Abstract
Samples of SAF2906 duplex stainless steel were aged at 650 °C, 700 °C, 750 °C, 800 °C, 850 °C, 900 °C and 950 °C for 1 h, after high temperature solution heat treatment. The morphology of 𝜎-phase in aged SAF2906 duplex stainless steel was then studied by means of scanning electron microscopy, X-ray diffraction and transmission electron microscopy, and the chemical composition of the 𝜎-phase was determined using X-ray energy dispersive spectrometry. The results indicated that the 𝜎 precipitation in SAF2906 duplex stainless steel formed both inside δ-ferrite with high Cr and Mo concentrations, and along δ-ferrite/γ-austenite interfaces; however, relative to the SAF2205 and SAF2507 duplex stainless steels, the content of Cr in 𝜎-phase increased significantly up to 70 %, which was much higher than Fe in the same phase and became the major element of 𝜎-phase.
References
[1] J. Nilsson: Mater. Sci. Technol. 8 (1992) 685–700. DOI:10.1179/mst.1992.8.8.68510.1179/mst.1992.8.8.685Search in Google Scholar
[2] V. Moura, L. Lima: Mater. Charact. 59 (2008) 1127–1132. DOI:10.1016/j.matchar.2007.09.00210.1016/j.matchar.2007.09.002Search in Google Scholar
[3] B. Deng, Y.M. Jiang: Appl. Surf. Sci. 253 (2007) 7369–7375. DOI:10.1016/j.apsusc.2006.10.05710.1016/j.apsusc.2006.10.057Search in Google Scholar
[4] R. Perren, T. Suter: Corros. Sci. 43 (2001) 727–745. DOI:10.1016/S0010-938X(00)00087-110.1016/S0010-938X(00)00087-1Search in Google Scholar
[5] L. Weber, P. Uggowitzer: Mater. Sci. Eng. A 242 (1998) 222–229. DOI:10.1016/S0921-5093(97)00521-210.1016/S0921-5093(97)00521-2Search in Google Scholar
[6] W. Zhang, L.Z. Jiang: Mater. Charact. 60 (2009) 50–55. DOI:10.1016/j.matchar.2008.07.00210.1016/j.matchar.2008.07.002Search in Google Scholar
[7] E. Angelini, B. Benedetti: Corros. Sci. 46 (2004) 1351–1367. 10.1016/j.corsci.2003.09.024Search in Google Scholar
[8] M. Moayed, N. Laycock: Corros. Sci. 45 (2003) 1203–1216. DOI:10.1016/S0010-938X(02)00215-910.1016/S0010-938X(02)00215-9Search in Google Scholar
[9] L. Garfias-Mesias, J. Skyes: Corros. Sci. 38 (1996) 1319–1330. DOI:10.1016/0010-938X(96)00022-410.1016/0010-938X(96)00022-4Search in Google Scholar
[10] H. Sieurin, R. Sandstrom: Mater. Sci. Eng. A 444 (2007) 271–276. DOI:10.1016/j.msea.2006.08.10710.1016/j.msea.2006.08.107Search in Google Scholar
[11] T.H. Chen, J.R. Yang: Mater. Sci. Eng. A 301 (2001) 28–41. DOI:10.1016/S0921-5093(01)00911-X10.1016/S0921-5093(01)00911-XSearch in Google Scholar
[12] R. Badji, M. Bouabdallah: Mater. Sci. Eng. A 496 (2008) 447–454. DOI:10.1016/j.msea.2008.06.02410.1016/j.msea.2008.06.024Search in Google Scholar
[13] J.M. Pardal, S.S.M. Tavares: Mater. Charact. 60 (2009) 165–172. DOI:10.1016/j.matchar.2008.08.00710.1016/j.matchar.2008.08.007Search in Google Scholar
[14] J.K.L. Lai, K.W. Wong: Mater. Sci. Eng. A 203 (1995) 356–364. DOI:10.1016/0921-5093(95)09863-110.1016/0921-5093(95)09863-1Search in Google Scholar
[15] R. Perren, T. Suter: Corros. Sci. 43 (2001) 707–726. DOI:10.1016/S0010-938X(00)00087-110.1016/S0010-938X(00)00087-1Search in Google Scholar
[16] R. Merello, F. Botana: Corros. Sci. 45 (2003) 909–921. DOI:10.1016/S0010-938X(02)00154-310.1016/S0010-938X(02)00154-3Search in Google Scholar
[17] N. Bastos Ivan, S. Tavares Sergio: Scr. Mater. 57 (2007) 913–916. DOI:10.1016/j.scriptamat.2007.07.03710.1016/j.scriptamat.2007.07.037Search in Google Scholar
[18] A. Invernizzi, E. Sivieri: Mater. Sci. Eng. A 485 (2008) 234–242. DOI:10.1016/j.msea.2007.08.03610.1016/j.msea.2007.08.036Search in Google Scholar
[19] B. Deng, Y.M. Jiang: Electrochim. Acta 53 (2008) 5220–5225. DOI:10.1016/j.electacta.2007.10.02510.1016/j.electacta.2007.10.025Search in Google Scholar
[20] M. Martins, C. Casteletti Luiz: Mater. Charact. 55 (2005) 225–233. DOI:10.1016/j.matchar.2005.05.00810.1016/j.matchar.2005.05.008Search in Google Scholar
[21] R. Ovarfort: Corros. Sci. 29 (1989) 987–993. DOI:10.1016/0010-938X(89)90088-710.1016/0010-938X(89)90088-7Search in Google Scholar
© 2015 Carl Hanser Verlag GmbH & Co. KG