1986 Volume 27 Issue 10 Pages 741-749
Structures of Ti–Al–V alloys have been examined by means of electron probe microanalysis and X-ray diffractometry after being annealed for 2.68 Ms at 1073 K or for 691 ks at 1273 K.
Two three-phase equilibriums, Al8V5+(V, Ti)Al3+(V) and Ti3Al+(β−Ti)+TiAl, have been found, and isothermal diagrams at 1073 K and 1273 K have been reconstructed.
The titanium content in Al8V5 phase is about 5 mass% at 1273 K and 1 mass% at 1073 K. In the TiAl compound which contains vanadium up to the solubility limit, the axial ratio c/a varies from 1.012 to 1.050 with increasing aluminium content.