Abstract
The present work investigates the universal applicability of glow discharge plasmas for the microstructure representation of different materials taking the example of Ni-Ti alloys, Cu-Zn alloys, and the Ni based alloy “Hastelloy C 276”. Results are compared with the results provided by classical etching methods. Microstructures became visible for the previously mechanically polished materials within a few seconds, even without detailed optimization of the excitation conditions of the glow discharge plasma. The results partially significantly outperfomed the results of the classical preparation techniques with respect to the detectability of structural details such as grain and phase boundaries. Due to the demonstrated wide and relatively uncomplicated applicability, the per se established glow discharge technology is expected to have a huge potential for application for a rapid and high-contrast microstructure representation.
Kurzfassung
Die universelle Anwendbarkeit von Glimmentladungsplasmen zur Darstellung der Gefüge unterschiedlicher Materialien wird in der vorliegenden Arbeit am Beispiel von Ni-Ti-Legierungen, Cu-Zn-Legierungen und der Ni-Basislegierung „Hastelloy C 276“ untersucht und mit den Ergebnissen klassischer Ätzverfahren verglichen. Bereits ohne detaillierte Optimierung der Anregungsbedingungen des Glimmentladungsplasmas wurden für die zuvor mechanisch polierten Materialien die Gefüge innerhalb weniger Sekunden sichtbar, wobei die Ergebnisse die der klassischen Präparationstechniken bezüglich Erkennbarkeit von Gefügedetails wie Korn- und Phasengrenzen teils deutlich übertreffen. Aufgrund der demonstrierten breiten und vergleichsweise unkomplizierten Anwendbarkeit wird der an sich etablierten Glimmentladungstechnologie großes Anwendungspotential für eine rasche und kontrastreiche Gefügedarstellung konstatiert.
References / Literatur
[1] ASM Handbook: Metallography and Microstructures. Materials Park, OH: ASM International; 2004.Search in Google Scholar
[2] Petzow, G.: Metallographic etching: techniques for metallography, ceramography, plastography. 2nd ed., ASM International, Ohio, USA, 1999Search in Google Scholar
[4] Marcus, R.K.; Broekaert, J.A.C.: Glow discharge plasmas in analytical spectroscopy. J. Wiley, Chichester, England, 200310.1002/0470857854Search in Google Scholar
[5] Brackmann, V.; Hoffmann, V.; Kauffmann, A.; Helth, A.; Thomas, J.; Wendrock, H.; Freudenberger, J.; Gemming, T.; Eckert, J.: Glow discharge plasma as a surface preparation tool for microstructure investigations. Materials Characterization91 (2014), 76–8810.1016/j.matchar.2014.02.002Search in Google Scholar
[6] Shimizu, K.; Mitani, T.: New horizons of applied scanning electron microscopy. Springer-Verlag, Heidelberg, Germany, 201010.1007/978-3-642-03160-1Search in Google Scholar
[7] Undisz, A.; Schrempel, F.; Wesch, W.; Rettenmayr, M.: Mechanism of oxide layer growth during annealing of NiTi. Journal of Biomedical Materials Research Part A, 100A (2012) 7, 1743–175010.1002/jbm.a.34133Search in Google Scholar PubMed
[8] Undisz, A.; Hanke, R.; Freiberg, K. E.; Hoffmann, V.; Rettenmayr, M.: The effect of heating rate on the surface chemistry of NiTi, Acta Biomaterialia10 (2014) 11, 4919–492310.1016/j.actbio.2014.07.018Search in Google Scholar PubMed
[9] Undisz, A.; Reuther, K.; Reuther, H.; Rettenmayr, M.: Occurrence and origin of non-martensitic acicular artifacts on NiTi, Acta Materialia59 (2011) 1, 216–22410.1016/j.actamat.2010.09.026Search in Google Scholar
© 2016, Carl Hanser Verlag, München