Since a TiAl-type intermetallic compound (TiAl) has an excellent high temperature strength and corrosion resistance, in addition to light weight, it is expected to be applicable to the engine parts. However, it is difficult for TiAl to produce a part with a complex shape, and considerable cost will be required. In this study, it was tried to develop a technology for producing TiAl products with high density and high efficiency by using metal powder injection molding (MIM) process. Several kinds of TiAl alloy powders made by the self-propagating high temperature synthesis process were mixed with an organic binder, kneaded and then injection-molded into tensile specimens. These compacts were subjected to the treatment for removing the binder and sintering, resulted in a relative density as high as 97%. By room and high temperature tensile tests, it was found that, Ti-47.4Al-2.6Cr (at%) has the strength and ductility as those of the conventional processed materials.