Neutron diffraction study of δ-AlOOD at high pressure and its implication for symmetrization of the hydrogen bond

  • Asami Sano-Furukawa EMAIL logo , Kazuki Komatsu , Carine B. Vanpeteghem and Eiji Ohtani
From the journal American Mineralogist

Abstract

We have conducted a powder neutron diffraction study of the distorted rutile-type hydrous phase δ-AlOO(D0.74H0.26) at pressures up to 9.2 GPa. Rietveld refinement reveals that the observed diffraction data are best fitted by a model with an asymmetric hydrogen bond (space group P21nm). The Al-O2 bonds of the AlO6 octahedron remain longer than the Al-O1 bonds up to 9.2 GPa, reflecting the fact that O2 is the donor and O1 is the acceptor of the hydrogen bond of O2-D···O1. As pressure increases, the Al-O1 bond lengths remain almost constant or increase slightly, whereas the longer Al-O2 bonds are more compressible. The O···O distance of the shared edge of the octahedron is almost constant unlike the other O···O distances that decrease during compression. The bulk modulus of the AlO6 octahedron is determined to be 197.0(4) GPa, where K' is fixed to 4. The AlO6 octahedron rotates about 1° during compression to 9.2 GPa. As pressure increases and the O2···O1 distance decreases, the D···O1 bond is shortened, whereas the O2-D bond becomes elongated, with pressure dependencies of -1.81(9) × 10-2 Å/GPa and 0.57(8) × 10-2 Å/GPa, respectively, implying the symmetrization of the hydrogen bond at high pressure. The decrease in intensity of the 120 reflection as pressure increases suggests that the transition from the structure with space group P21nm to that with Pnnm would take place in δ-AlOOD at high pressure. This transition could be attributed to the disorder of deuterium or symmetrization of the hydrogen bond.

Received: 2007-11-9
Accepted: 2008-3-15
Published Online: 2015-4-1
Published in Print: 2008-10-1

© 2015 by Walter de Gruyter Berlin/Boston

Downloaded on 28.3.2024 from https://www.degruyter.com/document/doi/10.2138/am.2008.2849/html
Scroll to top button