Abstract
Systematic microstructural and mechanical investigations of the Fe84.3Cr4.3Mo4.6V2.2C4.6 alloy cast under special manufacturing conditions in the as-cast state and after specific heat treatment are presented to point out that the special manufacturing of the alloy led to high compression strength (up to 4680 MPa) combined with large fracture strain (about 20%) already in the as-cast state. One select chemical composition of the alloy, which was mentioned previously [Kuuuhn et al., Appl. Phys. Lett.90, 261901 (2007)] enhanced mechanical properties already in the as-cast state. Furthermore, that composition is comparable to commercial high-speed steel. By the special manufacturing used, a high purity of elements and a high cooling rate, which led to a microstructure similar to a composite-like material, composed of dendritic area (martensite, bainite, and ferrite) and interdendritic area (e.g., complex carbides). The presented article demonstrates an alloy that exhibits already in the as-cast state high fracture strength and large ductility. Furthermore, these outstanding mechanical properties remain unchanged after heating up to 873 K.
Similar content being viewed by others
References
U. Kuuuhn, N. Mattern, T. Gemming, U. Siegel, K. Werniewicz, J. Eckert Superior mechanical properties of FeCrMoVC. Appl. Phys. Lett. 90, 261901 (2007)
R.J. Parker, E.V. Zaretsky, D.M.W. Dietrich Rolling-Element Fatigue Lives of Four M-Series Steel and AISI 52100 at 150 °F (National Aeronautics and Space Administration, Cleveland, OH 1971)
L.P. Trusov, S.S. D’yachenko, V.P. Tarabanova, L.D. Mishchenko Grain size and heat resistance of Cr–Mo–V steel. Termicheskaya Obrabotka Metallov 11, 29 (1974)
E.C. Hwang, S. Lee, H.C. Lee Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls. Part II: Fracture behavior. Mater. Sci. Eng., A 254, 296 (1998)
S. Karagöz, H.O. Andrén Secondary hardening in high speed steels. Z. Metallkd. 83, 6 (1992)
H. Weiland High Speed Steels (Verlag VDI-Verlag 1982)
W. Haufe High Speed Steel and Its Heat Treating (Carl Hanser Verlag, Muuunchen, Germany 1951)
G. Krauss, F.B. Pickering, H.W. Rayson Constitution and properties of steels Materials Science and Technology edited by R.W. Cahn, P. Haasen, and E.J. Kramer Vol. 7 (Wiley-VCH Verlag, Weinheim, Germany 2005) 3–736
H.F. Fischmeister, S. Karagoz, H.O. Andrén An atom probe study of secondary hardening in high speed steels. Acta Metall. 36, (4) 817 (1988)
E.C. Hwang, S. Lee, H.C. Lee Effects of alloying elements on microstructure and fracture properties of cast high speed steel rolls. Part I: Microstructural analysis. Mater. Sci. Eng., A 254, 282 (1998)
G. Hackl, R. Ebner, F. Jeglisch Article about the development of high alloy high speed steels. Z. Metallkd. 83, 6 (1992)
W. Bleck Material Engineering for Academic Studies and Practical Experience (Verlag Mainz, Wissenschafts-Verlag, Aachen, Germany 2004)
H. Bhadeshia Bainite in Steels Vo. 2 (Verlag University Press, Cambridge 2001)
J. Bolton Modern developments in sintered high speed steels. Met. Powder Rep. 51, 17 (1996)
R.M. Srivastava, J. Eckert, W. Löser, B.K. Dhindaw, L. Schultz Cooling rate evaluation for bulk amorphous alloys from eutectic microstructures in casting processes. Mater. Trans., JIM 43, 1670 (2002)
M.M. Serna, L.C. Rossi MC complex carbide in AISI M2 high-speed steel. Mater. Lett. 63, 691 (2009)
K. Werniewicz, U. Kuuuhn, N. Mattern, B. Bartusch, J. Eckert, J. Das, L. Schultz, T. Kulik New Fe–Cr–Mo–Ga–C composites with high compressive strength and large plasticity. Acta Mater. 55, 3513 (2007)
Author information
Authors and Affiliations
Corresponding author
Additional information
This author was an editor of this journal during the review and decision stage. For the JMR policy on review and publication of manuscripts authored by editors, please refer to http://www.mrs.org/jmr_policy
Rights and permissions
About this article
Cite this article
Schlieter, A., Kuuuhn, U., Eckert, J. et al. Microstructure, thermal, and mechanical characterization of rapidly solidified high strength Fe84.3Cr4.3Mo4.6V2.2C4.6. Journal of Materials Research 25, 1164–1171 (2010). https://doi.org/10.1557/JMR.2010.0158
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2010.0158