Abstract
Processing atmosphere and precursor effects on liquid phase formation were investigated in the BaO–CuO thin film system. Liquid phase was observed at a significantly lower temperature (∼620 °C) under N2 atmosphere with carboxylate solution precursors. In the processing of the YBCO oxide superconductors, formation of the liquid phase facilitated the decomposition of BaCO3 and crystallization of the YBCO grains. Larger grains and greater (00l) preferred orientation were also observed in the YBCO films prepared with the presence of the liquid phase.
Similar content being viewed by others
References
J. Mannhart, J. Supercond. 3 (3), 281 (1990).
M. Murakami and N. Koyama, in High Temperature Superconductors: Relationships between Properties, Structure, and Solid-State Chemistry, edited by J. R. Jorgensen, K. Kitazawa, J. M. Tarascon, M. S. Thompson, and J. B. Torrance (Mater. Res. Soc. Symp. Proc. 156, Pittsburgh, PA, 1989), p. 201.
S. Jin, T. H. Tiefel, R. C. Sherwood, M. E. Davis, R. B. van Dover, G. W. Kammlott, R. A. Fastnacht, and H. D. Keith, Appl. Phys. Lett. 52 (24), 2074 (1988).
P. Sarkar, T. B. Troczynski, K. J. Vaidya, and P. S. Nicholson, in Ceramic Superconductors II, edited by M. F. Yan (The American Ceramics Society, Westerville, OH, 1988), p. 204.
R. S. Roth, K. L. Davis, and J. R. Dennis, Adv. Ceram. Mater. 2 (3B), 303 (1987).
R. S. Roth, C. J. Rawn, F. Beech, and J. D. Anderson, in Ceramic Superconductors II, edited by M. F. Yan (The American Ceramic Society, Westerville, OH, 1988), p. 13.
T. Aselage and K. Keefer, J. Mater. Res. 3, 1279 (1988).
P. K. Gallagher, Adv. Ceram. Mater. 2 (3B), 632 (1987).
J. Karpinski, C. Belli, E. Kaldis, A. Wisard, and E. Jilek, Physica C 153–1551, 830 (1988).
K. W. Lay and G. M. Renlund, J. Am. Ceram. Soc. 73 (5), 1208 (1990).
B. T. Ahn, V. Y. Lee, R. Beyers, T. M. Gur, and R. A. Huggins, in Ceramic Transactions, Superconductivity and Ceramic Superconductors, edited by K. M. Nair and E. A. Giess (The American Ceramics Society, Inc., Westerville, OH, 1990), Vol. 13.
K. Borowiec and K. Kolbrecka, Jpn. J. Appl. Phys. 28 (11), L1963 (1989).
J. E. Ullman, R. W. McCallum, and J. D. Verhoeven, J. Mater. Res. 4, 752 (1989).
J. J. Rha, K. J. Yoon, S. L. Kang, and D. N. Yoon, J. Am. Ceram. Soc. 71 (7), C328 (1988).
P-Y. Chu, I. C. Campion, and R. C. Buchanan, J. Mater. Res. 8, 261 (1993).
P-Y. Chu and R. C. Buchanan, J. Mater. Res. 6, 1736 (1991).
M. Nevriva, E. Poliert, L. Matejkova, and A. Triska, J. Cryst. Growth 91, 434 (1988).
See, for example, Ulmann’s Encyclopedia of Industrial Chemistry, 5th ed., Vol. A3, p. 334, and J. B. Pierce, Jr., U. S. Patent 1305 618.
S. Nakahara, G. J. Fisanick, M. F. Yan, R. B. van Dover, and T. Boone, J. Cryst. Growth 85, 639 (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chu, PY., Buchanan, R.C. Reactive liquid phase sintering of solution-derived YBa2Cu3O7−x superconducting thin films: Part I. Ambient and precursor effects on BaO–CuO liquid phase formation. Journal of Materials Research 8, 2134–2142 (1993). https://doi.org/10.1557/JMR.1993.2134
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1993.2134