Effect of titan yellow dye on morphological, structural, optical, and dielectric properties of zinc(tris) thiourea sulphate single crystals

  • Article
  • Published:
Journal of Materials Research Aims and scope Submit manuscript

Abstract

Zinc(tris) thiourea sulphate (ZTS) is as one of the potential candidates for nonlinear optical applications due to its high nonlinearity and excellent optical properties. The synthesis of pure and titan yellow dye doped ZTS has been done and good quality rod-like single crystals of size ∼60 mm long and 2 mm diameter were grown through simplest and low cost route. The structural and vibrational analysis rules out any extra phase or change in structure of ZTS due to dye doping. Scanning electron microscope study reveals that the grown crystals are of good quality with rod-like morphology. Diffuse reflectance spectrum show a new absorption band at ∼460 nm, which may be predicted as a signature of dye. The optical band gap was calculated to be 4.6 eV for pure and 4.5 eV for doped ZTS crystals. The violet-blue emission centered at 412 nm in pure and at 414 nm in doped crystals with an additional green emission bands at 528 nm with high intensity in the photoluminescence spectra were observed. The value of ε1 is found to be enhanced from 10 (in pure) to 14 (in doped) crystals. The properties are enhanced due to dye doping and may be more useful than pure crystals in optoelectronic devices.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

SCHEME 1
FIG. 1
FIG. 2
FIG. 3
FIG. 4
FIG. 5
FIG. 6
FIG. 7
FIG. 8

Similar content being viewed by others

References

  1. B. Saleh: MC Teich Fundamentals of Photonics (John Wiley & Sons: New York, 1991).

    Book  Google Scholar 

  2. B.G. Penn, B.H. Cardelino, C.E. Moore, A.W. Shields, and D. Frazier: Growth of bulk single crystals of organic materials for nonlinear optical devices: An overview. Prog. Cryst. Growth Charact. Mater. 22 (1), 19 (1991).

    Article  CAS  Google Scholar 

  3. M. Shakir, B. Singh, B. Kumar, and G. Bhagavannarayana: Ferroelectricity in glycine picrate: An astonishing observation in a centrosymmetric crystal. Appl. Phys. Lett. 95 (25), 252902 (2009).

    Article  CAS  Google Scholar 

  4. M. Shakir, S. Kushwaha, K. Maurya, and R. Bhatt: Unidirectional growth of l-proline cadmium chloride monohydrate single crystal and its characterization for structural, vibrational, LDT, optical and dielectric properties. Mater. Chem. Phys. 120, 566 (2010).

    Article  CAS  Google Scholar 

  5. M. Shkir, H. Abbas, S. Kumar, G. Bhagavannarayana, and S. AlFaify: Experimental and theoretical studies on bis (glycine) lithium nitrate (BGLiN): A physico-chemical approach. J. Phys. Chem. Solids 75 (8), 959 (2014).

    Article  CAS  Google Scholar 

  6. M. Shkir, S. AlFaify, H. Abbas, and G. Bhagavannarayana: A physico-chemical approach to study the experimental and theoretical properties of l-ornithine monohydrochloride: An organic nonlinear optical material. Mater. Chem. Phys. 155, 36–46 (2015).

    Article  CAS  Google Scholar 

  7. J. Badan, R. Hierle, A. Perigaud, J. Zyss, and D. Williams: NLO properties of organic molecules and polymeric materials, in American Chemical Society Symposium Series, Vol. 233 (American Chemical Society, Washington, DC, 1993).

    Google Scholar 

  8. N. Zaitseva and L. Carman: Rapid growth of KDP-type crystals. Prog. Cryst. Growth Charact. Mater. 43 (1), 1 (2001).

    Article  CAS  Google Scholar 

  9. M. Shkir, S. Muhammad, S. AlFaify, A. Irfan, and I. Yahia: A dual approach to study the electro-optical properties of a noncentrosymmetric l-asparagine monohydrate. Spectrochim. Acta, Part A 137, 432 (2015).

    Article  CAS  Google Scholar 

  10. M. Shkir, S. Muhammad, and S. AlFaify: Experimental and density functional theory (DFT): A dual approach to study the various important properties of monohydrated L-proline cadmium chloride for nonlinear optical applications. Spectrochim. Acta, Part A 143, 128–135 (2015).

    Article  CAS  Google Scholar 

  11. P. Newman, L. Warren, P. Cunningham, T. Chang, D. Cooper, G. Burdge, P. Polak-Dingels, and C. Lowe-Ma: Semiorganics: A new class of NLO materials. In MRS Proceedings, Vol. 173 (Cambridge University Press, Cambridge, 1989); p. 557.

    Google Scholar 

  12. P.H. Cunningham, L.F. Warren, Jr., O. Marcy, and M.J. Rosker: Semi-organic crystals for nonlinear optical devices. Google Patents, 1996.

  13. N.R. Dhumane, S.S. Hussaini, V.G. Dongre, and M.D. Shirsat: Influence of glycine on the nonlinear optical (NLO) properties of zinc(tris) thiourea sulfate (ZTS) single crystal. Opt. Mater. 31 (2), 328 (2008).

    Article  CAS  Google Scholar 

  14. D.J. Williams: Organic polymeric and non-polymeric materials with large optical nonlinearities. Angew. Chem., Int. Ed. Engl. 23 (9), 690 (1984).

    Article  Google Scholar 

  15. M. Shkir, B. Riscob, M. Ajmal Khan, S. AlFaify, E. Dieguez, and G. Bhagavannarayana: Effect of organic ligands (l-proline and l-methionine) on growth, structural, vibrational, crystalline perfection, SHG efficiency, microscopic and optical properties of KDP single crystals. Spectrochim. Acta, Part A 124, 571 (2014).

    Article  CAS  Google Scholar 

  16. M. Shkir, V. Ganesh, N. Vijayan, B. Riscob, A. Kumar, D.K. Rana, M. Shoeb Khan, M. Hasmuddin, M. Wahab, and R. Ramesh Babu: Analysis on structural, SHG efficiency, optical and mechanical properties of KDP single crystals influenced by glycine doping. Spectrochim. Acta, Part A 103, 199 (2013).

    Article  CAS  Google Scholar 

  17. G. Bhagavannarayana, S. Parthiban, and S. Meenakshisundaram: An interesting correlation between crystalline perfection and second harmonic generation efficiency on KCl-and oxalic acid-doped ADP crystals. Cryst. Growth Des. 8 (2), 446 (2007).

    Article  CAS  Google Scholar 

  18. S. Meenakshisundaram, S. Parthiban, N. Sarathi, R. Kalavathy, and G. Bhagavannarayana: Effect of organic dopants on ZTS single crystals. J. Cryst. Growth 293 (2), 376 (2006).

    Article  CAS  Google Scholar 

  19. S. Bhandari, N. Sinha, G. Ray, and B. Kumar: Enhanced optical, dielectric and piezoelectric behavior in dye doped zinc tris-thiourea sulphate (ZTS) single crystals. Chem. Phys. Lett. 591, 10 (2014).

    Article  CAS  Google Scholar 

  20. N. Sinha, N. Goel, B.K. Singh, M.K. Gupta, and B. Kumar: Enhancement in ferroelectric, pyroelectric and photoluminescence properties in dye doped TGS crystals. J. Solid State Chem. 190, 180 (2012).

    Article  CAS  Google Scholar 

  21. Y. Li, E.G. Johnson, C.D. Nie, J.A. Harrington, and R. Shori: Ho:YAG single crystal fiber: Fabrication and optical characterization. Opt. Express 22 (12), 14896 (2014).

    Article  CAS  Google Scholar 

  22. J. Didierjean, M. Castaing, F. Balembois, P. Georges, D. Perrodin, J.M. Fourmigué, K. Lebbou, A. Brenier, and O. Tillement: High-power laser with Nd:YAG single-crystal fiber grown by the micro-pulling-down technique. Opt. Lett. 31 (23), 3468 (2006).

    Article  CAS  Google Scholar 

  23. M. Enculescu: Morphological and optical properties of doped potassium hydrogen phthalate crystals. Phys. B 405 (17), 3722 (2010).

    Article  CAS  Google Scholar 

  24. B. Raju, A. Saritha, G. Bhagavannarayana, and K.A. Hussain: A comparative study on growth, structural, optical, thermal and mechanical properties of undoped and dye doped bis glycine cadmium chloride single crystals. J. Cryst. Growth 324 (1), 184 (2011).

    Article  CAS  Google Scholar 

  25. S. Chandran, R. Paulraj, and P. Ramasamy: Influence of amaranth dye on the growth and properties of KDP single crystal. Mater. Res. Bull. 68, 210 (2015).

    Article  CAS  Google Scholar 

  26. N. Zaitseva, L. Carman, I. Smolsky, R. Torres, and M. Yan: The effect of impurities and supersaturation on the rapid growth of KDP crystals. J. Cryst. Growth 204 (4), 512 (1999).

    Article  CAS  Google Scholar 

  27. S. Hirota, H. Miki, K. Fukui, and K. Maeda: Coloring and habit modification of dyed KDP crystals as functions of supersaturation and dye concentration. J. Cryst. Growth 235 (1–4), 541 (2002).

    Article  CAS  Google Scholar 

  28. A. Barbon, M. Bellinazzi, J.B. Benedict, M. Brustolon, S.D. Fleming, S-H. Jang, B. Kahr, and A.L. Rohl: Luminescent probes of crystal growth: Surface charge and polar axis sense in dye-doped potassium hydrogen phthalate. Angew. Chem., Int. Ed. 43 (40), 5328 (2004).

    Article  CAS  Google Scholar 

  29. K.L. Wustholz, B. Kahr, and P.J. Reid: Single-molecule orientations in dyed salt crystals. J. Phys. Chem. B 109 (34), 16357 (2005).

    Article  CAS  Google Scholar 

  30. J.B. Benedict, P.M. Wallace, P.J. Reid, S.H. Jang, and B. Kahr: Up-conversion luminescence in dye-doped crystals of potassium hydrogen phthalate. Adv. Mater. 15 (13), 1068 (2003).

    Article  CAS  Google Scholar 

  31. V.V. Poborchii, T. Tada, and T. Kanayama: A visible-near infrared range photonic crystal made up of Si nanopillars. Appl. Phys. Lett. 75 (21), 3276 (1999).

    Article  CAS  Google Scholar 

  32. S.M. Yang and G.A. Ozin: Opal chips: Vectorial growth of colloidal crystal patterns inside silicon wafers. Chem. Commun. 24, 2507–2508, 2507 (2000).

    Article  Google Scholar 

  33. M.C. Wanke, O. Lehmann, K. Müller, Q. Wen, and M. Stuke: Laser rapid prototyping of photonic band-gap microstructures. Science 275 (5304), 1284 (1997).

    Article  CAS  Google Scholar 

  34. P.M. Ushasree, R. Jayavel, C. Subramanian, and P. Ramasamy: Growth of zinc thiourea sulfate (ZTS) single crystals: A potential semiorganic NLO material. J. Cryst. Growth 197 (1–2), 216 (1999).

    Article  CAS  Google Scholar 

  35. G.D. Andreetti, L. Cavalca, and A. Musatti: The crystal and molecular structure of tris (thiourea) zinc (II) sulphate. Acta Crystallogr., Sect. B: Struct. Crystallogr. Cryst. Chem. 24 (5), 683 (1968).

    Article  CAS  Google Scholar 

  36. V. Venkataramanan, M. Srinivasan, and H. Bhat: Vibrational spectroscopic study of zinc tris (thiourea) sulphate, a new organometallic non-linear optical crystal. J. Raman Spectrosc. 25 (10), 805 (1994).

    Article  CAS  Google Scholar 

  37. M. Oussaid, P. Becker, M. Kemiche, and C. Carabatos-Nédelec: Low temperature phase transitions in zinc tris (thiourea) sulfate (ZTS) determined by Raman scattering. Phys. Status Solidi B 207 (1), 103 (1998).

    Article  CAS  Google Scholar 

  38. B.S. Samuel, R. Krishnamurthy, and R. Rajasekaran: Effect of l-aspartic acid on the growth, structure and spectral studies of zinc (tris) thiourea sulphate (ZTS) single crystals. Spectrochim. Acta, Part A 132 (0), 526 (2014).

    Article  CAS  Google Scholar 

  39. A.E. Morales, E.S. Mora, and U. Pal: Use of diffuse reflectance spectroscopy for optical characterization of un-supported nanostructures. Rev. Mex. Fis. S 53 (5), 18 (2007).

    CAS  Google Scholar 

  40. D.G. Barton, M. Shtein, R.D. Wilson, S.L. Soled, and E. Iglesia: Structure and electronic properties of solid acids based on tungsten oxide nanostructures. J. Phys. Chem. B 103 (4), 630 (1999).

    Article  CAS  Google Scholar 

  41. P. Kubelka and F. Munk: A contribution to the optics of pigments. Z. Tech. Phys. 12, 593 (1931).

    Google Scholar 

  42. B.M. Weckhuysen and R.A. Schoonheydt: Recent progress in diffuse reflectance spectroscopy of supported metal oxide catalysts. Catal. Today 49 (4), 441 (1999).

    Article  CAS  Google Scholar 

  43. F. Urbach: The long-wavelength edge of photographic sensitivity and of the electronic absorption of solids. Phys. Rev. 92 (5), 1324 (1953).

    Article  CAS  Google Scholar 

  44. M. Shkir, B. Riscob, V. Ganesh, N. Vijayan, R. Gupta, J. Plaza, E. Dieguez, and G. Bhagavannarayana: Crystal growth, structural, crystalline perfection, optical and mechanical properties of Nd3+ doped sulfamic acid (SA) single crystals. J. Cryst. Growth 380, 228 (2013).

    Article  CAS  Google Scholar 

  45. M. Shakir, S. Kushwaha, K. Maurya, G. Bhagavannarayana, and M. Wahab: Characterization of ZnSe nanoparticles synthesized by microwave heating process. Solid State Commun. 149 (45), 2047 (2009).

    Article  CAS  Google Scholar 

  46. M. Shkir, H. Abbas, and Z.R. Khan: Effect of thickness on the structural, optical and electrical properties of thermally evaporated PbI2 thin films. J. Phys. Chem. Solids 73 (11), 1309 (2012).

    Article  CAS  Google Scholar 

  47. M. Shkir, S. Alfaify, M. Ajmal Khan, E. Dieguez, and J. Perles: Synthesis, growth, crystal structure, EDX, UV-vis-NIR and DSC studies of l-proline lithium bromide monohydrate—A new semiorganic compound. J. Cryst. Growth 391, 104 (2014).

    Article  CAS  Google Scholar 

  48. M. Shkir, B. Riscob, M. Hasmuddin, P. Singh, V. Ganesh, M. Wahab, E. Dieguez, and G. Bhagavannarayana: Optical spectroscopy, crystalline perfection, etching and mechanical studies on P-nitroaniline (PNA) single crystals. Opt. Mater. 36 (3), 675 (2014).

    Article  CAS  Google Scholar 

  49. S. Xu, G. Li, S. Chua, X. Wang, and W. Wang: Observation of optically-active metastable defects in undoped GaN epilayers. Appl. Phys. Lett. 72 (19), 2451 (1998).

    Article  CAS  Google Scholar 

  50. S. Kushwaha, K. Maurya, N. Vijayan, A. Gupta, D. Haranath, B. Kumar, D. Kanjilal, and G. Bhagavannarayana: Au9+ swift heavy ion irradiation of Zn [CS(NH2)2]3·SO4 crystal: Crystalline perfection and optical properties. Nucl. Instrum. Methods Phys. Res., Sect. B 338, 1 (2014).

    Article  CAS  Google Scholar 

  51. A.A. Bol, J. Ferwerda, J.A. Bergwerff, and A. Meijerink: Luminescence of nanocrystalline ZnS:Cu2+. J. Lumin. 99 (4), 325 (2002).

    Article  CAS  Google Scholar 

  52. M. Pal, S. Bera, S. Sarkar, and S. Jana: Influence of Al doping on microstructural, optical and photocatalytic properties of sol–gel based nanostructured zinc oxide films on glass. RSC Adv. 4 (23), 11552 (2014).

    Article  CAS  Google Scholar 

  53. S. Kushwaha, K. Maurya, D. Haranath, and G. Bhagavannarayana: The effect of Cr3+ doping on the crystalline perfection and optical properties of zinc tris (thiourea) sulfate, a nonlinear optical material. J. Appl. Crystallogr. 44 (5), 1054 (2011).

    Article  CAS  Google Scholar 

  54. D. Xue and K. Kitamura: Dielectric characterization of the defect concentration in lithium niobate single crystals. Solid State Commun. 122 (10), 537 (2002).

    Article  CAS  Google Scholar 

  55. N.E. Hill: Dielectric properties and molecular behaviour (Van Nostrand Reinhold, 1969).

  56. J. Przeslawski, T. Iglesias, and J. Gonzalo: Dielectric losses behaviour under frequency and ac field amplitude variation in TGSe crystals. Solid State Commun. 96 (4), 195 (1995).

    Article  CAS  Google Scholar 

  57. M. Shakir, S. Kushawaha, K. Maurya, S. Kumar, M. Wahab, and G. Bhagavannarayana: Enhancement of second harmonic generation, optical and dielectric properties in L-asparagine monohydrate single crystals due to an improvement in crystalline perfection by annealing. J. Appl. Crystallogr. 43 (3), 491 (2010).

    Article  CAS  Google Scholar 

Download references

ACKNOWLEDGMENT

The author is highly thankful to King Khalid University, Abha, Saudi Arabia for providing all necessary facilities for current research.

Author information

Authors and Affiliations

  1. Department of Physics, Faculty of Science, King Khalid University, Abha, 61413, Saudi Arabia

    Mohd. Shkir

Authors
  1. Mohd. Shkir
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Mohd. Shkir.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Shkir, M. Effect of titan yellow dye on morphological, structural, optical, and dielectric properties of zinc(tris) thiourea sulphate single crystals. Journal of Materials Research 31, 1046–1055 (2016). https://doi.org/10.1557/jmr.2016.116

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1557/jmr.2016.116

Search

Navigation