1997 Volume 38 Issue 12 Pages 1078-1082
In-situ TEM observation of the deformed specimen on heating from R.T. up to 873 K in an Fe-30.3 mass%Mn-6.1 mass%Si shape memory alloy has been performed. It is found that the thicker ε-martensite plates will be disintegrated layer by layer through the reverse motion and annihilation of partial dislocations and the last induced ε-martensite will be the first to disappear. The in-situ observations on heating of the secondary deformed specimen after once thermo-mechanical cycling has also been conducted, from which the improvement mechanism of thermo-mechanical training can be well explained.