Abstract
The Ni–W binary system was assessed using critically evaluated experimental data with assistance from first principles analysis and the CALPHAD method. The solution phases (liquid, fcc-A1 and bcc-A2) were modeled using the substitutional regular solution model. The recently discovered Ni8W metastable phase was evaluated as Fe16C2-like martensite with three sublattices, and shown to be possibly stable according to first principles calculations. Ni8W was also modeled as an interstitial compound, but the model is not good because the solubility of tungsten in nickel is very low, especially at low temperatures. There is no experimental evidence for such low solubility. The other binary compounds Ni4W and Ni3W were assessed as stoichiometric ones. Compared independent experimental and first principles data agree well with the calculated phase diagram using updated thermodynamic parameters.
References
[1] R.J.Mitchell, M.Preuss, S.Tin, M.C.Mardy: Mater. Sci. Eng. A – Struct.473 (2008) 158–165. 10.1016/j.msea.2007.04.098Search in Google Scholar
[2] M.F.Ashby, D.R.H.Jones: Engineering Materials 1, An Introduction to Their Properties and Applications, Pergamon Press, Oxford (1989) 98–99.Search in Google Scholar
[3] N.Schindzielorz, K.Nowak, S.B.Maisel, S.Müller: Acta Mater.75 (2014) 307–315. 10.1016/j.actamat.2014.04.029Search in Google Scholar
[4] P.R. Mallory & Co., Inc.W-Ni-Fe-Mo Alloys. US Patent: us 3988118 (1976), 7 pp.Search in Google Scholar
[5] L.Chen, P.Ettmayer, W.Lengauer: Z. Metallkd.89 (1998) 83–89.Search in Google Scholar
[6] P.Indyka, E.Beltowska-Lehman, L.Tarkowski, A.Bigos, E.Garcia-Lecina: J. Alloys Compd.590 (2014) 75–79. 10.1016/j.jallcom.2013.12.085Search in Google Scholar
[7] R.H.Taylor, S.Curtarolo, G.L.W.Hart: J. Am. Chem. Soc.132 (2010) 6851–6854. 10.1021/ja101890kSearch in Google Scholar
[8] N.Tsyntsaru, H.Cesiulis, E.Pellicer, J.-P.Celsi, J.Sort: Electrochim. Acta104 (2013) 94–103. 10.1016/j.electacta.2013.04.022Search in Google Scholar
[9] N.Sulitanu: J. Magn. Magn. Mat.231 (2001) 85–93. 10.1016/S0304-8853(01)00041-5Search in Google Scholar
[10] G.Kresse, J.Furthmüller: Comp. Mater. Sci.6 (1996) 15–50. 10.1016/0927-0256(96)00008-0Search in Google Scholar
[11] G.Kresse, J.Furthmüller: Phys. Rev. B54 (1996) 11169–11186. 10.1103/PhysRevB.54.11169Search in Google Scholar PubMed
[12] J.P.Perdew, K.Burke, M.Ernzernhof: Phys. Rev. Lett.77 (1996) 3865–3868. PMid:10062328; 10.1103/PhysRevLett.77.3865Search in Google Scholar PubMed
[13] D.Lerch, O.Wieckhorst, G.L.W.Hart, R.W.Forcade, S.Müller: Modelling Simul. Mater. Sci. Eng.17 (2009), 19 pp.10.1088/0965-0393/17/5/055003Search in Google Scholar
[14] S.J.B.Kurz, S.B.Maisel, A.Leineweber, M.Höfler, S.Müller, E.J.Mittemeijer: J. Appl. Phys.116 (2014) 083515-1–083515-9. 10.1063/1.4894148Search in Google Scholar
[15] S.J.B.Kurz: Dr. Thesis, Nanocrystalline Thin Films: Microstructure, Stability and Properties, Max-Planck-Institut für Intelligente Systeme, Stuttgart, DEU (2014).Search in Google Scholar
[16] Z.W.Lu, B.M.Klein: Phys. Rev. B50 (1994) 5962–5970. 10.1103/PhysRevB.50.5962Search in Google Scholar
[17] G.B.Brook, Chapter 6, Crystal Chemistry, in: E.A.Brandes (Ed.), Smithells Metals Reference Book, 6th Edition, Butterworths, London (1983) 6–28–6–30.Search in Google Scholar
[18] G.B.Brook, Chapter 6, Crystal Chemistry, in: E.A.Brandes, G.B.Brook (Eds.), Smithells Metals Reference Book, 7th Edition, Butterworth-Heinemann, Oxford (1999) 6–28–6–30.Search in Google Scholar
[19] R.Naraghi, M.Selleby, J.Ågren: CALPHAD46 (2014) 148–158. 10.1016/j.calphad.2014.03.004Search in Google Scholar
[20] G.Badinier: Ph.D. Thesis, University of British Columbia, Canada, (2013).Search in Google Scholar
[21] F.Cardarelli, Materials Handbook, 2nd Ed., Springer, London (2008) 1219. 10.1007/978-1-4471-3648-4Search in Google Scholar
[22] S.Ishida, K.Kiwatase, S.Fujii, S.Asano: J. Phys.–Condens. Mat.4 (1992) 765–774. 10.1088/0953-8984/4/3/016765-774Search in Google Scholar
[23] T.Kakeshita, C.M.Wayman: Mat. Sci. Eng. A141 (1991) 209–219. 10.1016/0921-5093(91)90771-ESearch in Google Scholar
[24] W.Kohn: Phys. Rev.136 (1964) B864–B871. 10.1103/PhysRev.136.B864Search in Google Scholar
[25] G.Kresse, D.Joubert: Phys. Rev. B59 (1999) 1758–1775. 10.1103/PhysRevB.59.1758Search in Google Scholar
[26] K.Parlinski, Z.Q.Li, Y.Kawazoe: Phys. Rev. Lett.78 (1997) 4063–4066. 10.1103/PhysRevLett.78.4063Search in Google Scholar
[27] F.H.Ellinger, W.P.Sykes: T. Am. Soc. Metal.28 (1940) 619–645.Search in Google Scholar
[28] I.I.Kornilov, P.D.Budberg: Dokl. Akad. Nauk SSSR100 (1955) 73–75.Search in Google Scholar
[29] H.Hofmann: Dissertation, Technische Universität Berlin, DEU (1983).Search in Google Scholar
[30] A.Gabriel, H.L.Lukas, C.H.Allibert, I.Ansara: Z. Metallkd.76 (1985) 589–595.Search in Google Scholar
[31] W.B.Pearson: A Handbook of Lattice Spacings and Structures of Metals and Alloys, Vol. 4., Pergamon, Oxford UK (1958) 794.Search in Google Scholar
[32] C.Laugee, C.H.Allibert, I.Ansara: Z. Metallkd.76 (1985) 138–142.Search in Google Scholar
[33] A.L.Udovskii, V.N.Karpushkin, E.A.Nikishina: Izv. Akad. Nauk. SSSR, Metall. (1991) 87–103.Search in Google Scholar
[34] C.L.Meshkov, L.S.Guzei, V.A.Kasakov, M.Sokolovskaya: Mosc. Univ. Chem. Bull.27 (1972) 83–84.Search in Google Scholar
[35] J.Mayer, K.Urban: Phys. Status Solidi A90 (1985) 469–475. 10.1002/pssa.2210900209Search in Google Scholar
[36] V. SubramanyaSarma, J.Eickemeyer, C.Mickel, L.Schultz, B.Holzapfel: Mat. Sci. Eng. A-Struct.380 (2004) 30–33. 10.1016/j.msea.2004.05.024Search in Google Scholar
[37] S.B.Maisel, N.Schindzielorz, S.Müller, H.Reichert, A.Bosak: J. Appl. Cryst.46 (2013) 1211–1215. 10.1107/S0021889813016270Search in Google Scholar
[38] R.Vogel: Z. Anorg. Chem.116 (1921) 231–242. 10.1002/zaac.19211160123Search in Google Scholar
[39] K.Becker, F.Ebert: Z. Phys.16 (1923) 165–169. 10.1007/BF01327387Search in Google Scholar
[40] R.Cury, J.-M.Joubert, S.Tusseau-Nenez, E.Leroy, A.Allavena-Valette: Intermetallics17 (2009) 174–178. 10.1016/j.intermet.2008.11.001Search in Google Scholar
[41] S.Inomata, M.Kajihara: J. Alloys Compd.509 (2011) 4958–4966. 10.1016/j.jallcom.2011.01.139Search in Google Scholar
[42] H.Okamoto: Desk Handbook, Phase Diagrams for Binary Alloys, ASM International, Materials Park, Ohio, USA (2000) 626.Search in Google Scholar
[43] L.P.Arapova: Sov. Phys. J.16 (1973) 1173–1175. 10.1007/BF00890486Search in Google Scholar
[44] H.Okamoto: Desk Handbook, Phase Diagrams for Binary Alloys, ASM International, Materials Park, Ohio, USA (2000) 572. PMid:11198271Search in Google Scholar
[45] Ya.S.Umanskii, A.N.Dubrovina, L.P.Arapova: Izv. VUZov, Chern. Metall.11 (1969) 129–131 (cited by Hofmann [29]).Search in Google Scholar
[46] L.P.Arapova: Sov. Phys. J.19 (1976) 1197–1199. 10.1007/BF00891478Search in Google Scholar
[47] J.M.Walsh, M.J.Donachie: Metall. Trans.4 (1973) 2854–2855. 10.1007/BF02644589Search in Google Scholar
[48] X.Liu, J.Pilling, R.W.Heckel, J.K.Lee: Mat. Sci. Tech. Ser.7 (1991) 228–237. 10.1179/mst.1991.7.3.228Search in Google Scholar
[49] J.Lee, C.R.Lear, Z.Zhang, P.Bellon, R.S.Averback: Metall. Mater. Trans. A46A (2015) 1046–1061. 10.1007/s11661-014-2704-4Search in Google Scholar
[50] C.J.Marvel, P.R.Cantwell, M.P.Harmer: Scripta Mater.96 (2015) 45–48. 10.1016/j.scriptamat.2014.10.002Search in Google Scholar
[51] K.E.Poulsen, S.Rubæk, E.W.Langer: Scripta Metall. Mater.8 (1974) 1297–1300. 10.1016/0036-9748(74)90349-4Search in Google Scholar
[52] P.E.Blöchl: Phys. Rev. B50 (1994) 17953–17979. 10.1103/PhysRevB.50.17953Search in Google Scholar
[53] J.P.Perdew, K.Burke, M.Ernzernhof: Phys. Rev. Lett.78 (1997) 1396–1396. 10.1103/PhysRevLett.78.1396Search in Google Scholar
[54] N.Dupin: Personal communication, Ni-Ti-W TDB file, (2013).Search in Google Scholar
[55] P.Gustafson, A.Gabriel, I.Ansara: Z. Metallkd.78 (1986) 151–156.Search in Google Scholar
[56] A.T.Dinsdale: CALPHAD15 (1991) 317–425. 10.1016/0364-5916(91)90030-NSearch in Google Scholar
[57] O.Redlich, A.T.Kister: Ind. Eng. Chem.40 (1948) 345–348. 10.1021/ie50458a036Search in Google Scholar
[58] J.O.Andersson, T.Helander, L.Höglund L., P.F.Shi, B.Sundman: Calphad26 (2002) 273–312. 10.1016/S0364-5916(02)00037-8Search in Google Scholar
[59] S.Jonsson: Ph.D. Thesis, Royal Institute of Technology, Stockholm, Sweden (1993).Search in Google Scholar
[60] Y.Peng, P.Zhou, Y.Du, K.Chang: Int. J. Refract. Met. H.40 (2013) 36–42. 10.1016/j.ijrmhm.2013.03.012Search in Google Scholar
[61] H.Okamoto: Desk Handbook, Phase Diagrams for Binary Alloys, ASM International, Materials Park, Ohio, USA (2000) 238.Search in Google Scholar
[62] E.Parthe, L.Gelato, B.Chabot, M.Penzo, K.Cenzual, R.Gladyshevskii, TYPIX Standardised Data and Crystal Chemistry Characterization of Inorganic Structure Types, 4.3. Strukturbericht Table in: E.Fluck (ed.) Gmelin Handbook of Inorganic and Organometallic Chemistry, Springer Verlag, 8th Ed., Berlin, Heidelberg DEU (1993) 363–371.Search in Google Scholar
[63] T.Hahn, in: D. W.Penfold, M. H.Dacombe, S. E.Barnes and N. J.Ashcroft (eds.) International Tables for Crystallography, Vol. A, Fifth Edition, The International Union for Crystallography by Springer, DEU (2005) 292, 356, 478, 688, 734.Search in Google Scholar
[64] M.H.de Sa, I.Isomäki, J.A.Ferreira, M.Hämäläinen, M.H.Braga: Mater. Sci. Forum730–732 (2013) 775–780.Search in Google Scholar
[65] L.Kaufman, H.Nesor: Can. Metall. Quart.14 (1975) 221–232. 10.1179/000844375795050157Search in Google Scholar
[66] M.Hansen, Constitution of Binary Alloys, 2nd Edition, McGraw-Hill, New York, (1958) 1058.Search in Google Scholar
© 2017, Carl Hanser Verlag, München
This work is licensed under the Creative Commons Attribution 4.0 International License.