The interfacial tension (IFT) of Polypropylene/Polyamide6 (PP/PA6) and Polypropylene/Polyethylene terephthalate (PP/PET) pairs was evaluated as a function of temperature and Glycidyl Methacrylate grafted PP (PP-g-GMA) content, using the pendant drop method (PDM). PP-g-GMA was used as the compatibilizer in both systems. It was observed that IFT values of both systems showed a linear decrease with increasing temperature. Also, presence of a small amount of PP-g-GMA compatibilizer in the PP phase reduced the IFT of polymeric pairs dramatically, while adding more compatibilizer had no influence on IFT, due to the saturation of the interface. The saturation concentrations of GMA in the PP phase were obtained for 0.05 wt.% and 0.025 wt.% in PP/PA6 and PP/PET systems, respectively. The IFT values of compatibilized systems were reduced by 68% for PP/PA6 and 57% for PP/PET pairs compared to non-compatibilized ones.
References
Abbacha, N., Fellahi, S., Synthesis of PP-G-MAH and Evaluation of its Effect on the Properties of Glass Fibre Reinforced Nylon 6/Polypropylene Blends, Macromol. Symp., 178, 131–138 (2002).10.1002/1521-3900(200202)178:1<131::AID-MASY131>3.0.CO;2-DSearch in Google Scholar
Anastasiadis, S. H., et al., The Determination of Polymer Interfacial Tension by Drop Image Processing: Comparison of Theory and Experiment for the Pair, Poly(Dimethyl Siloxane)/Polybutadiene, Polym. Eng. Sci., 26, 1410–1418(1986).10.1002/pen.760262010Search in Google Scholar
Anastasiadis, S. H., et al., The Determination of Interfacial Tension By Video Image Processing of Pendant Fluid Drops, J. Colloid Interface Sci., 119, 55–66(1987).10.1016/0021-9797(87)90244-XSearch in Google Scholar
Anastasiadis, S. H., et al., Interfacial Tension of Immiscible Polymer Blends: Temperature and Molecular Weight Dependance, Macromolecules, 21, 2980–2987(1988).10.1021/ma00188a015Search in Google Scholar
Arashiro, E. Y., Demarquette, N. R., Use of the Pendant Drop Method to Measure Interfacial Tension between Molten Polymers, Mater. Res.2, 23–32(1999).10.1590/S1516-14391999000100005Search in Google Scholar
Arashiro, E. Y., Demarquette, N. R., Influence of Temperature, Molecular Weight, and Polydispersity of Polystyrene on Interfacial Tension Between Low-Density Polyethylene and Polystyrene, J. Appl. Polym. Sci., 74, 2423–2431 (1999).10.1002/(SICI)1097-4628(19991205)74:10<2423::AID-APP10>3.0.CO;2-LSearch in Google Scholar
Bashforth, S., Adams, J. C.: An Attempt to Test the Theory of Capillary Action, Cambridge University Press and Deighton, Bell, London(1882).Search in Google Scholar
Brandrup, J., et al.: Polymer Handbook, 4th Edition, John Wiley & Sons, New York(1999).Search in Google Scholar
Chen, C. C., White, J. L., Compatibilizing Agents in Polymer Blends: Interfacial Tension, Phase Morphology, and Mechanical Properties, Polym. Eng. Sci., 33, 923–930(1993).10.1002/pen.760331409Search in Google Scholar
Champagne, M. F., et al., Reactive Compatibilization of Polypropylene/Polyethylene Terephthalate Blends, Polym. Eng. Sci., 39, 976–984(1999).10.1002/pen.11487Search in Google Scholar
Chapleau, N., et al., Measuring the Interfacial Tension of Polyamide/Polyethylene and Polycarbonate/Polypropylene Blends: Effect of Temperature, Polymer, 41, 6695–6698(2000).10.1016/S0032-3861(00)00006-9Search in Google Scholar
Demarquette, N. R., Interfacial Tension in Polymer Blends: Measurement and Analysis, Phd Thesis, McGill University, Montreal(1993).Search in Google Scholar
Demarquette, N. R., Kamal, M. R., Interfacial Tension in Polymer Melts. I: An Improved Pendant Drop Apparatus, Polym. Eng. Sci., 34, 1823–1833(1994).10.1002/pen.760342407Search in Google Scholar
Demarquette, N. R., et al., Comparison between Five Experimental Methods to Evaluate Interfacial Tension Between Molten Polymers, Polym. Eng. Sci., 43, 670–683(2003).10.1002/pen.10055Search in Google Scholar
Garmabi, H., et al., Effect of Temperature and Compatibilizer on Interfacial Tension Of PE/PA-6 and PP/EVOH, Int. Polym. Proc., 2, 183–191(1998).Search in Google Scholar
Gonzalez, J., et al., Dynamic Thermal Decomposition of Blends of Polyamide 6 with Functionalized and Non-Functionalized PP, Polym. Deg. Stab., 68, 9–19(2000).10.1016/S0141-3910(99)00160-3Search in Google Scholar
Guerrica-E., G., et al., Interfacial Tension as a Parameter to Characterize the Miscibility Level of Polymer Blends, Polymer Testing, 19, 849–854(2000).10.1016/S0142-9418(99)00055-0Search in Google Scholar
Golmohamadi, A. S., Garmabi, H., Optimization of Melt Grafting of GMA on PP in the Presence and Absence of Coagent, Macro, France, Paris(2004).Search in Google Scholar
Jannerfeldt, G., et al., Influence of Hyperbranched Polymers on the Interfacial Tension of Polypropylene/Polyamide-6 Blends, J. Polym. Sci.: Part B: Polym. Phys., 37, 2069–2077(1999).10.1002/(SICI)1099-0488(19990815)37:16<2069::AID-POLB10>3.0.CO;2-USearch in Google Scholar
Kamal, M. R., et al., Interfacial Tension in Polymer Melts. Part II: Effects of Temperature and Molecular Weight on Interfacial Tension, Polym. Eng. Sci., 34, 1834–1839(1994).10.1002/pen.760342408Search in Google Scholar
Kim, J. K., Jeong, W. Y., Measurement of Contact Angles and Interfacial Tensions of a Reactive Polymer Blend Using the Neumann Triangle Method, Polymer, 42, 4423–4432(2001).10.1016/S0032-3861(00)00838-7Search in Google Scholar
Koning, C., et al., Strategies for Compatibilization of Polymer Blends, Prog. Polym. Sci., 23, 707–757(1998).10.1016/S0079-6700(97)00054-3Search in Google Scholar
La Mantia, F. P., Capizzi, L., Recycling of Compatibilized and Uncompatibilized Nylon/Polypropylene Blends, Polym. Deg. Stab., 71, 285–291(2001).10.1016/S0141-3910(00)00177-4Search in Google Scholar
Lepers, J.-C., et al., The Relative Role of Coalescence and Interfacial Tension in Controlling Dispersed Phase Size Reduction During the Compatibilization of Polyethylene Terephthalate/Polypropylene Blends, J. Polym. Sci.: Part B: Polym. Phys., 35, 2271–2280(1997).10.1002/(SICI)1099-0488(199710)35:14<2271::AID-POLB7>3.0.CO;2-ZSearch in Google Scholar
Lepers, J.-C., et al., The Influence of Partial Emulsification on Coalescence Suppression and Interfacial Tension Reduction in PP/PET Blends, J. Polym. Sci.: Part B: Polym. Phys., 37, 939–951(1999).10.1002/(SICI)1099-0488(19990501)37:9<939::AID-POLB6>3.0.CO;2-OSearch in Google Scholar
Morita, A. T., et al., Influence of Drop Volume on Surface Tension Evaluated Using the Pendant Drop Method, Colloid Polym. Sci., 28, 857–864(2002).10.1007/s00396-002-0694-zSearch in Google Scholar
Palmer, G., Demarquette, N. R., Evaluation of Imbedded Fiber Retraction Phenomenological Models for Determining Interfacial Tension between Molten Polymers, Polymer, 46, 8169–8177(2005).10.1016/j.polymer.2005.06.047Search in Google Scholar
Reignier, J., et al., Factors Influencing Encapsulation Behaviour in Composite Droplet-Type Polymer Blends, Polymer, 44, 49–59(2003).10.1016/S0032-3861(02)00684-5Search in Google Scholar
Roeder, J., et al., Compatibility Effect on the Thermal Degradation Behaviour of Polypropylene Blends with Polyamide 6, Ethylene Propylene Diene Copolymer and Polyurethane, Polym. Deg. Stab., 90, 481–487(2005).10.1016/j.polymdegradstab.2005.04.008Search in Google Scholar
Ronca, G., Russell, T. P., Thermodynamics of Phase Separation in Polymer Mixtures, Macromolecules, 18, 665–670(1985).10.1021/ma00146a015Search in Google Scholar
Shariatpanahi, H., et al., Relationship between Interfacial Tension and Dispersed Phase Particle Size in Polymer Blends. II. PP/PA6, J. Appl. Polym. Sci., 88, 54–63(2003).10.1002/app.11550Search in Google Scholar
Tedesco, A., et al., Comparative Study of PP-MA and PP-GMA as Compatibilizing Agents on Polypropylene/Nylon 6 Blends, Polymer Testing, 21, 11–15(2002).10.1016/S0142-9418(01)00038-1Search in Google Scholar
Teng, J., et al., Reactive Blending of Functionalized Polypropylene and Polyamide 6: In Situ Polymerization and In Situ Compatibilization, Polym. Eng. Sci., 44, 648–659(2004).10.1002/pen.20059Search in Google Scholar
Verdier, C., et al., High Temperature Interfacial Tension Measurements of PA6/PP Interfaces Compatibilized with Copolymers Using a Spinning Drop Tensiometer, Polymer, 41, 6683–6689(2000).10.1016/S0032-3861(00)00059-8Search in Google Scholar
Welge, I., Wolf, B. A., Reduction of the Interfacial Tension between ‘Immiscible’ Polymers: To Which Phase One Should Add a Compatibilizer, Polymer, 42, 3467–3473(2001).10.1016/S0032-3861(00)00781-3Search in Google Scholar
Willemse, R. C., et al., Co-continuous Morphologies in Polymer Blends: The Influence of the Interfacial Tension, Polymer, 40, 827–834(1999).10.1016/S0032-3861(98)00307-3Search in Google Scholar
Wilkinson, A. N., et al., The Effects of SEBS-G-Maleic Anhydride Reaction on the Morphology and Properties of Polypropylene/PA6/SEBS Ternary Blends, Polymer, 45, 5239–5249(2004).10.1016/j.polymer.2004.05.033Search in Google Scholar
Wu, S., Surface And Interfacial Tensions Of Polymer Melts. II. Poly(Methyl Methacrylate), Poly(N-Butyl Methacrylate) And Polystyrene, J. Phys. Chem., 74, 632–638(1970).10.1021/j100698a026Search in Google Scholar
Wu, S.: Polymer Interface & Adhesion, Marcel Dekker, New York(1982).Search in Google Scholar
Wu, S., Formation of Dispersed Phase in Incompatible Polymer Blends: Interfacial and Rheological Effects, Polym. Eng. Sci., 27, 335–343(1987).10.1002/pen.760270506Search in Google Scholar
Xanthos, M., et al., Polypropylene/Polyethylene Terephthalate Blends Compatibilized through Functionalization, Polym. Eng. Sci., 30, 355–365(1990).10.1002/pen.760300607Search in Google Scholar
Xie, X.-M., et al., Effect of Interfacial Tension on the Formation of the Gradient Morphology in Polymer Blends, J. Colloid & Interface Sci., 206, 189–194(1998).Search in Google Scholar
Xing, P., et al., Critical Experimental Comparison between Five Techniques for the Determination of Interfacial Tension in Polymer Blends: Model System of Polystyrene/Polyamide-6, Macromolecules, 33, 8020–8034(2000).10.1021/ma000537xSearch in Google Scholar
Zhaohui, L., et al., The Interfacial Tension and Morphology of Reactive Polymer Blends, Materials Letters, 48, 81–88(2001).10.1016/S0167-577X(00)00283-4Search in Google Scholar
Zoller, P., Pressure-Volume-Temperature Relationships of Solid and Molten Polypropylene and Poly(Butene-1), J. Appl. Polym. Sci., 23, 1057–1061(1979).10.1002/app.1979.070230411Search in Google Scholar
© 2009, Carl Hanser Verlag, Munich