Abstract
For the assessment of the precipitation state in aluminum-based alloys by transmission electron microscopy (TEM), the sample must have an orientation in the [100] direction of the matrix. TEMs equipped with objective lenses that are optimized for high resolution are mostly characterized by limited sample tilt angles. The required crystal orientation must thus be taken into account during sampling. A favorably oriented grain was chosen in a coarse-grained material using electron backscatter diffraction and prepared in a suitable direction applying the in-situ lift-out method in the focused ion beam device. After that, the final correction of the orientation in the TEM amounts to less than 12°.
Kurzfassung
Für die Beurteilung des Ausscheidungszustandes in Aluminiumbasislegierungen mittels Transmissionselektronenmikroskopie (TEM) ist eine Orientierung der Probe in [100]-Richtung der Matrix erforderlich. TEMs, deren Objektivlinsen für hohe Auflösungen optimiert sind, haben meist begrenzte Kippwinkel für die Probe. Es muss daher bereits bei der Probenahme der geforderten Kristallorientierung Rechnung getragen werden. Mittels Elektronenrückstreubeugung wurde in einem grobkörnigen Material ein günstig orientiertes Korn ausgewählt und in einer geeigneten Richtung mittels In-situ Lift-out Methode im Focused Ion Beam Gerät präpariert. Die finale Korrektur der Orientierung im TEM beträgt dann unter 12°.
References / Literatur
[1] Totten, G. E.; MacKenzie, D. S.; Handbook of Aluminum Vol. 1: Marcel Dekker Inc., New York, 200310.1201/9780203912607Search in Google Scholar
[2] Ostermann, F.: Anwendungstechnologie Aluminium, Springer-Verlag, Berlin Heidelberg, 2014.10.1007/978-3-662-43807-7Search in Google Scholar
[3] Hatch, J. E.: Aluminum Properties and Physical Metallurgy, ASM International, 1984.Search in Google Scholar
[4] Wolverton, C.: Acta Mat.55 (2007), 5867–5872. 10.1016/j.actamat.2007.06.039Search in Google Scholar
[5] Silcock, J. M.; Heal, T. J.; Hardy, H. K: J. Inst. Metals84 (1955): 23–35.Search in Google Scholar
[6] Pogatscher, S.; Antrekowitsch, H.; Werinos, M.; Moszener, F.; Gerstl, S. S. A.; Franzis, M. F.; Curtin, W. A.; Löffler, J. F.; Uggowitzer, P. J.: Phys. Rev. Lett.112 (2014) 22570110.1103/PhysRevLett.112.225701Search in Google Scholar PubMed
[7] Thomas, J.; Gemming, T.: Analytische Transmissionselektronenmikroskopie, Springer-Verlag, Wien Heidelberg New York Dordrecht London, 2013.10.1007/978-3-7091-1440-7Search in Google Scholar
[8] Ayache, J.; Beaunier, L.; Boumendil, J.; Ehret, G.; Laub, D.: Sample Preparation Handbook for Transmission Electron Microscopy – Techniques, Springer Science+Business Media LLC, New York Dordrecht Heidelberg London, 2010.10.1007/978-1-4419-5975-1Search in Google Scholar
[9] Schwartz, A. J.; Kumar, M.; Adams, B. L.; Field, D. P.: Electron Backscatter Diffraction in Materials Science, Springer Science+Business Media, New York, 2009.10.1007/978-0-387-88136-2Search in Google Scholar
[10] Schwarzer, R.: Prakt. Metallographie51 (2014), 160–179. 10.3139/147.110280Search in Google Scholar
[11] Vander Voort, G. F.: Prakt. Metallographie48 (2011): 454–473. 10.3139/147.110151Search in Google Scholar
[12] Giannuzzi, L. A.; Stevie, F. A.: Introduction to Focused Ion Beams: Springer Science+Business Media Inc., New-York, 2005. 10.1007/b101190Search in Google Scholar
[13] Mühle, U.; Jansen, S.; Leinert, S.; Breuer, D.; Prakt. Metallographie43 (2006); 306–31510.3139/147.100304Search in Google Scholar
[14] Ringer, S. P.; Hono, K.; Sakurai, T.: Met. and Mater. Trans.26 (1995): 2207–221710.1007/BF02671236Search in Google Scholar
© 2019, Carl Hanser Verlag, München