta Universitatis Upsaliensis, Uppsala, 1970).

    Google Scholar 

  106. A. Applebaum, R. V. Knoell, and S. P. Murarka, J. Appl. Phys. 57, 1322(1985).

    Article  Google Scholar 

  107. J. W. Westwater, Am. Sci. 47, 427 (1959).

    CAS  Google Scholar 

  108. J. M. Coulson and J. F. Richardson, Chemical Engineering (Pergamon, New York, 1964), Vol. 1, p. 242.

    Google Scholar 

  109. H. Cremer and S. B. Watkins, Chemical Engineering Practice, Vol. 7, Heat Transfer (Butterworths, London, 1963).

    Google Scholar 

  110. J. Bardolle, in Interfaces et Surfaces en Metallurgie, edited by G. Martin, J. Levy, J. Oudar, G. Saada, and G. Saintfort (Trans Tech Publications, Aedermannsdorf, Switzerland, 1975), p. 476.

    Google Scholar 

  111. K. R. Lawless, Rep. Prog. Phys. 37, 231 (1974).

    Article  CAS  Google Scholar 

  112. G. van Gurp and C. Langereis, J. Appl. Phys. 46, 4301 (1975).

    Article  Google Scholar 

  113. S. S. Lau, J. W. Mayer and K. N. Tu, J. Appl. Phys. 49, 4005 (1978).

    Article  CAS  Google Scholar 

  114. G. J. van Gurp, W. F. van der Weg, and D. Sigurd, J. Appl. Phys. 49, 4011 (1978).

    Article  Google Scholar 

  115. F. M. d’Heurle, C. S. Petersson, L. Stolt, and B. Stritzker, J. Appl. Phys. 53, 5678 (1982).

    Article  Google Scholar 

  116. A. Appelbaum, M. Einzenberg, and R. Brener, Vacuum 33, 227 (1983).

    Article  CAS  Google Scholar 

  117. P. Gas, F. K. LeGoues, J. Tardy, and F. M. d’Heurle, J. Appl. Phys. 61, 2203 (1987).

    Article  CAS  Google Scholar 

  118. L. S. Hung, J. Gyulai, J. Mayer, S. S. Lau, and M.-A. Nicolet, J. Appl. Phys. 54, 5076 (1983).

    Article  CAS  Google Scholar 

  119. P. Joubert, These, Université de Rennes, September 1984.

  120. P. Joubert, J. Appl. Phys. 60, 2823 (1986).

    Article  CAS  Google Scholar 

  121. F. P. Price, in Nucleation, edited by A. C. Zettlemoyer (Marcel Dekker, New York, 1969), p. 406.

    Google Scholar 

  122. W. G. Moffat, G. W. Pearsaland J. Wulff, The Structure and Properties of Materials, Vol. I, Structure (Wiley, New York, 1964), p. 130, Fig. 6.7.

    Google Scholar 

  123. J. E. Breedon, J. F. Jackson, M. J. Marcinkowski, and M. E. Taylor, J. Mater. Sci. 8, 1701 (1973).

    Google Scholar 

  124. C. C. Coffin and S. Johnston, Proc. R. Soc. London Ser. A146, 564 (1934).

    Google Scholar 

  125. T. Takamori, R. Messier and R. Roy, J. Mater. Sci. 8, 1809 (1973).

    Article  CAS  Google Scholar 

  126. M. Kikuchi, A. Matsuda, T. Kurosu, A. Mineo, and J. K. Callahan, Solid State Commun. 14, 731 (1974).

    Article  CAS  Google Scholar 

  127. C. E. Wickersham, G. Bajor, and J. E. Greene, Solid State Commun. 27, 17 (1978).

    Article  CAS  Google Scholar 

  128. C. E. Wickersham, G. Bajor, and J. E. Greene, J. Vac. Sci. Technol. A 3, 336(1985).

    Article  Google Scholar 

  129. C. E. Wickersham and J. E. Poole, Mater. Lett. 4, 268 (1986).

    Article  CAS  Google Scholar 

  130. Wim van Saarloos and J. D. Weeks, Phys. Rev. Lett. 51, 1046 (1983).

    Article  Google Scholar 

  131. R. M. Bradley, J. Appl. Phys. 60, 3146 (1986).

    Article  CAS  Google Scholar 

  132. P. Gas, J. Tardy, F. K. LeGoues, and F. M. d’Heurle, Appl. Phys. Lett. 50, 1135(1987).

    Article  CAS  Google Scholar 

  133. O. Thomas, L. Krusin-Elbaum, T. Gallo, and F. M. d’Heurle (unpublished).

Download references

Author information

Authors and Affiliations

  1. IBM Research Center, P. O. Box. 218, Yorktown Heights, New York, 10598, USA

    F. M. d’Heurle

  2. Institutet for Mikrovågsteknik, Kungliga Tekniska Högskolan, Stockholm, S-70044, Sweden

    F. M. d’Heurle

Authors
  1. F. M. d’Heurle
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

d’Heurle, F.M. Nucleation of a new phase from the interaction of two adjacent phases: Some silicides. Journal of Materials Research 3, 167–195 (1988). https://doi.org/10.1557/JMR.1988.0167

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1557/JMR.1988.0167

Search

Navigation