Abstract
Fine KSbOSiO4 (KSS) powders have been prepared by a sol-gel method starting from the system of TEOS, KSb(OH)6, H2O, C2H5OH, or mechanochemical mixing method with a stoichiometric mixture of amorphous silica and KSb(OH)6. The KSS crystallized sluggishly into a tetragonal symmetry in low temperature and transformed into an orthorhombic one in higher temperature, indicating the amorphous-like powder patterns in the intermediate step. This amorphization process could be related to some redistribution of the polysilicate network structures. The mechanochemical activation energy stored in the powder surface, as well as the coexisting matrix (KSbO3), retards the transformation. It was concluded that the KSS powders composed of high molecular weight siloxane polymers, which were formed by hydrolysis in the presence of a small amount of NH3 aqueous solution, showed higher sinterability. The sintering, where the calcining process was omitted, enabled the dense tetragonal-type ceramics stabilized at lower temperature, rather than higher temperature, to fabricate.
Similar content being viewed by others
References
I. Tordjman, R. Masse, and J. C. Guitel, Z. Kristallogr. 139, 103–108 (1974).
F. C. Zumsteg, J. D. Bierlein, and T. E. Gier, J. Appl. Phys. 47, 4980–4985 (1976).
M-P. Crosnier, D. Guyomard, A. Verbaere, and Y. Piffard, Eur. J. Solid State Inorg. Chem. 27, 845–854 (1990).
C. Pagnoux, A. Verbaere, Y. Kanno, Y. Piffard, and M. Tournoux, J. Solid State Chem. 99, 173–181 (1992).
J. Ravez, A. Simon, B. Boulonger, M. P. Crosnier, and Y. Piffard, Ferroelectrics 124, 379–384 (1991).
Y. Kanno, C. Pagnoux, Y. Piffard, and M. Tournoux, J. Mater. Res. 6, 2499–2500 (1991).
Y. Kanno, C. Pagnoux, Y. Piffard, and M. Tournoux, Mater. Res. Bull. XXVI, 1339–1345 (1991).
Y. Kanno and T. Suzuki, Hyomen Kagaku 9, 207–212 (1988).
Y. Kanno J. Mater. Sci. 24, 2415–2420 (1989).
J. Sanchez and A. McCormick, Chem. Mater. 3, 320–324 (1991).
B.E. Yoldas, J. Non-Cryst. Solids 51, 105–121 (1982).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kanno, Y. Tetragonal-orthorhombic phase transformation and sintering behavior of KSbOSiO4 (isomorphous derivative of KTP). Journal of Materials Research 9, 2323–2329 (1994). https://doi.org/10.1557/JMR.1994.2323
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1994.2323